Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure...Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.展开更多
Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thi...Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316 L substrate. The corrosion resistance of this film in 0.5 mol·L^（-1） H_2SO_4 solution containing 5 ppm F- at 80°C was investigated using polarization tests. The results showed that the surface treatment of the SS316 L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316 L, the Ag-doped carbon-coated SS316 L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell（PEMFC） and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 m？·cm^2 to 21.6 m？·cm^2 at a compaction pressure of 1.2 MPa.展开更多
The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the...The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the base materials, the microstructure of nickel cladding is observed by scanning electron microscopy （SEM） at high, and room temperature, and the results show that the nickel cladding on base material can be protected from oxidation in the high temperature. Non-vacuum roll bonding tests of nickel plating on base materials are done by the roll bonding equipment, and the roll bonding plates of stainless/carbon steel are obtained. The microstructure and the elements distribution of non-vacuum roll bonding interface are analyzed by optical microscope （OM） and SEM. The results reflect that the nickel plating layer and the base materials bond well.展开更多
The objective of this work is to investigate the fatigue behavior of reinforced concrete(RC) beams strengthened with externally bonded carbon fiber reinforced polymer(CFRP) and steel plate. An experimental investigati...The objective of this work is to investigate the fatigue behavior of reinforced concrete(RC) beams strengthened with externally bonded carbon fiber reinforced polymer(CFRP) and steel plate. An experimental investigation and theoretical analysis were made on the law of deflection development and stiffness degradation, as well as the influence of fatigue load ranges. Test results indicate that the law of three-stage change under fatigue loading is followed by both midspan deflection and permanent deflection, which also have positive correlation with fatigue load amplitude. Fatigue stiffness of composite strengthened beams degrades gradually with the increasing of number of cycles. Based on the experimental results, a theoretical model by effective moment of inertia method is developed for calculating the sectional stiffness of such composite strengthened beams under fatigue loading, and the calculated results are in good agreement with the experimental results.展开更多
In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carri...In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carried out by using the LS-DYNA software and SPH-FEM coupling algorithm in the present study.The explosive welding window is calculated and established.It is found that the numerical simulation results are in good agreement with the experimental results.The displacement,velocity and pressure-time curves of characteristic elements show that the quality of explosive welding composites is superior.It is proved that SPH-FEM coupling algorithm is effective for explosive welding of TA1/304 stainless steel and can effectively guide the selection of explosive welding parameters.展开更多
The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative ...The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative model has been set up to investigate effect of the thickness of coating and/or substrate on the detectibility of debonging in SSCPs.Two parameters,namely the maximum defect temperature difference and defect appearing index,are defined to evaluate the detectivity of defects,and their computational methods and formulas are given respectively.The preliminary changing tendency of the maximum defect temperature difference and defect appearing index with the thickness of coating and/or substrate is found by numerical simulation.展开更多
文摘Effect of annealing on "fly-line"(adiabatic sheer line) microstructure and properties of explosively composited stainless steel-stainless steel plates was studied.Results show that the flyline microstructure will diminish through certain annealing process,while the cracks formed from fly-line microstructure will remain.Therefore,fly-line microstructure can be considered as a plastic deformation microstructure and crack source s meanwhile its formation is considered as a special plastic deformation mechanism of metal under explosive load.
基金financially supported by the National Natural Science Foundation of China(No.21106012)the Educational Department Foundation of Liaoning Province of China(NO.L2014180)
文摘Ni–Cr enrichment on stainless steel SS316 L resulting from chemical activation enabled the deposition of carbon by spraying a stable suspension of carbon nanoparticles; trace Ag was deposited in situ to prepare a thin continuous Ag-doped carbon film on a porous carbon-coated SS316 L substrate. The corrosion resistance of this film in 0.5 mol·L^（-1） H_2SO_4 solution containing 5 ppm F- at 80°C was investigated using polarization tests. The results showed that the surface treatment of the SS316 L strongly affected the adhesion of the carbon coating to the stainless steel. Compared to the bare SS316 L, the Ag-doped carbon-coated SS316 L bipolar plate was remarkably more stable in both the anode and cathode environments of proton exchange membrane fuel cell（PEMFC） and the interface contact resistance between the specimen and Toray 060 carbon paper was reduced from 333.0 m？·cm^2 to 21.6 m？·cm^2 at a compaction pressure of 1.2 MPa.
文摘The non-vacuum roll bonding method of nickel plating on the base materials is put forward in accordance with the primary problems existed in the roll bonding of stainless/carbon steel. After nickel plating test on the base materials, the microstructure of nickel cladding is observed by scanning electron microscopy （SEM） at high, and room temperature, and the results show that the nickel cladding on base material can be protected from oxidation in the high temperature. Non-vacuum roll bonding tests of nickel plating on base materials are done by the roll bonding equipment, and the roll bonding plates of stainless/carbon steel are obtained. The microstructure and the elements distribution of non-vacuum roll bonding interface are analyzed by optical microscope （OM） and SEM. The results reflect that the nickel plating layer and the base materials bond well.
基金Project(51108355)supported by the National Natural Science Foundation of ChinaProject(2011CDB269)supported by the Natural Science Foundation of Hubei Province,China
文摘The objective of this work is to investigate the fatigue behavior of reinforced concrete(RC) beams strengthened with externally bonded carbon fiber reinforced polymer(CFRP) and steel plate. An experimental investigation and theoretical analysis were made on the law of deflection development and stiffness degradation, as well as the influence of fatigue load ranges. Test results indicate that the law of three-stage change under fatigue loading is followed by both midspan deflection and permanent deflection, which also have positive correlation with fatigue load amplitude. Fatigue stiffness of composite strengthened beams degrades gradually with the increasing of number of cycles. Based on the experimental results, a theoretical model by effective moment of inertia method is developed for calculating the sectional stiffness of such composite strengthened beams under fatigue loading, and the calculated results are in good agreement with the experimental results.
基金Project was supported by the National Natural Science Foundation of China(Grant No.11902003).
文摘In order to guide the explosive welding experiment of titanium-stainless steel,Three-dimensional numerical simulation of explosive welding,which select TA1 as flyer plate and 304 stainless steel as base plate,is carried out by using the LS-DYNA software and SPH-FEM coupling algorithm in the present study.The explosive welding window is calculated and established.It is found that the numerical simulation results are in good agreement with the experimental results.The displacement,velocity and pressure-time curves of characteristic elements show that the quality of explosive welding composites is superior.It is proved that SPH-FEM coupling algorithm is effective for explosive welding of TA1/304 stainless steel and can effectively guide the selection of explosive welding parameters.
基金the National Natural Science Foundation of China(No.51075388)the Fundamental Research Funds for the Central Universities (No.2009KJ05)
文摘The non-destructive testing(NDT)of debonding in stainless steel composites plate(SSCP)is performed by infrared thermography,finite element analysis(FEA)software ANSYS is taken as the simulative tool,and 2D simulative model has been set up to investigate effect of the thickness of coating and/or substrate on the detectibility of debonging in SSCPs.Two parameters,namely the maximum defect temperature difference and defect appearing index,are defined to evaluate the detectivity of defects,and their computational methods and formulas are given respectively.The preliminary changing tendency of the maximum defect temperature difference and defect appearing index with the thickness of coating and/or substrate is found by numerical simulation.