The effects of the content of rare earth elements on the microstructure and properties of hot-dip Zn-5 Al alloy steel wire for bridge cables were investigated.The microstructure of the hot-dip coating was analyzed usi...The effects of the content of rare earth elements on the microstructure and properties of hot-dip Zn-5 Al alloy steel wire for bridge cables were investigated.The microstructure of the hot-dip coating was analyzed using an optical microscope and a scanning electron microscope equipped with an energy-dispersive spectrometer.The bonding force between the hot-dip coating and steel wire was determined by the winding test.The corrosion resistance of the steel wire hot-dip coating was tested by the electrochemical workstation.The hot-dip Zn-5A1 alloy coating has a corrosion-resistant structure composed of a zinc-rich phase and an aluminum-rich phase.Due to the enhanced bonding force,the micro structure of the hot-dip coating of the Zn-5A1 alloy with rare earth elements is more compact and uniform than that without rare earth elements.The addition of rare earth elements improves the corrosion resistance of Zn-5A1 alloy coated steel wire.Due to the rare earth segregation,which prevents the corrosion of the grain boundary and enhances the anti-intergranular corrosion performance,steel wire exhibits the optimum corrosion resistance when the content of rare earth elements is 0.08 wt.%.展开更多
基金The authors would like to acknowledge the support from Key-Area Research and Development Program of Guangdong Province(2019B111106002)the Natural Science Foundation of the Jiangsu Higher Education Institutions of China(21KJB460023).
文摘The effects of the content of rare earth elements on the microstructure and properties of hot-dip Zn-5 Al alloy steel wire for bridge cables were investigated.The microstructure of the hot-dip coating was analyzed using an optical microscope and a scanning electron microscope equipped with an energy-dispersive spectrometer.The bonding force between the hot-dip coating and steel wire was determined by the winding test.The corrosion resistance of the steel wire hot-dip coating was tested by the electrochemical workstation.The hot-dip Zn-5A1 alloy coating has a corrosion-resistant structure composed of a zinc-rich phase and an aluminum-rich phase.Due to the enhanced bonding force,the micro structure of the hot-dip coating of the Zn-5A1 alloy with rare earth elements is more compact and uniform than that without rare earth elements.The addition of rare earth elements improves the corrosion resistance of Zn-5A1 alloy coated steel wire.Due to the rare earth segregation,which prevents the corrosion of the grain boundary and enhances the anti-intergranular corrosion performance,steel wire exhibits the optimum corrosion resistance when the content of rare earth elements is 0.08 wt.%.