Sodium-ion batteries(SIBs) have been considered to be potential candidates for next-generation low-cost energy storage systems due to the low-cost and abundance of Na resources. However, it is a big challenge to find ...Sodium-ion batteries(SIBs) have been considered to be potential candidates for next-generation low-cost energy storage systems due to the low-cost and abundance of Na resources. However, it is a big challenge to find suitable anode materials with low-cost and good performance for the application of SIBs. Hard carbon could be a promising anode material due to high capacity and expectable low-cost if originating from biomass. Herein, we report a hard carbon material derived from abundant and abandoned biomass of sorghum stalk through a simple carbonization method. The effects of carbonization temperature on microstructure and electrochemical performance are investigated. The hard carbon carbonized at 1300 ℃ delivers the best rate capability(172 mAh g^(-1) at 200 mA g^(-1)) and good cycling performance(245 mAh g^(-1) after 50 cycles at 20 mA g^(-1),96% capacity retention). This contribution provides a green route for transforming sorghum stalk waste into "treasure"of promising low-cost anode material for SIBs.展开更多
Active carbons(ACs) were prepared through chemical activation of biochar from whole corn stalk(WCS)and corn stalk pith(CSP) at varying temperatures using potassium hydroxide as the activating agent. ACs were character...Active carbons(ACs) were prepared through chemical activation of biochar from whole corn stalk(WCS)and corn stalk pith(CSP) at varying temperatures using potassium hydroxide as the activating agent. ACs were characterized via pore structural analysis and scanning electron microscopy(SEM). These adsorbents were then assessed for their adsorption capacity for butanol vapor. It was found that WCS activated at900 °C for 1 h(WCS-900) had optimal butanol adsorption characteristics. The BET surface area and total pore volume of the WCS-900 were 2330 m2/g and 1.29 cm3/g, respectively. The dynamic adsorption capacity of butanol vapor was 410.0 mg/g, a 185.1% increase compared to charcoal-based commercial AC(143.8 mg/g).展开更多
Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and wer...Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and were identified to be Cu(0) and Cu(Ⅰ) in XRD patterns. Excellent catalytic activity and selectivity were achieved in the N-arylation of pyrazole under ligand and protection gas free conditions. About90.4% of product yield was achieved with only 0.5 mol% of copper catalyst(Cu-C-300), which was considerably more efficient than previous reports. XPS results suggested that the N-arylation of pyrazole activity was closely related to the surface Cu(Ⅰ) species.展开更多
基金financial support by the 2011 Program of Hubei ProvinceNational Key R&D Program of China (No.2015CB251100)+3 种基金National Science Foundation of China (No. 21673165, 21373155 and 21333007)Natural Science Foundation of Hubei Province, China (Grant No. 2015CFC774)Program for New Century Excellent Talents in University (NCET-12-0419)Hubei National Funds for Distinguished Young Scholars (2014CFA038)
文摘Sodium-ion batteries(SIBs) have been considered to be potential candidates for next-generation low-cost energy storage systems due to the low-cost and abundance of Na resources. However, it is a big challenge to find suitable anode materials with low-cost and good performance for the application of SIBs. Hard carbon could be a promising anode material due to high capacity and expectable low-cost if originating from biomass. Herein, we report a hard carbon material derived from abundant and abandoned biomass of sorghum stalk through a simple carbonization method. The effects of carbonization temperature on microstructure and electrochemical performance are investigated. The hard carbon carbonized at 1300 ℃ delivers the best rate capability(172 mAh g^(-1) at 200 mA g^(-1)) and good cycling performance(245 mAh g^(-1) after 50 cycles at 20 mA g^(-1),96% capacity retention). This contribution provides a green route for transforming sorghum stalk waste into "treasure"of promising low-cost anode material for SIBs.
基金supported by following projects:“Development of high value carbon based adsorbents from thermochemically produced biochar”USDA-NIFA2011-67009-20030 through the USDA-NIFA Agriculture and Food Research Initiative Sustainable Bioenergy Program which funded the Micropore analyzer and instruments for modifying AC+1 种基金NSF EPSCoR TrackⅡDakota Bio Con center(National Science Foundation/EPSCo R Award No.1330842)supported Mr.Cao Yuhe for his PhD study and GC–MS instrumentDOE Sun Grant Concept Project“Developing Gas Stripping-Adsorption/Desorption Separation Processes based on Porous Carbon Adsorbents for Biofuel Purification from Bioreactors”(North Central Sun Grant Award No.1300478)supported upgrading the Chemical Adsorption Analyzer
文摘Active carbons(ACs) were prepared through chemical activation of biochar from whole corn stalk(WCS)and corn stalk pith(CSP) at varying temperatures using potassium hydroxide as the activating agent. ACs were characterized via pore structural analysis and scanning electron microscopy(SEM). These adsorbents were then assessed for their adsorption capacity for butanol vapor. It was found that WCS activated at900 °C for 1 h(WCS-900) had optimal butanol adsorption characteristics. The BET surface area and total pore volume of the WCS-900 were 2330 m2/g and 1.29 cm3/g, respectively. The dynamic adsorption capacity of butanol vapor was 410.0 mg/g, a 185.1% increase compared to charcoal-based commercial AC(143.8 mg/g).
基金supported by the Natural Science Foundation of China(91645115 and 21473003)High-level talents funding project of Hebei(CL201601,E2016100015)science technology research and development guidance program project of Baoding City(No.16ZF027)
文摘Carbon-supported copper catalyst was prepared for the first time in one-step with copper nitrate and corn stalk through calcination under different temperatures. Uniformly dispersed nanoparticles were obtained and were identified to be Cu(0) and Cu(Ⅰ) in XRD patterns. Excellent catalytic activity and selectivity were achieved in the N-arylation of pyrazole under ligand and protection gas free conditions. About90.4% of product yield was achieved with only 0.5 mol% of copper catalyst(Cu-C-300), which was considerably more efficient than previous reports. XPS results suggested that the N-arylation of pyrazole activity was closely related to the surface Cu(Ⅰ) species.