The 2205 duplex stainless ＋ DH36 clad steel plate was welded by gas metal arc welding（GMAW）, and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the weldi...The 2205 duplex stainless ＋ DH36 clad steel plate was welded by gas metal arc welding（GMAW）, and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the welding procedure for the base metal of carbon steel, the transition layer, and the cladding material is excellent. The test results indicate that the phase proportion and component dilution of the GMAW-welded joints of clad steel plate can be effectively controlled to yield joints with good mechanical properties and corrosion resistance.展开更多
A stainless steel clad plate composed of stainless steel and carbon steel was prepared by vacuum hot rolling process, and its microstructure, especially the bonding interface, was evaluated using an optical microscope...A stainless steel clad plate composed of stainless steel and carbon steel was prepared by vacuum hot rolling process, and its microstructure, especially the bonding interface, was evaluated using an optical microscope, a scanning electron micro- scope and a transmission electron microscope （TEM）. The corresponding mechanical properties were also assessed by means of hardness and shear tests. The results showed a bonding interface formed between stainless steel and carbon steel, which was relatively straight in macroscope but serrated in microscope. Decarburization layer and carbon-enriched layer were distinguished at the side of carbon steel and stainless steel near the interface, respectively, which should be related to diffusion of carbon and alloying elements. The carbon-enriched layer could also be identified as a recombination region, whose microstructure was mainly recognized as martensite by TEM. Consequently, the hardness was the highest at this region. Furthermore, the result of shear test at the bonding interface showed that the shear strength was 395 MPa and the fracture mode was dominated as ductile fracture, indicating the bonding interface with good quality.展开更多
文摘The 2205 duplex stainless ＋ DH36 clad steel plate was welded by gas metal arc welding（GMAW）, and the welding performance of the clad steel plate was investigated. The results show that the adaptability of the welding procedure for the base metal of carbon steel, the transition layer, and the cladding material is excellent. The test results indicate that the phase proportion and component dilution of the GMAW-welded joints of clad steel plate can be effectively controlled to yield joints with good mechanical properties and corrosion resistance.
文摘A stainless steel clad plate composed of stainless steel and carbon steel was prepared by vacuum hot rolling process, and its microstructure, especially the bonding interface, was evaluated using an optical microscope, a scanning electron micro- scope and a transmission electron microscope （TEM）. The corresponding mechanical properties were also assessed by means of hardness and shear tests. The results showed a bonding interface formed between stainless steel and carbon steel, which was relatively straight in macroscope but serrated in microscope. Decarburization layer and carbon-enriched layer were distinguished at the side of carbon steel and stainless steel near the interface, respectively, which should be related to diffusion of carbon and alloying elements. The carbon-enriched layer could also be identified as a recombination region, whose microstructure was mainly recognized as martensite by TEM. Consequently, the hardness was the highest at this region. Furthermore, the result of shear test at the bonding interface showed that the shear strength was 395 MPa and the fracture mode was dominated as ductile fracture, indicating the bonding interface with good quality.
