The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at e...The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at early stage when the CaF2 content was greater than 30 wt%, followed by a modification to the aluminosilicate-type inclusions. Because the slag was saturated by MgO, the activity of MgO was unity irrespective of CaF2 content in the slag. Thus, Mg was transferred from slag to metal phase. Mg transferred to molten steel reacted with Al2O3-rich inclusions to form MgO.Al2O3 spinel. However, the spinel inclusion was modified to aluminosilicate-type inclusions by the reaction with Si and Ca transferred from slag to molten steel about 2-3 h later.展开更多
Refining process of 430 stainless steel in AOD （argon oxygen decarburization） was simulated under the experimental condition. Al was chosen as deoxidizer, Mg-Al alloy was added in process of refining, and slag used ...Refining process of 430 stainless steel in AOD （argon oxygen decarburization） was simulated under the experimental condition. Al was chosen as deoxidizer, Mg-Al alloy was added in process of refining, and slag used in oxidation period of AOD was chosen in the experiments. The variation of total oxygen content, the size, morphology and composition of inclusions in refining process and the mechanical properties, pitting corrosion resistance of final samples were studied. The results show that no obvious differences in total oxygen content were observed among all the experiments. Neither chain nor cluster Al_2O_3 inclusions were found in refining process of experiments treated by Mg-Al alloys, the average size of inclusions in the steel treated by Mg-Al alloys was less than that of inclusions in steel not treated by Mg-Al alloy. 430 stainless steel treated by Mg-Al alloy shows better tensile strength, yield strength, and pitting resistance than that in the contrast experiment.展开更多
文摘The influence of CaF2 content on the formation behavior of spinel inclusions in the Ni-Cr-V-alloyed special steel was presented. The spinel was not formed at CaF2 content lower than 10 wt%. However, it was formed at early stage when the CaF2 content was greater than 30 wt%, followed by a modification to the aluminosilicate-type inclusions. Because the slag was saturated by MgO, the activity of MgO was unity irrespective of CaF2 content in the slag. Thus, Mg was transferred from slag to metal phase. Mg transferred to molten steel reacted with Al2O3-rich inclusions to form MgO.Al2O3 spinel. However, the spinel inclusion was modified to aluminosilicate-type inclusions by the reaction with Si and Ca transferred from slag to molten steel about 2-3 h later.
基金Sponsored by National Natural Science Foundation of China(50704010)Fundamental Research Funds for Central Universities of China(090402019)
文摘Refining process of 430 stainless steel in AOD （argon oxygen decarburization） was simulated under the experimental condition. Al was chosen as deoxidizer, Mg-Al alloy was added in process of refining, and slag used in oxidation period of AOD was chosen in the experiments. The variation of total oxygen content, the size, morphology and composition of inclusions in refining process and the mechanical properties, pitting corrosion resistance of final samples were studied. The results show that no obvious differences in total oxygen content were observed among all the experiments. Neither chain nor cluster Al_2O_3 inclusions were found in refining process of experiments treated by Mg-Al alloys, the average size of inclusions in the steel treated by Mg-Al alloys was less than that of inclusions in steel not treated by Mg-Al alloy. 430 stainless steel treated by Mg-Al alloy shows better tensile strength, yield strength, and pitting resistance than that in the contrast experiment.