The current status of nitrogen containing stainless steels at home and aboard has been introduced. The function and existing forms of nitrogen in the stainless steels, influence of nitrogen on mechanical properties an...The current status of nitrogen containing stainless steels at home and aboard has been introduced. The function and existing forms of nitrogen in the stainless steels, influence of nitrogen on mechanical properties and anti-corrosion properties as well as the application of nitrogen containing cast stainless steels were discussed in this paper. It is clear that nitrogen will be a potential and important alloying element in stainless steels. And Argon Oxygen Decarbonization (AOD) refining can provide an advanced manufacture process for nitrogen containing stainless steels with ultra-low- carbon and high cleanliness.展开更多
Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added ...Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.展开更多
Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2...Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2.0×1017ions·cm-2. The saturation dose of Cu implantation in AISI420 SS and Cu surface concentration were calculated at the energy of 100keV. The effect of dose on the antibacterial activity was analyzed. Results of antibacterial test show that the saturation dose is the optimum implantation dose for best antibacterial activity, which is above 99% against both Escherichia coli and Staphylococcus aureus. Novel phases such as Fe4Cu3 and Cu9.9Fe0.1 were found in the implanted layer by glancing angle X-ray diffraction (GXRD). The antibacterial activity of AISI420 SS attributes to Cu-contained phase.展开更多
Nickel-containing stainless steels have been widely applied in watch and jewelry production, and their re- sponses to the Nickel Directive become a universal concern in the industry. The nickel release rates and corro...Nickel-containing stainless steels have been widely applied in watch and jewelry production, and their re- sponses to the Nickel Directive become a universal concern in the industry. The nickel release rates and corrosion be- haviors of types 316L, 304, 303 and 201 stainless steels under the conditions of solid solution and mirror polishing were studied by artificial sweat soaking and electrochemical methods. The results show that the weekly nickel release rates in artificial sweat do not strictly correspond to the nickel contents, which present a descending order as 303 stainless steel of 2.06 μg/cm2 , 201 stainless steel of 1.51 μg/cm2 , 304 stainless steel of 0.08μg/cm2 and 316L stainless steel of 0.02 μg/cm2. Both the nickel release rates of type 303 and 201 stainless steels significantly exceed the threshold values regulated in EN1811 ： 2011 ; therefore, they should be avoided to be used as watch and jewelry materials owing to the risk of nickel sensitization. The nickel release rates of 316L and 304 stainless steels meet the requirements of the standard. Sulfide inclusions in stainless steel become the sources of pitting and exacerbate the damage of the passivation membrane, which is the significant cause to enhance the nickel release rates.展开更多
文摘The current status of nitrogen containing stainless steels at home and aboard has been introduced. The function and existing forms of nitrogen in the stainless steels, influence of nitrogen on mechanical properties and anti-corrosion properties as well as the application of nitrogen containing cast stainless steels were discussed in this paper. It is clear that nitrogen will be a potential and important alloying element in stainless steels. And Argon Oxygen Decarbonization (AOD) refining can provide an advanced manufacture process for nitrogen containing stainless steels with ultra-low- carbon and high cleanliness.
基金supported by National Basic Research Program of China (973 Program, Grant No. 2006CB605005)Shanghai Municipal Committee of Science and Technology of china(Grant No. 005207019,Grant No. 08520708000)
文摘Stress corrosion cracking （SCC） of stainless steels and Ni-based alloys in high temperature water coolant is one of the key problems affecting the safe operation of nuclear power plants （NPPs）. The nitrogen-added stainless steel is a kind of possible candidate materials for mitigating SCC since reducing the carbon content and adding nitrogen to offset the loss in strength caused by the decrease in carbon content can mitigate the problem of sensitization. However, the reports of SCC of nitrogen-added stainless steels in high temperature water are few available. The effects of applied potential and sensitization treatment on the SCC of a newly developed nitrogen-containing stainless steel （SS） 316LN in high temperature water doped with chloride at 250 ℃ were studied by using slow strain rate tests （SSRTs）. The SSRT results are compared with our data previously published for 316 SS without nitrogen and 304NG SS with nitrogen, and the possible mechanism affecting the SCC behaviors of the studied steels is also discussed based on SSRT and microstucture analysis results. The susceptibility to cracking of 316LN SS normally increases with increasing potential. The susceptibility to SCC of 316LN SS was less than that of 316 SS and 304NG SS. Sensitization treatment at 700℃ for 30 h showed little effect on the S CC of 316LN S S and significant effect on the S CC of 316 S S. The predominant cracking mode for the 316LN S S in both annealed state and the state after the sensitization treatment was transgranular. The presented conditions of mitigating stress corrosion cracking are some useful information for the safe use of 316LN SS in NPPs.
基金This work was supported by the National Natural Science Foundation of China(No.50101009)
文摘Antibacterial activity of AISI420 stainless steel (SS) implanted by copper was investigated. Ions extracted from a metal vapor vacuum arc (MEVVA) are sourced with 100keV energy and a dose range from 0.2×1017 to 2.0×1017ions·cm-2. The saturation dose of Cu implantation in AISI420 SS and Cu surface concentration were calculated at the energy of 100keV. The effect of dose on the antibacterial activity was analyzed. Results of antibacterial test show that the saturation dose is the optimum implantation dose for best antibacterial activity, which is above 99% against both Escherichia coli and Staphylococcus aureus. Novel phases such as Fe4Cu3 and Cu9.9Fe0.1 were found in the implanted layer by glancing angle X-ray diffraction (GXRD). The antibacterial activity of AISI420 SS attributes to Cu-contained phase.
基金financially supported by the foundation of Jewelry Engineering Technology Development Center of Guangdong Colleges and Universities(item No.131,Yue Edu.Sci)
文摘Nickel-containing stainless steels have been widely applied in watch and jewelry production, and their re- sponses to the Nickel Directive become a universal concern in the industry. The nickel release rates and corrosion be- haviors of types 316L, 304, 303 and 201 stainless steels under the conditions of solid solution and mirror polishing were studied by artificial sweat soaking and electrochemical methods. The results show that the weekly nickel release rates in artificial sweat do not strictly correspond to the nickel contents, which present a descending order as 303 stainless steel of 2.06 μg/cm2 , 201 stainless steel of 1.51 μg/cm2 , 304 stainless steel of 0.08μg/cm2 and 316L stainless steel of 0.02 μg/cm2. Both the nickel release rates of type 303 and 201 stainless steels significantly exceed the threshold values regulated in EN1811 ： 2011 ; therefore, they should be avoided to be used as watch and jewelry materials owing to the risk of nickel sensitization. The nickel release rates of 316L and 304 stainless steels meet the requirements of the standard. Sulfide inclusions in stainless steel become the sources of pitting and exacerbate the damage of the passivation membrane, which is the significant cause to enhance the nickel release rates.