Spherical YAG：Ce^3＋ phosphor particles with narrow size distribution were prepared by spray pyrolysis. The effects of the concentration of solution, the flow rate of cartier gas and the annexing temperature on the p...Spherical YAG：Ce^3＋ phosphor particles with narrow size distribution were prepared by spray pyrolysis. The effects of the concentration of solution, the flow rate of cartier gas and the annexing temperature on the phosphor morphology were studied. The productivity of precursor particles shows a trend of drop after rising with the increase of concentration Raising the flow rate of nitrogen can improve the productivity of the precursor particles. Phosphor prepared by spray pyrolysis has obviously higher emission intensity than that synthesized by solid state reaction, spray pyrolysis makes Ce^3＋ ions well distributed in the crystal lattice as the luminescent centers, and phosphor particles have regular sphericity and narrow size distribution.展开更多
Y 0.9-xGd xEu 0.1BO 3 phosphors were synthesized by spray drying (SD) method, and the results were compared with those by conventional solid state (SS) and citrate gel (CG) methods. The PL intensity of phospho...Y 0.9-xGd xEu 0.1BO 3 phosphors were synthesized by spray drying (SD) method, and the results were compared with those by conventional solid state (SS) and citrate gel (CG) methods. The PL intensity of phosphors increases with the increase of x value in Y 0.9-xGd xEu 0.1BO 3 (prepared by SD) due to an energy migration process like Gd 3+-(Gd 3+) n-Eu 3+ occurred in the material. Compared with the latter two methods, the phosphor particles prepared by spray drying method have a better morphology, such as homogeneous size (about 1～3 μm) with spherical shape and smooth surface. Furthermore, the spray drying-derived phosphors have higher photoluminescence (PL) intensity than those by citrate gel method, but still a little lower than those by the solid state method.展开更多
基金Project supported by National "The Tenth Five-Year"plan (2003BA316A01-03-05) and "The Tenth Five-Year"Plan(BE2004021) of Jiangsu provicce
文摘Spherical YAG：Ce^3＋ phosphor particles with narrow size distribution were prepared by spray pyrolysis. The effects of the concentration of solution, the flow rate of cartier gas and the annexing temperature on the phosphor morphology were studied. The productivity of precursor particles shows a trend of drop after rising with the increase of concentration Raising the flow rate of nitrogen can improve the productivity of the precursor particles. Phosphor prepared by spray pyrolysis has obviously higher emission intensity than that synthesized by solid state reaction, spray pyrolysis makes Ce^3＋ ions well distributed in the crystal lattice as the luminescent centers, and phosphor particles have regular sphericity and narrow size distribution.
文摘Y 0.9-xGd xEu 0.1BO 3 phosphors were synthesized by spray drying (SD) method, and the results were compared with those by conventional solid state (SS) and citrate gel (CG) methods. The PL intensity of phosphors increases with the increase of x value in Y 0.9-xGd xEu 0.1BO 3 (prepared by SD) due to an energy migration process like Gd 3+-(Gd 3+) n-Eu 3+ occurred in the material. Compared with the latter two methods, the phosphor particles prepared by spray drying method have a better morphology, such as homogeneous size (about 1～3 μm) with spherical shape and smooth surface. Furthermore, the spray drying-derived phosphors have higher photoluminescence (PL) intensity than those by citrate gel method, but still a little lower than those by the solid state method.