Bi-doped SiO2-Al2O3-GeO2 fiber preforms are prepared by modified chemical vapor deposition （MCVD） and solution doping process. The characteristic spectra of the preforms and fibers are experimentally investigated, a...Bi-doped SiO2-Al2O3-GeO2 fiber preforms are prepared by modified chemical vapor deposition （MCVD） and solution doping process. The characteristic spectra of the preforms and fibers are experimentally investigated, and a distinct difference in emission between the two is observed. Under 808-nm excitation, an ultra-broad near-infrared （NIR） emission with full-width at half-maximum （FWHM） of 495 nm is observed in the Bi-doped fiber. This observation, to our knowledge, is the first in this field. The NIR emission consists of two bands, which may be ascribed to the Bi0 and Bi＋ species, respectively. This Bi-doDed fiber is promising for broadband or）tical amolification and widely tunable laser.展开更多
为找出光纤预制棒废料中提取的白炭黑的改性效果好的硅烷偶联剂,用KH-560、KH-151、KH-171、KH-602和CG-551等10种硅烷偶联剂对该白炭黑进行改性。白炭黑在140℃下活化20 h,将活化的白炭黑3 g分别与10种不同的偶联剂0.3 m L在45 m L二...为找出光纤预制棒废料中提取的白炭黑的改性效果好的硅烷偶联剂,用KH-560、KH-151、KH-171、KH-602和CG-551等10种硅烷偶联剂对该白炭黑进行改性。白炭黑在140℃下活化20 h,将活化的白炭黑3 g分别与10种不同的偶联剂0.3 m L在45 m L二甲苯溶剂中130℃加热搅拌13 h,离心分离后,固体样品加适量的无水乙醇洗涤烘干后即得到改性的白炭黑。改性后样品的沉降性、亲油化度、表面羟基数等实验结果表明,10种硅烷偶联剂都能对白炭黑进行改性,其中KH-560、CG-8030、KH-151、KH-171、KH-172、KH-570对白炭黑的改性效果优于含氨基或巯基的KH-602、KH-792、CG-551、KH-550等。展开更多
文摘Bi-doped SiO2-Al2O3-GeO2 fiber preforms are prepared by modified chemical vapor deposition （MCVD） and solution doping process. The characteristic spectra of the preforms and fibers are experimentally investigated, and a distinct difference in emission between the two is observed. Under 808-nm excitation, an ultra-broad near-infrared （NIR） emission with full-width at half-maximum （FWHM） of 495 nm is observed in the Bi-doped fiber. This observation, to our knowledge, is the first in this field. The NIR emission consists of two bands, which may be ascribed to the Bi0 and Bi＋ species, respectively. This Bi-doDed fiber is promising for broadband or）tical amolification and widely tunable laser.
文摘为找出光纤预制棒废料中提取的白炭黑的改性效果好的硅烷偶联剂,用KH-560、KH-151、KH-171、KH-602和CG-551等10种硅烷偶联剂对该白炭黑进行改性。白炭黑在140℃下活化20 h,将活化的白炭黑3 g分别与10种不同的偶联剂0.3 m L在45 m L二甲苯溶剂中130℃加热搅拌13 h,离心分离后,固体样品加适量的无水乙醇洗涤烘干后即得到改性的白炭黑。改性后样品的沉降性、亲油化度、表面羟基数等实验结果表明,10种硅烷偶联剂都能对白炭黑进行改性,其中KH-560、CG-8030、KH-151、KH-171、KH-172、KH-570对白炭黑的改性效果优于含氨基或巯基的KH-602、KH-792、CG-551、KH-550等。