The low cycle fatigue behavior of zirconium−titanium−steel composite plate under symmetrical and asymmetric stress control was studied.The effects of mean stress and stress amplitude on cyclic deformation,ratcheting e...The low cycle fatigue behavior of zirconium−titanium−steel composite plate under symmetrical and asymmetric stress control was studied.The effects of mean stress and stress amplitude on cyclic deformation,ratcheting effect and damage mechanism were discussed in detail.The results show that under symmetric stress control,the forward ratcheting deformation is observed.Under asymmetric stress control,the ratcheting strain increases rapidly with mean stress and stress amplitude increasing.Under high stress amplitude,the influence of mean stress is more significant.In addition,by studying the variation of strain energy density,it is found that the stress amplitude mainly promotes the fatigue damage,while the mean stress leads to the ratcheting damage.In addition,fractographic observation shows that the crack initiates in the brittle metal compound at the interface,and the steel has higher resistance to crack propagation.Finally,the accuracy of life prediction model considering ratcheting effect is discussed in detail,and a high-precision life prediction model directly based on mean stress and stress amplitude is proposed.展开更多
Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure...Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.展开更多
In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carri...In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carried out by using the LS-DYNA software and SPH-FEM coupling algorithm in the present study.The explosive welding window is calculated and established.It is found that the numerical simulation results are in good agreement with the experimental results.The displacement,velocity and pressure-time curves of characteristic elements show that the quality of explosive welding composites is superior.It is proved that SPH-FEM coupling algorithm is effective for explosive welding of TA1/304 stainless steel and can effectively guide the selection of explosive welding parameters.展开更多
Two types of titanium/steel composite plates with the same thickness were manufactured by parallel explosive welding and double vertical explosive welding and rolling, respectively. The comparative analysis of microst...Two types of titanium/steel composite plates with the same thickness were manufactured by parallel explosive welding and double vertical explosive welding and rolling, respectively. The comparative analysis of microstructure showed that the interface of double vertical explosive welding plate （B plate） tended to be straight while the interface of parallel explosive welding plate （A plate） was wavy bonding. Defects near the interface of B plate were extruded, and the thickness of the diffusion layer of B plate was thicker under the effects of preheating temperature and press-working. Comparative tests of mechanical properties indicated that the tensile shear strength of B plate was lower while its micro-hardness was higher. Specimens of these two types of plates were neither separated nor cracked after bending up to 180° in the three-point bending test. From the microstructural observation of tensile fracture characteristics, A plate had strong toughness fracture while B plate had mainly ductile fracture with cleavage fracture as the supplement. Macroscopically, the tensile strength of the latter was 7.9% less than that of the former. However, both satisfied the Chinese standard of tensile strength.展开更多
The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative ...The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative model has been set up to investigate effect of the thickness of coating and/or substrate on the detectibility of debonging in SSCPs.Two parameters,namely the maximum defect temperature difference and defect appearing index,are defined to evaluate the detectivity of defects,and their computational methods and formulas are given respectively.The preliminary changing tendency of the maximum defect temperature difference and defect appearing index with the thickness of coating and/or substrate is found by numerical simulation.展开更多
基金the financial support from the National Natural Science Foundation of China(Nos.51975271,51675260,51475223)the Starting Research Fund of Nanjing Vocational University of Industry Technology,China(No.YK20-14-05)。
文摘The low cycle fatigue behavior of zirconium−titanium−steel composite plate under symmetrical and asymmetric stress control was studied.The effects of mean stress and stress amplitude on cyclic deformation,ratcheting effect and damage mechanism were discussed in detail.The results show that under symmetric stress control,the forward ratcheting deformation is observed.Under asymmetric stress control,the ratcheting strain increases rapidly with mean stress and stress amplitude increasing.Under high stress amplitude,the influence of mean stress is more significant.In addition,by studying the variation of strain energy density,it is found that the stress amplitude mainly promotes the fatigue damage,while the mean stress leads to the ratcheting damage.In addition,fractographic observation shows that the crack initiates in the brittle metal compound at the interface,and the steel has higher resistance to crack propagation.Finally,the accuracy of life prediction model considering ratcheting effect is discussed in detail,and a high-precision life prediction model directly based on mean stress and stress amplitude is proposed.
文摘Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.
基金Project was supported by the National Natural Science Foundation of China(Grant No.11902003).
文摘In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carried out by using the LS-DYNA software and SPH-FEM coupling algorithm in the present study.The explosive welding window is calculated and established.It is found that the numerical simulation results are in good agreement with the experimental results.The displacement,velocity and pressure-time curves of characteristic elements show that the quality of explosive welding composites is superior.It is proved that SPH-FEM coupling algorithm is effective for explosive welding of TA1/304 stainless steel and can effectively guide the selection of explosive welding parameters.
基金This project was sponsored by the National Natural Science Foundation of China （No. 51541112） and Special Fund Achievement Transformation Projects in Jiangsu of China （No. BA2012030）.
文摘Two types of titanium/steel composite plates with the same thickness were manufactured by parallel explosive welding and double vertical explosive welding and rolling, respectively. The comparative analysis of microstructure showed that the interface of double vertical explosive welding plate （B plate） tended to be straight while the interface of parallel explosive welding plate （A plate） was wavy bonding. Defects near the interface of B plate were extruded, and the thickness of the diffusion layer of B plate was thicker under the effects of preheating temperature and press-working. Comparative tests of mechanical properties indicated that the tensile shear strength of B plate was lower while its micro-hardness was higher. Specimens of these two types of plates were neither separated nor cracked after bending up to 180° in the three-point bending test. From the microstructural observation of tensile fracture characteristics, A plate had strong toughness fracture while B plate had mainly ductile fracture with cleavage fracture as the supplement. Macroscopically, the tensile strength of the latter was 7.9% less than that of the former. However, both satisfied the Chinese standard of tensile strength.
基金the National Natural Science Foundation of China(No.51075388)the Fundamental Research Funds for the Central Universities (No.2009KJ05)
文摘The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative model has been set up to investigate effect of the thickness of coating and/or substrate on the detectibility of debonging in SSCPs.Two parameters,namely the maximum defect temperature difference and defect appearing index,are defined to evaluate the detectivity of defects,and their computational methods and formulas are given respectively.The preliminary changing tendency of the maximum defect temperature difference and defect appearing index with the thickness of coating and/or substrate is found by numerical simulation.