In this paper, 1.2 kV, 3.3 kV, and 5.0 kV class 4H-SiC power Schottky barrier diodes （SBDs） are fabricated with three N-type drift layer thickness values of 10 μm, 30μm, and 50 μm, respectively. The avalanche bre...In this paper, 1.2 kV, 3.3 kV, and 5.0 kV class 4H-SiC power Schottky barrier diodes （SBDs） are fabricated with three N-type drift layer thickness values of 10 μm, 30μm, and 50 μm, respectively. The avalanche breakdown capabilities, static and transient characteristics of the fabricated devices are measured in detail and compared with the theoretical pre- dictions. It is found that the experimental results match well with the theoretical calculation results and are very close to the 4H-SiC theoretical limit line. The best achieved breakdown voltages （BVs） of the diodes on the 10 p.m, 30 m, and 50 -tm epilayers are 1400 V, 3320 V, and 5200 V, respectively. Differential specific-on resistances （Ron-sp） are 2.1 m--cm2, 7.34 mO. cm2, and 30.3 m-. cm2, respectively.展开更多
基金supported by the National Natural Science Foundation of China(Grant Nos.61404098,61176070,and 61274079)the Doctoral Fund of Ministry of Education of China(Grant Nos.20110203110010 and 20130203120017)+1 种基金the National Key Basic Research Program of China(Grant No.2015CB759600)the Key Specific Projects of Ministry of Education of China(Grant No.625010101)
文摘In this paper, 1.2 kV, 3.3 kV, and 5.0 kV class 4H-SiC power Schottky barrier diodes （SBDs） are fabricated with three N-type drift layer thickness values of 10 μm, 30μm, and 50 μm, respectively. The avalanche breakdown capabilities, static and transient characteristics of the fabricated devices are measured in detail and compared with the theoretical pre- dictions. It is found that the experimental results match well with the theoretical calculation results and are very close to the 4H-SiC theoretical limit line. The best achieved breakdown voltages （BVs） of the diodes on the 10 p.m, 30 m, and 50 -tm epilayers are 1400 V, 3320 V, and 5200 V, respectively. Differential specific-on resistances （Ron-sp） are 2.1 m--cm2, 7.34 mO. cm2, and 30.3 m-. cm2, respectively.