The glass-ceramics were prepared with the spodumene mineral as the main raw material,and the effects of ZrO_(2)replacing TiO_(2)on the samples were systematically investigated.The results show that the substitution of...The glass-ceramics were prepared with the spodumene mineral as the main raw material,and the effects of ZrO_(2)replacing TiO_(2)on the samples were systematically investigated.The results show that the substitution of ZrO_(2)for TiO_(2)is not conductive to precipitate𝛽β-quartz solid solution phase,but can improve the transparency and flexural strength of glass-ceramics.And the glass-ceramic with the highest visible light transmittance(87%)and flexural strength(231.80 MPa)exhibits an ultra-low thermal expansion of-0.028×10^(-7)K^(-1)in the region of 30-700℃.展开更多
In this paper ,spodumene mineral was used as raw material for fabricating glass ceramic with the addition of MgO,ZnO and TiO2,ZrO2. The expansion coefficient of the materials is 5. 5×107/℃ . Also the effects of ...In this paper ,spodumene mineral was used as raw material for fabricating glass ceramic with the addition of MgO,ZnO and TiO2,ZrO2. The expansion coefficient of the materials is 5. 5×107/℃ . Also the effects of the heat treatment on the crystallzing behaviour has been discussed by XRD and DTA.展开更多
文摘The glass-ceramics were prepared with the spodumene mineral as the main raw material,and the effects of ZrO_(2)replacing TiO_(2)on the samples were systematically investigated.The results show that the substitution of ZrO_(2)for TiO_(2)is not conductive to precipitate𝛽β-quartz solid solution phase,but can improve the transparency and flexural strength of glass-ceramics.And the glass-ceramic with the highest visible light transmittance(87%)and flexural strength(231.80 MPa)exhibits an ultra-low thermal expansion of-0.028×10^(-7)K^(-1)in the region of 30-700℃.
文摘In this paper ,spodumene mineral was used as raw material for fabricating glass ceramic with the addition of MgO,ZnO and TiO2,ZrO2. The expansion coefficient of the materials is 5. 5×107/℃ . Also the effects of the heat treatment on the crystallzing behaviour has been discussed by XRD and DTA.