Magnesite-bonded wood wool panel(MWWP)is an inorganic-bonded panel product in which wood excelsior is bonded with magnesite.Lowering the hygroscopicity is one of the key measures to improve the quality of the panel.In...Magnesite-bonded wood wool panel(MWWP)is an inorganic-bonded panel product in which wood excelsior is bonded with magnesite.Lowering the hygroscopicity is one of the key measures to improve the quality of the panel.In this study,moisture absorption mechanism of MWWP and measures generally applied to lower its hygroscopicity were reviewed.Three methods were then experimented to improve the dimensional stability of the panel,including adjusting the molar ratio of raw materials,adding additives and optimizing the conditioning process.The results showed that satisfying dimensional stability could be achieved when the molar ratio of MgO to MgCl_(2) was 5:1,the No.2 composite additive(aluminum powder+NH_(4)H_(2)PO_(4)+ferric alum)was adopted and a constant temperature and humidity treatment was applied in the first stage of conditioning.展开更多
基金This study is funded by National Natural Science Foundation(31070502)Public Farewell Project of National Forestry Bureau(201004006-6)support of the Priority Academic Program Development of Jiangsu Higher Education Institutions and Co-innovation Center of Efficient Processing and Utilization of Forest Resources,Nanjing Forestry University,Nanjing 210037,China.
文摘Magnesite-bonded wood wool panel(MWWP)is an inorganic-bonded panel product in which wood excelsior is bonded with magnesite.Lowering the hygroscopicity is one of the key measures to improve the quality of the panel.In this study,moisture absorption mechanism of MWWP and measures generally applied to lower its hygroscopicity were reviewed.Three methods were then experimented to improve the dimensional stability of the panel,including adjusting the molar ratio of raw materials,adding additives and optimizing the conditioning process.The results showed that satisfying dimensional stability could be achieved when the molar ratio of MgO to MgCl_(2) was 5:1,the No.2 composite additive(aluminum powder+NH_(4)H_(2)PO_(4)+ferric alum)was adopted and a constant temperature and humidity treatment was applied in the first stage of conditioning.