Highly Improved Electrochemical Performances of the Nanocrystalline and Amorphous Mg_2Ni-type Alloys by Substituting Ni with M (M=Cu,Co,Mn)

The element Ni in the Mg2Ni alloy is partially substituted by M（M = Cu, Co, Mn） in order to ameliorate the electrochemical hydrogen storage performances of Mg2Ni-type electrode alloys. The nanocrystalline and amorphous Mg20Ni10-xMx（M = None, Cu, Co, Mn; x = 0-4） alloys were prepared by melt spinning. The effects of the M（M = Cu, Co, Mn） content on the structures and electrochemical hydrogen storage characteristics of the as-cast and spun alloys were comparatively studied. The analyses by XRD, SEM and HRTEM reveal that all the as-cast alloys have a major phase of Mg2Ni but the M（M = Co, Mn） substitution brings on the formation of some secondary phases, MgCo2 and Mg for the（M = Co） alloy, and Mn Ni and Mg for the（M = Mn） alloy. Besides, the as-spun（M = None, Cu） alloys display an entirely nanocrystalline structure, whereas the as-spun（M = Co, Mn） alloys hold a nanocrystalline/amorphous structure, suggesting that the substitution of M（M = Co, Mn） for Ni facilitates the glass formation in the Mg2Ni-type alloys. The electrochemical measurements indicate that the variation of M（M = Cu, Co, Mn） content engenders an obvious effect on the electrochemical performances of the as-cast and spun alloys. To be specific, the cyclic stabilities of the alloys augment monotonously with increasing M（M = Cu, Co, Mn） content, and the capacity retaining rate（S20） is in an order of（M = Cu） 〉（M = Co） 〉（M = Mn） 〉（M = None） for x≤1 but changes to（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None） for x≥2. The discharge capacities of the as-cast and spun alloys always grow with the rising of M（M = Co, Mn） content but first mount up and then go down with increasing M（M = Cu） content. Whatever the M content is, the discharge capacities are in sequence：（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None）. The high rate discharge abilities（HRDs） of all the alloys grow clearly with rising M（M = Cu, Co） content except for（M = Mn） alloy, whose HRD has a maximum value with varying M（M = Mn） content. Furthermore, for the as-cast alloys, the HRD is in order of（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None）, while for the as-spun（20 m·s^-1） alloys, it changes from（M = Co） 〉（M = Mn） 〉（M = Cu） 〉（M = None） for x = 1 to（M = Cu） 〉（M = Co） 〉（M = None） 〉（M = Mn） for x = 4.

Metal Fe,Ni and Fe-Ni Fine Fibers Derived from the Organic Gel-Thermal Reduction Process

The organic gel-thermal reduction process was successfully used for the preparation of magnetic metal Ni, Fe, Fe-Ni fine fibers from raw materials of citric acid or lactic acid and metal salts. Ni, Fe and Fe-Ni fine fibers synthesized were featured with diameters of around 1 μm and lengths of as long as 2 m for Ni fibers, 0.5 m for iron fibers, 1 m for Fe-Ni fibers. The structure, thermal decomposition process and morphologies of the gel precursors and fibers derived from thermal reduction of these gel precursors were characterized by FTIR, XRD,TG/DSC and SEM, respectively. The gel spinnability largely depends on molecular structures of metal-carboxylate complexes formed in the gel. It is reasoned that these gels consist of linear-type structural molecules [（C6H6O7）Ni]n or [（C6H5O7）2Ni3] for the nickel citrate gel, [（C3H5O3）3Fe] for the ferric lactate gel, [（C6H5O7）5（NiFe）3] for the iron-nickel citrate gel respectively and the gels obtain showed a good spinning performance.

Cotton Spinning Industry Reports Continued Growth (Part B) Analysis of economic performance of China's cotton spinning industry in Q1-Q3 (Continued from Nov. 15, 2010)

Manufacturing and sales According to data collected from 11,934 statistics-worthy Chinese cotton spinning enterprises surveyed by National Bureau of Statistics of China, total industrial production value of the industry increased 27.39

Electrochemical Performance of Nanocrystalline and Amorphous Mg–Nd–Ni–Cu-Based Mg_2Ni-type Alloy Electrodes Used in Ni-MH Batteries

Nanocrystalline and amorphous Mg2Ni-type（Mg24Ni10Cu2）100–xNdx（x = 0, 5, 10, 15, 20） alloys were prepared by melt-spinning technology. The structures of as-cast and spun alloys were characterised by X-ray diffraction,scanning electron microscopy and transmission electron microscopy. Electrochemical performance of the alloy electrodes was measured using an automatic galvanostatic system. The electrochemical impedance spectra and Tafel polarisation curves of the alloy electrodes were plotted using an electrochemical work station. The hydrogen diffusion coefficients were calculated using the potential step method. Results indicate that all the as-cast alloys present a multiphase structure with Mg2 Ni type as the major phase with Mg6 Ni, Nd5Mg41 and Nd Ni as secondary phases. The secondary phases increased with the increasing Nd content. The as-spun Nd-free alloy exhibited nanocrystalline structure, whereas the as-spun Nd-doped alloys exhibited nanocrystalline and amorphous structures. These results suggest that adding Nd facilitates glass formation of Mg2Ni-type alloys. Melt spinning and Nd addition improved alloy electrochemical performance, which includes discharge potential characteristics, discharge capacity, electrochemical cycle stability and high-rate discharge ability.