The warm compacting behaviors of four different kinds of stainless steel powders,304L,316L,410L and 430L,were studied. The results show that warm compaction can be applied to stainless steel powders. The green densiti...The warm compacting behaviors of four different kinds of stainless steel powders,304L,316L,410L and 430L,were studied. The results show that warm compaction can be applied to stainless steel powders. The green densities and strengths of compacts obtained through warm compaction are generally higher than those obtai ned through cold compaction. The compacting behaviors in warm compaction and col d compaction are similar. Under the compacting pressure of 700 MPa,the warm co mpacted densities are 0.100.22 g/cm^3 higher than the cold compacted o nes,and the green strengths are 11.5%50% higher. The optimal warm compa cting temperature is 100110 ℃. In the die wall lubricated warm compact ion,the optimum internal lubricant content is 0.2%.展开更多
One kind of quenched Cr12 steel dies for impacting stainless steel wire rope （SSWR） was treated by low temperature liquid sulfurization catalyzed with rare earths, in order to extend their service life for assuring ...One kind of quenched Cr12 steel dies for impacting stainless steel wire rope （SSWR） was treated by low temperature liquid sulfurization catalyzed with rare earths, in order to extend their service life for assuring the continuity of production line, and simultaneously improve the surface quality of SSWR obtained. After immerged into the melting sulphur containing 4 % （mass fraction） of LaF3 and 1% of CeCl3 at 463 K for 4 h, the sulfurized dies were very smooth and black, with little distortion and hardness loss. They exhibited a certain extent of corrosion-resistance in air due to the coexisting rare earths in the sulfurized layer. Optical observations showed that the sulfurized layer was uniform and had scale-like structure. The trail of machined SSWR indicated that the production capacity of sulfurized dies had been doubled and the replacing period on line was postponed. SEM morphology also proved that the wear extent of cavities on sulfurized dies decreased greatly and the surface quality of SSWR obtained was improved markedly.展开更多
文摘The warm compacting behaviors of four different kinds of stainless steel powders,304L,316L,410L and 430L,were studied. The results show that warm compaction can be applied to stainless steel powders. The green densities and strengths of compacts obtained through warm compaction are generally higher than those obtai ned through cold compaction. The compacting behaviors in warm compaction and col d compaction are similar. Under the compacting pressure of 700 MPa,the warm co mpacted densities are 0.100.22 g/cm^3 higher than the cold compacted o nes,and the green strengths are 11.5%50% higher. The optimal warm compa cting temperature is 100110 ℃. In the die wall lubricated warm compact ion,the optimum internal lubricant content is 0.2%.
基金Project supported by the Natural Science Fund of Jiangsu Province (BK2002062)Startup Fund of Hohai University(2084/40501107)
文摘One kind of quenched Cr12 steel dies for impacting stainless steel wire rope （SSWR） was treated by low temperature liquid sulfurization catalyzed with rare earths, in order to extend their service life for assuring the continuity of production line, and simultaneously improve the surface quality of SSWR obtained. After immerged into the melting sulphur containing 4 % （mass fraction） of LaF3 and 1% of CeCl3 at 463 K for 4 h, the sulfurized dies were very smooth and black, with little distortion and hardness loss. They exhibited a certain extent of corrosion-resistance in air due to the coexisting rare earths in the sulfurized layer. Optical observations showed that the sulfurized layer was uniform and had scale-like structure. The trail of machined SSWR indicated that the production capacity of sulfurized dies had been doubled and the replacing period on line was postponed. SEM morphology also proved that the wear extent of cavities on sulfurized dies decreased greatly and the surface quality of SSWR obtained was improved markedly.