The CdS/spherical g-C3N4 n-n heterojunction photocatalyst was fabricated via a solvothermal method.The tetracycline was used to characterize the photocatalytic properties of the as-developed hybrids.The photocatalytic...The CdS/spherical g-C3N4 n-n heterojunction photocatalyst was fabricated via a solvothermal method.The tetracycline was used to characterize the photocatalytic properties of the as-developed hybrids.The photocatalytic degradation mechanism of the as-developed heterojunction photocatalyst was also analyzed.Research results show that CdS nanoparticles are well dispersed in the surface layer of spherical g-C3N4.Moreover,the mass ratio of CdS to spherical g-C3N4 will influence the photocatalytic activity of the asdeveloped composites,which shows the trend of first increasing and then decreasing as it increased.When the mass ratio is 7:1,in 25 min,the as-developed heterojunction shows 93.2%of the maximum photocatalytic efficiency and still exhibits 83.6%after 5 times cycle testing.Moreover,the as-developed hybrids can accelerate the electron transport and improve the separation efficiency of photo-generated carriers compared with pure samples.In addition,the holes and superoxide radicals are dominating active species during the photocatalytic degradation process.展开更多
Novel WO3/g-C3N4/Ni（OH）x hybrids have been successfully synthesized by a two-step strategy of high temperature calcination and in situ photodeposition.Their photocatalytic performance was investigated using TEOA as ...Novel WO3/g-C3N4/Ni（OH）x hybrids have been successfully synthesized by a two-step strategy of high temperature calcination and in situ photodeposition.Their photocatalytic performance was investigated using TEOA as a hole scavenger under visible light irradiation.The loading of WO3 and Ni（OH）x cocatalysts boosted the photocatalytic H2 evolution efficiency of g-C3N4.WO3/g-C3N4/Ni（OH）x with 20 wt%defective WO3 and 4.8 wt%Ni（OH）x showed the highest hydrogen production rate of 576 μmol/（g·h）,which was 5.7,10.8 and 230 times higher than those of g-C3N4/4.8 wt%Ni（OH）x,20 wt%WO3/C3N4 and g-C3N4 photocatalysts,respectively.The remarkably enhanced H2 evolution performance was ascribed to the combination effects of the Z-scheme heterojunction（WO3/g-C3N4） and loaded cocatalysts（Ni（OH）x）,which effectively inhibited the recombination of the photoexcited electron-hole pairs of g-C3N4 and improved both H2 evolution and TEOA oxidation kinetics.The electron spin resonance spectra of ·O2^- and ·OH radicals provided evidence for the Z-scheme charge separation mechanism.The loading of easily available Ni（OH）x cocatalysts on the Z-scheme WO3/g-C3N4 nanocomposites provided insights into constructing a robust multiple-heterojunction material for photocatalytic applications.展开更多
基金Funded by the Natural Science Foundation of Hebei Province,China(Nos.E2019210251 and B2019210331).
文摘The CdS/spherical g-C3N4 n-n heterojunction photocatalyst was fabricated via a solvothermal method.The tetracycline was used to characterize the photocatalytic properties of the as-developed hybrids.The photocatalytic degradation mechanism of the as-developed heterojunction photocatalyst was also analyzed.Research results show that CdS nanoparticles are well dispersed in the surface layer of spherical g-C3N4.Moreover,the mass ratio of CdS to spherical g-C3N4 will influence the photocatalytic activity of the asdeveloped composites,which shows the trend of first increasing and then decreasing as it increased.When the mass ratio is 7:1,in 25 min,the as-developed heterojunction shows 93.2%of the maximum photocatalytic efficiency and still exhibits 83.6%after 5 times cycle testing.Moreover,the as-developed hybrids can accelerate the electron transport and improve the separation efficiency of photo-generated carriers compared with pure samples.In addition,the holes and superoxide radicals are dominating active species during the photocatalytic degradation process.
基金supported by the National Natural Science Foundation of China (51672089)the Industry and Research Collaborative Innovation Major Projects of Guangzhou (201508020098)+1 种基金the State Key Laboratory of Advanced Technology for Material Synthesis and Processing (Wuhan University of Technology) (2015-KF-7)the Hunan Key Laboratory of Applied Environmental Photocatalysis (Changsha University) (CCSU-XT-04)~~
文摘Novel WO3/g-C3N4/Ni（OH）x hybrids have been successfully synthesized by a two-step strategy of high temperature calcination and in situ photodeposition.Their photocatalytic performance was investigated using TEOA as a hole scavenger under visible light irradiation.The loading of WO3 and Ni（OH）x cocatalysts boosted the photocatalytic H2 evolution efficiency of g-C3N4.WO3/g-C3N4/Ni（OH）x with 20 wt%defective WO3 and 4.8 wt%Ni（OH）x showed the highest hydrogen production rate of 576 μmol/（g·h）,which was 5.7,10.8 and 230 times higher than those of g-C3N4/4.8 wt%Ni（OH）x,20 wt%WO3/C3N4 and g-C3N4 photocatalysts,respectively.The remarkably enhanced H2 evolution performance was ascribed to the combination effects of the Z-scheme heterojunction（WO3/g-C3N4） and loaded cocatalysts（Ni（OH）x）,which effectively inhibited the recombination of the photoexcited electron-hole pairs of g-C3N4 and improved both H2 evolution and TEOA oxidation kinetics.The electron spin resonance spectra of ·O2^- and ·OH radicals provided evidence for the Z-scheme charge separation mechanism.The loading of easily available Ni（OH）x cocatalysts on the Z-scheme WO3/g-C3N4 nanocomposites provided insights into constructing a robust multiple-heterojunction material for photocatalytic applications.