An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cemen...An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cement. 15% SBR latex polymer was used by weight of cement. Cubes of size 150 × 150 × 150 mm for compressive strength, prism specimens of size 150 mm × 150 mm × 700 mm for flexure strength and, specimen of size 150 × 150 × 150 mm with 16 mm diameter tor steel bar of length 650 mm embedded in concrete cube at the center for bond test were prepared. Various specimens were tested after 28 days of curing. Area under curve (toughness) is measured and mentioned in this work.展开更多
Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to des...Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to design and prepare a high-performance assembled asphalt concrete block for fast repair of the potholes.A series of composite modified asphalt binders with 10%crumb rubber(CR)and different dosages(0%,1%,3%,5%)of polyurethane(PU)are examined to determine the optimized binder.Subsequently,the corresponding asphalt mixtures are prepared for further comparison and assessment of engineering properties,such as moistureinduced damage,high-temperature deformation,and low-temperature cracking characteristics.The test results show that PU can significantly improve the high-temperature performance and hardness of(crumb rubber modified asphalt)CRMA binder;3%PU contributes allowing the resistance of CRMA mixture to moisture-induced damage at higher levels,particularly under water whole immersion;as 3%PU is added,the high-temperature rutting deformation resistance of the CRMA mixture increases significantly,and the low-temperature anti-cracking properties are also improved slightly.Therefore,the innovatively designed high-quality assembled fast-repairing asphalt concrete block is recommended as an appropriate option for highway maintenance.展开更多
文摘An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cement. 15% SBR latex polymer was used by weight of cement. Cubes of size 150 × 150 × 150 mm for compressive strength, prism specimens of size 150 mm × 150 mm × 700 mm for flexure strength and, specimen of size 150 × 150 × 150 mm with 16 mm diameter tor steel bar of length 650 mm embedded in concrete cube at the center for bond test were prepared. Various specimens were tested after 28 days of curing. Area under curve (toughness) is measured and mentioned in this work.
基金the Scientific Technology R&D Project of CCCC Asset Management Co.,Ltd.(RP2022015294&RP2022015296).
文摘Conventional repairing methods for asphalt pavement have some inconveniences,such as insufficient strength,and are typically time-consuming.To address these issues,this study proposes a new technological method to design and prepare a high-performance assembled asphalt concrete block for fast repair of the potholes.A series of composite modified asphalt binders with 10%crumb rubber(CR)and different dosages(0%,1%,3%,5%)of polyurethane(PU)are examined to determine the optimized binder.Subsequently,the corresponding asphalt mixtures are prepared for further comparison and assessment of engineering properties,such as moistureinduced damage,high-temperature deformation,and low-temperature cracking characteristics.The test results show that PU can significantly improve the high-temperature performance and hardness of(crumb rubber modified asphalt)CRMA binder;3%PU contributes allowing the resistance of CRMA mixture to moisture-induced damage at higher levels,particularly under water whole immersion;as 3%PU is added,the high-temperature rutting deformation resistance of the CRMA mixture increases significantly,and the low-temperature anti-cracking properties are also improved slightly.Therefore,the innovatively designed high-quality assembled fast-repairing asphalt concrete block is recommended as an appropriate option for highway maintenance.