A temperature stable Li2Zn0.95(SrxCa1-x)0.05Ti3O8(0≤x≤1)ceramics were fabricated using a conventional solid-state route sintered at 1100℃for 4 h.The XRD results indicate that the main phase Li2ZnTi3O8 and secondary...A temperature stable Li2Zn0.95(SrxCa1-x)0.05Ti3O8(0≤x≤1)ceramics were fabricated using a conventional solid-state route sintered at 1100℃for 4 h.The XRD results indicate that the main phase Li2ZnTi3O8 and secondary phase including SrxCa1-xTiO3(0≤x≤1)solid solution and TiO2 co-exist in composite and form a stable composite system when the(CaxSr1-x)(0≤x≤1)substitutes for Zn of Li2ZnTi3O8 ceramic.As x is increased from 0 to 1,the relative permittivity(εr)increases from 26.65 to 27.12,and the quality factor(Q×f)increases from 63300 to 66600 GHz.With the increased of x,the temperature coefficient of resonant frequency(τf)increases from 0.27 to 8.23 ppm/℃,and then decreases to 3.51 ppm/℃.On the whole,the Li2Zn0.95(SrxCa1-x)0.05Ti3O8(0≤x≤1)ceramics show excellent comprehensive properties of middleεr=25-27,higher Q×f≥60000 GHz andτf≤±8.5 ppm/℃.展开更多
基金Funded by the Open Project Program of Key Laboratory of Inorganic Functional Materials and Devices,Chinese Academy of Sciences(No.KLIFMD201606)the Open Fund of National Innovation Platform(No.2017YJ163)+1 种基金the National Natural Science Foundation of China(Nos.51502220,51521001,and 51672197)the Open Foundation of Hubei Key Laboratory of Theory and Application of Advanced Materials Mechanics(Wuhan University of Technology)(No.TAM201802)。
文摘A temperature stable Li2Zn0.95(SrxCa1-x)0.05Ti3O8(0≤x≤1)ceramics were fabricated using a conventional solid-state route sintered at 1100℃for 4 h.The XRD results indicate that the main phase Li2ZnTi3O8 and secondary phase including SrxCa1-xTiO3(0≤x≤1)solid solution and TiO2 co-exist in composite and form a stable composite system when the(CaxSr1-x)(0≤x≤1)substitutes for Zn of Li2ZnTi3O8 ceramic.As x is increased from 0 to 1,the relative permittivity(εr)increases from 26.65 to 27.12,and the quality factor(Q×f)increases from 63300 to 66600 GHz.With the increased of x,the temperature coefficient of resonant frequency(τf)increases from 0.27 to 8.23 ppm/℃,and then decreases to 3.51 ppm/℃.On the whole,the Li2Zn0.95(SrxCa1-x)0.05Ti3O8(0≤x≤1)ceramics show excellent comprehensive properties of middleεr=25-27,higher Q×f≥60000 GHz andτf≤±8.5 ppm/℃.