A polystyrene-bonded stannic chloride catalyst was synthesized by the method of lithium polystyryl combined with stannic chloride. This catalyst is a polymeric organometallic compound containing 0.25 mmol Sn (Ⅳ)/g ca...A polystyrene-bonded stannic chloride catalyst was synthesized by the method of lithium polystyryl combined with stannic chloride. This catalyst is a polymeric organometallic compound containing 0.25 mmol Sn (Ⅳ)/g catalyst. The catalyst showed sufficient stability and catalytic activity in organic reaction such as esterification, acetalation and ketal formation, and it could be reused many times without losing its catalytic activity.展开更多
A composite ion exchange material, polyaniline stannic silicate was prepared under different experimental conditions. Ion exchange material synthesized at pH 1.0 shows an ion exchange capacity 1.6 meq/g for Na+ ions. ...A composite ion exchange material, polyaniline stannic silicate was prepared under different experimental conditions. Ion exchange material synthesized at pH 1.0 shows an ion exchange capacity 1.6 meq/g for Na+ ions. The exchanger has been characterized on the basis of X-ray and TGA. Ion exchange capacity, pH titration, elution and distribution studies were also carried out to determine the preliminary ion exchange properties of the material. The effect of temperature on the ion exchange capacity of the material at different temperatures has been studied. The sorption behavior of metal ions was also explored in different surfactant mediums. The practical utility of the material was explored by achieving quantitative separation of toxic metal ions in synthetic mixtures.展开更多
Highly transparent conductive stoichiometric nanocrystalline stannic oxide coatings were deposited onto Corning®EAGLE XG®slim glass substrates.Including each coating,it was deposited for various concentratio...Highly transparent conductive stoichiometric nanocrystalline stannic oxide coatings were deposited onto Corning®EAGLE XG®slim glass substrates.Including each coating,it was deposited for various concentrations in the aerosol solution with the substrate temperature maintained at 623.15 K by an ultrasonic spray pyrolysis(USP)technique.Nitrogen was em-ployed both as the solution carrier in addition to aerosol directing gas,maintaining its flow rates at 3500.0 and 500.0 mL/min,respectively.The coatings were polycrystalline,with preferential growth along the stannic oxide(112)plane,irrespective of the molarity content in the spray solution.The coating prepared at 0.2 M,a concentration in the aerosol solution,showed an average transmission of 60%in the visible light region spectrum with a maximum conductivity of 24.86 S/cm.The coatings deposited exhibited in the general photoluminescence spectrum emission colors of green,greenish white,and bluish white calculated on the intensities of the excitonic and oxygen vacancy defect level emissions.展开更多
Polyaniline stannic molybdate—an organic-inorganic composite material, was prepared via sol-gel mixing of organic polymer polyaniline into matrices of inorganic precipitate of stannicmolybdate. The composite material...Polyaniline stannic molybdate—an organic-inorganic composite material, was prepared via sol-gel mixing of organic polymer polyaniline into matrices of inorganic precipitate of stannicmolybdate. The composite material synthesized at pH 1.2 showed an ion exchange capacity 1.8 meq/g for Na+?ions. Ion exchange capacity, pH titration and distribution studies were carried out to determine the preliminary ion exchange properties of the material. The distribution studies showed the selectivity of Hg(II) ions by this material. The effect of temperature on the ion exchange capacity of the material at different temperatures had been studied. The sorption behavior of metal ions was also explored in different surfactant media.展开更多
文摘A polystyrene-bonded stannic chloride catalyst was synthesized by the method of lithium polystyryl combined with stannic chloride. This catalyst is a polymeric organometallic compound containing 0.25 mmol Sn (Ⅳ)/g catalyst. The catalyst showed sufficient stability and catalytic activity in organic reaction such as esterification, acetalation and ketal formation, and it could be reused many times without losing its catalytic activity.
文摘A composite ion exchange material, polyaniline stannic silicate was prepared under different experimental conditions. Ion exchange material synthesized at pH 1.0 shows an ion exchange capacity 1.6 meq/g for Na+ ions. The exchanger has been characterized on the basis of X-ray and TGA. Ion exchange capacity, pH titration, elution and distribution studies were also carried out to determine the preliminary ion exchange properties of the material. The effect of temperature on the ion exchange capacity of the material at different temperatures has been studied. The sorption behavior of metal ions was also explored in different surfactant mediums. The practical utility of the material was explored by achieving quantitative separation of toxic metal ions in synthetic mixtures.
基金the financial support from the Escuela Superior de Medicina,Instituto Politécnico Nacional,through Project No.20210385。
文摘Highly transparent conductive stoichiometric nanocrystalline stannic oxide coatings were deposited onto Corning®EAGLE XG®slim glass substrates.Including each coating,it was deposited for various concentrations in the aerosol solution with the substrate temperature maintained at 623.15 K by an ultrasonic spray pyrolysis(USP)technique.Nitrogen was em-ployed both as the solution carrier in addition to aerosol directing gas,maintaining its flow rates at 3500.0 and 500.0 mL/min,respectively.The coatings were polycrystalline,with preferential growth along the stannic oxide(112)plane,irrespective of the molarity content in the spray solution.The coating prepared at 0.2 M,a concentration in the aerosol solution,showed an average transmission of 60%in the visible light region spectrum with a maximum conductivity of 24.86 S/cm.The coatings deposited exhibited in the general photoluminescence spectrum emission colors of green,greenish white,and bluish white calculated on the intensities of the excitonic and oxygen vacancy defect level emissions.
文摘Polyaniline stannic molybdate—an organic-inorganic composite material, was prepared via sol-gel mixing of organic polymer polyaniline into matrices of inorganic precipitate of stannicmolybdate. The composite material synthesized at pH 1.2 showed an ion exchange capacity 1.8 meq/g for Na+?ions. Ion exchange capacity, pH titration and distribution studies were carried out to determine the preliminary ion exchange properties of the material. The distribution studies showed the selectivity of Hg(II) ions by this material. The effect of temperature on the ion exchange capacity of the material at different temperatures had been studied. The sorption behavior of metal ions was also explored in different surfactant media.