A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution bin...A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution binder,followed by casting infiltration to prepare the ZTA particles reinforced high chromium cast iron(HCCI)composites.The result reveals that a distinct interface layer forms at the ZTA/HCCI interface,which consists of phases of ZrB_(2),FeB,Fe_(2)B,and NaSiO_(4).The interfacial wettability between ZTA and HCCI is improved by the diffusion and reaction of Ni and B_(4)C.The wear test reveals that the Ni-B_(4)C plated ZTA particles can effectively improve the wear resistance of the ZTA/HCCI composite,and the wear rate of the composite is decreased to 11.6%of HCCI.展开更多
The effects of RE, V, Ti and B on the microstructure and properties of high chromium cast iron containing 3% molybdenum under as-cast and heat treatment conditions were investigated with the method of comparing experi...The effects of RE, V, Ti and B on the microstructure and properties of high chromium cast iron containing 3% molybdenum under as-cast and heat treatment conditions were investigated with the method of comparing experiments. The results show that with the increase of RE content, the primary austenite of high chromium cast iron is obviously refined. The morphology of carbide is changed from netlike and lath to small multiangular isolated blocks or massive blocks, the isolated degree of carbide is improved obviously, and the size is significantly refined. The addition of V and B into high chromium cast iron can refine the microstmcture, reduce coarse columnar crystals and make the carbide smaller and uniform. Through composite modification with RE, V, Ti and B, the hardness, wear resistance and impact toughness of high chromium cast iron are increased conspicuously. After heat treatment, the hardness of high chromium iron is increased significantly, but the toughness and wear resistance do not show great improvement.展开更多
This study developed a new technology for preparing high-chromium cast iron(HCCI)/low-carbon steel(LCS)wear-resistant composite plates by hot rolling at a 1050°C and a rolling speed of 0.2 m/s.The effects of diff...This study developed a new technology for preparing high-chromium cast iron(HCCI)/low-carbon steel(LCS)wear-resistant composite plates by hot rolling at a 1050°C and a rolling speed of 0.2 m/s.The effects of different rolling reductions(30%,45%,and 60%)on the microstructure(interface and HCCI layer)and mechanical properties(bonding strength,hardness,and wear resistance)of the composite plate were studied.SEM images showed that when the reduction was increased,no impurities and interlayers were found between the microscopic interfaces after hot rolling,and the bonding interface exhibited a wave-like shape.EDS analysis showed that the Cr element diffusion between two metals after hot rolling was promoted when the reduction was increased,thereby improving the bonding quality under the same rolling temperature and rolling speed.Experiments showed that due to the stress release effect of the LCS of the cladded layer,the macro-slab shape after hot rolling performed well,and the brittle HCCI layer underwent thermoplastic deformation without cracking.Moreover,the increase of rolling reduction improved the bonding quality.As the rolling reduction was increased,the volume fraction of Cr-carbides in the HCCI layer also increased,resulting in an increase of hardness and wear-resistance.展开更多
Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refi...Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refiner plates is of significance to the wood industry. It may affect refining quality, production efficiency, and power consumption. In this paper, the abrasion resistance of the refiner plate made of different materials, the stainless steels and high chromium cast irons, were tested and compared. The results showed that abrasion resistance of refiner plate made of high chromium cast irons was better than that of the stainless steel materials. Although the two kinds of materials have the same compositions, their abrasion resistances have ap-parent difference. The main reason is that the material microstructures have very important effects on their performance. The refiner plates made of developed high chromium cast irons don抰 demand the complex heat treatment. This can simplify the producing process, save the cost of production, decrease labor strength, and increase the production efficiency.展开更多
为了揭示高铬铸铁组织的微观本质并利用其分析结果预测合金的淬硬性,利用余瑞璜的固体与分子经验电子理论(EET)和Fe C Cr三元系平衡相图对Fe C Cr三元系高铬铸铁合金奥氏体的价电子结构进行了分析。结果表明,在工业应用的成分范围内C C...为了揭示高铬铸铁组织的微观本质并利用其分析结果预测合金的淬硬性,利用余瑞璜的固体与分子经验电子理论(EET)和Fe C Cr三元系平衡相图对Fe C Cr三元系高铬铸铁合金奥氏体的价电子结构进行了分析。结果表明,在工业应用的成分范围内C Cr键是合金奥氏体所有键中的最强键,形成C Cr偏聚单元。wCr/wC≥6时,含C Cr结构单元的权重会大大提高,促进了奥氏体的陈留,可以获得奥氏体基体组织。当wCr/wC=5.5～6.5时,Fe C Cr三元系高铬铸铁可获得最佳的淬硬性。展开更多
基金financially supported by the National Natural Science Foundation of China(52005217)the University Research Platform and Research Projects of Guangdong Education Department(2022ZDZX3003)+2 种基金Basic and Applied Basic Research Fund Project of Guangdong Province in China(2022A1515010091,2021A1515010523,and 2020A1515110020)Basic Scientific Research Projects of Central Universities(No.21620344)Jinan University Open Fund for Advanced Materials(JNIWRM2021004)。
文摘A chemical composite plating of Ni-B_(4)C was used to prepare the surface-modified zirconia toughened alumina(ZTA)ceramic particles.The ceramic preforms were prepared by the plated ZTA and sodium silicate solution binder,followed by casting infiltration to prepare the ZTA particles reinforced high chromium cast iron(HCCI)composites.The result reveals that a distinct interface layer forms at the ZTA/HCCI interface,which consists of phases of ZrB_(2),FeB,Fe_(2)B,and NaSiO_(4).The interfacial wettability between ZTA and HCCI is improved by the diffusion and reaction of Ni and B_(4)C.The wear test reveals that the Ni-B_(4)C plated ZTA particles can effectively improve the wear resistance of the ZTA/HCCI composite,and the wear rate of the composite is decreased to 11.6%of HCCI.
基金supported by the Harbin Scientific Research Fund for Young Scholars (No.2005AFQXJ030)the Harbin Science and Technology Project (No.2002AA5CG026)the Foundation of Heilong-jiang Educational Committee (No.11511051)
文摘The effects of RE, V, Ti and B on the microstructure and properties of high chromium cast iron containing 3% molybdenum under as-cast and heat treatment conditions were investigated with the method of comparing experiments. The results show that with the increase of RE content, the primary austenite of high chromium cast iron is obviously refined. The morphology of carbide is changed from netlike and lath to small multiangular isolated blocks or massive blocks, the isolated degree of carbide is improved obviously, and the size is significantly refined. The addition of V and B into high chromium cast iron can refine the microstmcture, reduce coarse columnar crystals and make the carbide smaller and uniform. Through composite modification with RE, V, Ti and B, the hardness, wear resistance and impact toughness of high chromium cast iron are increased conspicuously. After heat treatment, the hardness of high chromium iron is increased significantly, but the toughness and wear resistance do not show great improvement.
文摘This study developed a new technology for preparing high-chromium cast iron(HCCI)/low-carbon steel(LCS)wear-resistant composite plates by hot rolling at a 1050°C and a rolling speed of 0.2 m/s.The effects of different rolling reductions(30%,45%,and 60%)on the microstructure(interface and HCCI layer)and mechanical properties(bonding strength,hardness,and wear resistance)of the composite plate were studied.SEM images showed that when the reduction was increased,no impurities and interlayers were found between the microscopic interfaces after hot rolling,and the bonding interface exhibited a wave-like shape.EDS analysis showed that the Cr element diffusion between two metals after hot rolling was promoted when the reduction was increased,thereby improving the bonding quality under the same rolling temperature and rolling speed.Experiments showed that due to the stress release effect of the LCS of the cladded layer,the macro-slab shape after hot rolling performed well,and the brittle HCCI layer underwent thermoplastic deformation without cracking.Moreover,the increase of rolling reduction improved the bonding quality.As the rolling reduction was increased,the volume fraction of Cr-carbides in the HCCI layer also increased,resulting in an increase of hardness and wear-resistance.
文摘Defibrator is a very important machine in the wood industry for producing fiberboard. The refiner plates are the key parts of defibrator that directly act with the wood, and broken easily. The working life of the refiner plates is of significance to the wood industry. It may affect refining quality, production efficiency, and power consumption. In this paper, the abrasion resistance of the refiner plate made of different materials, the stainless steels and high chromium cast irons, were tested and compared. The results showed that abrasion resistance of refiner plate made of high chromium cast irons was better than that of the stainless steel materials. Although the two kinds of materials have the same compositions, their abrasion resistances have ap-parent difference. The main reason is that the material microstructures have very important effects on their performance. The refiner plates made of developed high chromium cast irons don抰 demand the complex heat treatment. This can simplify the producing process, save the cost of production, decrease labor strength, and increase the production efficiency.
文摘为了揭示高铬铸铁组织的微观本质并利用其分析结果预测合金的淬硬性,利用余瑞璜的固体与分子经验电子理论(EET)和Fe C Cr三元系平衡相图对Fe C Cr三元系高铬铸铁合金奥氏体的价电子结构进行了分析。结果表明,在工业应用的成分范围内C Cr键是合金奥氏体所有键中的最强键,形成C Cr偏聚单元。wCr/wC≥6时,含C Cr结构单元的权重会大大提高,促进了奥氏体的陈留,可以获得奥氏体基体组织。当wCr/wC=5.5～6.5时,Fe C Cr三元系高铬铸铁可获得最佳的淬硬性。