The effect of particle shape on the porosity and compressive strength of porous hydroxyapatite （HA） scaffolds was investigated by sintering the mixture of rod-shaped HA （r-HA） and spherical HA （s-HA） with polyac...The effect of particle shape on the porosity and compressive strength of porous hydroxyapatite （HA） scaffolds was investigated by sintering the mixture of rod-shaped HA （r-HA） and spherical HA （s-HA） with polyacrylamide used as the sacrificial template. It was found, for the first time, that addition of r-HA into s-HA could exponentially decrease the porosity of sintered HA scaffolds and enhance their compressive strength with the increase of r-HA content. The mechanism, according to the results from scanning electron microscopy and X-ray diffraction, lies in the restriction of s-HA to the grain formation and growth of r-HA during sintering and results in the fusion of r-HA with s-HA. These findings suggest that mixture of r-HA and s-HA might provide a new and facile way to improve the compressive strength of oorous HA scaffolds.展开更多
基金supported by the National Natural Science Foundation of China (Nos. 11532004 and 31370946)the National Science and Technology Support Program of China (No. 2012BAI17B03-4)+1 种基金the Development of Strategic Emerging Industries of Shenzhen Project (Nos. JCYJ20140417113430596 and CXZZ201404171134 30716)the Science and Technology Project of Guangdong Province (No. 2015A010105021)
文摘The effect of particle shape on the porosity and compressive strength of porous hydroxyapatite （HA） scaffolds was investigated by sintering the mixture of rod-shaped HA （r-HA） and spherical HA （s-HA） with polyacrylamide used as the sacrificial template. It was found, for the first time, that addition of r-HA into s-HA could exponentially decrease the porosity of sintered HA scaffolds and enhance their compressive strength with the increase of r-HA content. The mechanism, according to the results from scanning electron microscopy and X-ray diffraction, lies in the restriction of s-HA to the grain formation and growth of r-HA during sintering and results in the fusion of r-HA with s-HA. These findings suggest that mixture of r-HA and s-HA might provide a new and facile way to improve the compressive strength of oorous HA scaffolds.