An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cemen...An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cement. 15% SBR latex polymer was used by weight of cement. Cubes of size 150 × 150 × 150 mm for compressive strength, prism specimens of size 150 mm × 150 mm × 700 mm for flexure strength and, specimen of size 150 × 150 × 150 mm with 16 mm diameter tor steel bar of length 650 mm embedded in concrete cube at the center for bond test were prepared. Various specimens were tested after 28 days of curing. Area under curve (toughness) is measured and mentioned in this work.展开更多
Acid rain can deteriorate the performance of reinforced concrete structure.Combined with the characteristics of acid rain in China,the properties of steel fiber reinforced concrete subjected to acid rain were studied....Acid rain can deteriorate the performance of reinforced concrete structure.Combined with the characteristics of acid rain in China,the properties of steel fiber reinforced concrete subjected to acid rain were studied.The effects of steel fiber content and pH value of acid rain on the mass loss,erosion depth,neutralization depth,and splitting tensile strength of tested concrete were investigated.The mercury intrusion pore(MIP) test was used to analyze the influence of steel fiber on the acid rain resistance of concrete matrix.The results show that the corrosion of steel fiber reinforced concrete subjected to acid rain results from the combined effect of H^+ and SO4^2- in the acid rain,and steel fiber can improve the acid rain resistance of the tested concrete by improving the pore structure and enhancing the tie effect of the concrete matrix.The experiment further indicates that the optimum content of steel fiber is 1.5%compared to the various mixing proportion in this tests.The tested concrete mass loss and splitting tensile strength decrease followed by increasing as a function of corrosion time when the pH value of the simulation solution is 3 or 4,while they decrease continuously in the simulation solution at pH 2.Thanks to the tie effect of steel fiber,the spalling of concrete matrix is significantly improved,and the erosion depth and neutralization depth are less than those of conventional concrete.展开更多
Steel fiber reinforced concrete(SFRC)has drawn extensive attention in recent years for its superior mechanical response to dynamic and impact loadings.Based on the existing test results,the highstrength steel fibers e...Steel fiber reinforced concrete(SFRC)has drawn extensive attention in recent years for its superior mechanical response to dynamic and impact loadings.Based on the existing test results,the highstrength steel fibers embedded in a concrete matrix usually play a strong bridging effect to enhance the bonding force between fiber and the matrix,and directly contribute to the improvement of the post-cracking behavior and residual strength of SFRC.To gain a better understanding of the action behavior of steel fibers in matrix and further capture the failure mechanism of SFRC under dynamic loads,the mesoscopic modeling approach that assumes SFRC to be composed of different mesoscale phases(i.e.,steel fibers,coarse aggregates,mortar matrix,and interfacial transition zone(ITZ))has been widely employed to simulate the dynamic responses of SFRC material and structural members.This paper presents a comprehensive review of the state-of-the-art mesoscopic models and simulations for SFRC under dynamic loading.Generation approaches for the SFRC mesoscale model in the simulation works,including steel fiber,coarse aggregate,and the ITZ between them,are reviewed and compared systematically.The material models for different phases and the interaction relationship between fiber and concrete matrix are summarized comprehensively.Additionally,some example applications for SFRC under dynamic loads(i.e.,compression,tension,and contact blast)simulated using the general mesoscale models are given.Finally,some critical analysis on the current shortcomings of the mesoscale modeling of SFRC is highlighted,which is of great significance for the future investigation and development of SFRC.展开更多
A whole of 110 specimens divided into 22 groups were tested with varying the volume fraction of steel fibers and the matrix strength of these specimens. The stress-strain behaviors of four types of steel fiber reinfo...A whole of 110 specimens divided into 22 groups were tested with varying the volume fraction of steel fibers and the matrix strength of these specimens. The stress-strain behaviors of four types of steel fiber reinforced concrete (SFRC) under uniaxial tension were studied experimentally. When the matrix strength and the fiber content increase, the tensile stress and tensile strain vary differently according to the fiber type. The mechanisms of reinforcing effect for different types of fiber were analyzed and the stress-strain curves of the specimens were plotted. Some experimental factors for stress or strain of SFRC were given. A tensile toughness modulus Re0.5 was introduced to evaluate the toughness characters of SFRC under uniaxial tension. Moreover, the formula of the tensile stress-strain curve of SFRC was regressed. The theoretical curve and the experimental ones fit well, which can be used for references in construction.展开更多
The flexural behaviors of continuous fully and partially prestressed steel fiber reinforced high strength concrete beams are studied by experiment and nonlinear finite element analysis. Three levels of partial prestre...The flexural behaviors of continuous fully and partially prestressed steel fiber reinforced high strength concrete beams are studied by experiment and nonlinear finite element analysis. Three levels of partial prestress ratio (PPR) are considered, and three pairs of two-span continuous beams with box sections varying in size are designed. The major parameters involved in the study include the PPR and the fiber location. It is concluded that the prestressed high strength concrete beam exhibits satisfactory ductility; the influences of steel fiber on the crack behaviors for partially prestressed beams are not as obvious as those for fully prestressed ones; steel fibers can improve the structural stiffness after cracking for fully prestressed high strength concrete beams; the moment redistribution from mid-span to intermediate support in the first stage should be mainly considered in practical design.展开更多
By the nonlinear finite element analysis (FEA) method, the mechanical properties of the steel fiber reinforced concrete (SFRC) deep beams were discussed in terms of the crack load and ultimate bearing capacity. In...By the nonlinear finite element analysis (FEA) method, the mechanical properties of the steel fiber reinforced concrete (SFRC) deep beams were discussed in terms of the crack load and ultimate bearing capacity. In the simulation process, the ANSYS parametric design language (APDL) was used to set up the finite element model; the model of bond stress-slip relationship between steel bar and concrete was established. The nonlinear FEA results and test results demonstrated that the steel fiber can not only significantly improve the cracking load and ultimate bearing capacity of the concrete but also repress the development of the cracks. Meanwhile, good agreement was found between the experimental data and FEA results, if the unit type, the parameter model and the failure criterion are selected reasonably.展开更多
Three kinds of polymers, polymethyl acrylate emulsion (POLYVINYLformal solution (PV- FO), styrene acrylate copolymer emulsion (SA)are chosen To study the effect of polymer in steel fiber rein forcedce- Ment composites...Three kinds of polymers, polymethyl acrylate emulsion (POLYVINYLformal solution (PV- FO), styrene acrylate copolymer emulsion (SA)are chosen To study the effect of polymer in steel fiber rein forcedce- Ment composites (SFRCC). The experimental results show That thebonding properties in SFRCC are remarkably im- Proved after theaddition of three kinds of polymer.展开更多
Through the experiments of 7 T-section composite beams, steel fiber reinforced self-stressing concrete (SFRSC) as the composite beam in the composite layer was studied under the hogging bending. The tests simulated ...Through the experiments of 7 T-section composite beams, steel fiber reinforced self-stressing concrete (SFRSC) as the composite beam in the composite layer was studied under the hogging bending. The tests simulated composite layer tensile strain under the hogging bending of inverted loading composite beams, giving the relationship under the different fatigue stress ratios between fatigue cycles and steel bar’s stress range, crack width, stiffness loss and damage, etc., in composite layer. This article established fatigue life equation, and analyzed SFRSC reinforced mechanism to crack width and stiffness loss. The results show that SFRSC as the composite beam concrete has excellent properties of crack resistance and tensile, can reinforce the fatigue crack width and stiffness loss of composite beams, and improve the durability and in normal use of composite beams in the hogging bending zone.展开更多
This study empirically investigated the influence of freeze-thaw cycling on the dynamic splitting tensile properties of steel fiber reinforced concrete(SFRC).Brazilian disc splitting tests were conducted using four lo...This study empirically investigated the influence of freeze-thaw cycling on the dynamic splitting tensile properties of steel fiber reinforced concrete(SFRC).Brazilian disc splitting tests were conducted using four loading rates(0.002,0.02,0.2,and 2 mm/s)on specimens with four steel fiber contents(0%,0.6%,1.2%,and 1.8%)subjected to 0 and 50 freeze-thaw cycles.The dynamic splitting tensile damage characteristics were evaluated using acoustic emission(AE)parameter analysis and Fourier transform spectral analysis.The results quantified using the freeze-thaw damage factor defined in this paper indicate that the degree of damage to SFRC caused by freeze-thaw cycling was aggravated with increasing loading rate but mitigated by increasing fiber content.The percentage of low-frequency AE signals produced by the SFRC specimens during loading decreased with increasing loading rate,whereas that of high-frequency AE signals increased.Freeze-thaw action had little effect on the crack types observed during the early and middle stages of the loading process;however,the primary crack type observed during the later stage of loading changed from shear to tensile after the SFRC specimens were subjected to freeze-thaw cycling.Notably,the results of this study indicate that the freeze-thaw damage to SFRC reduces AE signal activity at low frequencies.展开更多
To explore a new structure form of fiber reinforced concrete, namely, the layered steel fiber and layered hybrid fiber reinforced concrete (LSFRC and LHFRC), the mechanical properties of LSFRC and LHFRC, such as com...To explore a new structure form of fiber reinforced concrete, namely, the layered steel fiber and layered hybrid fiber reinforced concrete (LSFRC and LHFRC), the mechanical properties of LSFRC and LHFRC, such as compressive strength, tensile strength, flexural strength, fatigue and durability were focused on. The experimental results show that LSFRC and LHFRC can improve the flexural strength of concrete by 20%-50%. In the aspect of improving the flexural strength of concrete, adulterant rate has more obvious effect than length/diameter ratio. Double logarithmic fatigue equation considered liveability was founded. The impermeability of LHFRC is superior to LSFRC and plain concrete (C). However, the porosity of LHFRC is lower than LSFRC and C. The shrinkage of LHFRC at every age is obviously lower than C. The antifreeze durability of LHFRC is also better than C.展开更多
The general goal of this research is to investigate whether steel fiber has a significant “positive” or “negative” influence on concrete compressive strength, as well as the optimal steel fiber ratio that delivers...The general goal of this research is to investigate whether steel fiber has a significant “positive” or “negative” influence on concrete compressive strength, as well as the optimal steel fiber ratio that delivers best result. Manually, cement, fine aggregates, coarse aggregates, steel fibers, and water were mixed together properly. A slump test was carried on the mixed concrete. After determining the workability, the mixed concrete was poured into cubes dimension 150 mm × 150 mm × 150 mm and left for 24 hours. After 24 hours, the samples were removed from the mold and placed in a water tank to cure for 7 to 28 days. The cube was tested for compressive and flexural strength in a universal testing machine after the samples had cured for the required 7 - 28 days. This study focuses on how to obtain high strength concrete using with steel fiber in the Conventional mix ratio to enhance concrete strength. Concrete reinforcement using steel fibers alters the characteristics of the concrete, allowing it to withstand fracture and hence improve its mechanical qualities. This study reports on an experimental study that reveals the effect of steel fiber on concrete compressive strength and the optimal steel fiber ratio that produces the best results. Steel fiber reinforcing improved the compressive strength of concrete. The average compressive strength of normal M25 concrete with 0% steel fibers and curing ages of 7 and 28 days was determined to be 22.97 N/mm<sup>2</sup> and 25.78 N/mm<sup>2</sup>, respectively. The steel fibers are then added in various concentrations, such as 1%, 2%, and 3%, with aspect ratios of 70. The compressive strength of concrete with 1%, 2%, and 3% steel fiber with an aspect ratio of 70 was examined at 7 days and found to be 23.96, 24.80, and 26.14 N/mm<sup>2</sup> correspondingly.展开更多
Recent developments on high-performance double-hooked-end steel fibers have enhanced the wide applications of steel fiber reinforced concrete(SFRC).This study presents the compressive properties and the cyclic flexura...Recent developments on high-performance double-hooked-end steel fibers have enhanced the wide applications of steel fiber reinforced concrete(SFRC).This study presents the compressive properties and the cyclic flexural performance of the SFRC that were experimentally examined.Three different double-hooked-end steel fibers at 0.25%,0.5%,0.75%,and 1%volume fractions were considered.All fiber types had similar length to diameter ratios,while the first two fiber types had similar anchorage mechanisms(4D)and tensile strength and the third type had different anchorage mechanism(5D)and a higher tensile strength.The increased volumetric ratio of the fibers increased the post-peak compressive strain(ductility),the tensile strength,and the cyclic flexural strength and cumulative energy dissipation characteristics of the SFRC.Among the 4D fibers,the mixtures with the larger steel fibers showed higher flexural strength and more energy dissipation compared to the SFRCs with smaller size fibers.For 1%steel fiber dosage,4D and 5D specimens showed similar cyclic flexural responses.Finally,a 3D finite element model that can predict the monotonic and cyclic flexural responses of the double-hooked-end SFRC was developed.The calibration process considered the results obtained from the inverse analysis to determine the tensile behavior of the SFRC.展开更多
The stress transfer mechanism of steel fibre reinforced concrete is studied. The solutions for the stress and displacement were regarded as the superposition of ' the elementary solutions' and ' the improv...The stress transfer mechanism of steel fibre reinforced concrete is studied. The solutions for the stress and displacement were regarded as the superposition of ' the elementary solutions' and ' the improved solutions'. The elementary solutions were found by using two-dimensional elastic theory and the improved solutions were found by using the Love displacement function method. The calculated results indicate that the solutions possess good convergence. By comparing the three-dimensional solutions with the shear-lag solutions, evident difference may be found.展开更多
Freeze-thaw durabilities of three types of concretesnormal portland cement concrete (OPC), high strength concrete (HSC) and steel fiber reinforced high strength concrete (SFRHSC) were systemically investigated u...Freeze-thaw durabilities of three types of concretesnormal portland cement concrete (OPC), high strength concrete (HSC) and steel fiber reinforced high strength concrete (SFRHSC) were systemically investigated under the attacks of chemical solution, and combination of external flexural stress and chemical solution. Four kinds of bitterns from salt lakes in Sinkiang, Qinghai, Inner Mongolia and Tibet provinces of China were used as chemical attack solutions. The relative dynamic modulus (RDM) was used as an index for evaluating the damage degree during the course of chemical attack and stress corrosion. The experimental results show that the freeze-thaw durability of concrete is visibly reduced in the present of the flexural stress, i e, stress accelerates the damage process. In order to quantify the stress accelerated effect, a stress accelerating coefficient was proposed. The stress accelerating coefficient is closely related with the types of bitterns and the numbers of freeze-thaw cycles is. The more numbers of freeze-thaw cycles is, the greater the stress accelerating coefficient for various concretes will be. In addition, there also exists a critical ratio of external stress to the maximum flexural stress. If the stress ratio exceeds the critical one, the freeze-thaw durability of various concretes will be greatly decreased compared to the responding concretes without applied stress. The critical stress ratio of OPC, HSC and SFRHSC is 0.30, 0.40 and 0.40, respectively, indicating that HSC and SFRHSC have advantages over OPC and are suitable to use in the bittern erosion regions.展开更多
This paper presents a precise solution to predict the behavior of steel fiber reinforced concrete(SFRC) under the four point bending test(FPBT).All the force components at the beam section(before and after cracking) a...This paper presents a precise solution to predict the behavior of steel fiber reinforced concrete(SFRC) under the four point bending test(FPBT).All the force components at the beam section(before and after cracking) are formulated by applying these assumptions:a realistic stress-strain model is used for concrete behavior in compression,a linear response is considered for the uncracked tension region in a concrete constitutive model,and an exponential relationship is proposed as a stress-crack opening in the crack region which requires two parameters.Then the moment capacity of the critical cracked section is calculated by using these forces and satisfying equilibrium law at the section.Parametric studies are done on the behavior of SFRC to assess the sensitivity of the solution.Finally,this solution is validated with some existing experimental data.The result shows the proposed solution is able to estimate the behavior of SFRC under FPBT.展开更多
The article aimed to study the durability of steel fiber reinforced concrete under the coupled sewage-loading according to compressive strength,flexural strength,compressive strength corrosion coefficient,flexural str...The article aimed to study the durability of steel fiber reinforced concrete under the coupled sewage-loading according to compressive strength,flexural strength,compressive strength corrosion coefficient,flexural strength corrosion coefficient,compressive strength balance coefficient,flexural strength balance coefficient.Through the homemade load frame applied to design specimens,the pre-loading level are equivalent the damage intensity of 0%,10%,30% and 50% four different ways.The experimental results show that the performance of concrete down gradually and sustaining load aggravated the degree of domestic sewage attacking concrete after six month;under different stress states,the more loading levels,the more serious domestic sewage attacked the steel fiber reinforced concrete.It is proved that the concrete damage can be inhibited by adding the steel fiber,when steel fiber volume fraction is 1.0%,the corrosion resistance of concrete is best.展开更多
The road surface of cement concrete in highway is easily cracked and even destroyed due to inhomogeneous subsiding of the road foundation. In this work, a super-thin-coating material is prepared in order to repair the...The road surface of cement concrete in highway is easily cracked and even destroyed due to inhomogeneous subsiding of the road foundation. In this work, a super-thin-coating material is prepared in order to repair the destroyed thin road surface, in which polymers and steel-fiber are added into ordinary concrete to form a steel fiber reinforced polymer-cement-based composite, the composite was successfully used to repair road surface. Microstructure and mechanical properties of the composites are measured and analyzed.展开更多
The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete (SFHPC) after exposure to high temperatures. Three types of steel fibers were ...The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete (SFHPC) after exposure to high temperatures. Three types of steel fibers were used and three-point bending tests on notched beams of SFHPC were carried out. The results showed that the flexural toughness and fracture energy of SFHPC increased evidently with the fiber content. The hooked steel fibers with higher strength possess higher flexural toughness and fracture energy than the marked steel fibers with lower strength. After exposure to high temperatures of 300, 600 and 900 ℃ in an electrical furnace, the compressive strength, flexural toughness and fracture energy of SFHPC decreased less than that of HPC without fibers, Both steel fiber content and type had strong influences on the flexural toughness and fracture energy. In addition, the failure patterns of SFHPC beams changed from pull-out of steel fibers at lower temperatures to tensile failure of steel fibers at 900 ℃.展开更多
文摘An experimental investigation is carried out to study the toughness of polymer modified steel fiber reinforced concrete. Volume fraction of steel fibers is varied from 0% to 7% at the interval of 1% by weight of cement. 15% SBR latex polymer was used by weight of cement. Cubes of size 150 × 150 × 150 mm for compressive strength, prism specimens of size 150 mm × 150 mm × 700 mm for flexure strength and, specimen of size 150 × 150 × 150 mm with 16 mm diameter tor steel bar of length 650 mm embedded in concrete cube at the center for bond test were prepared. Various specimens were tested after 28 days of curing. Area under curve (toughness) is measured and mentioned in this work.
基金Funded by National Natural Science Foundation of China(No.51380445)Natural Science Foundation of Shan’xi Province,China(No.2013JQ7033)Startup Foundation for Talents of Xi’an University of Architecture and Technology(No.DB 09077)
文摘Acid rain can deteriorate the performance of reinforced concrete structure.Combined with the characteristics of acid rain in China,the properties of steel fiber reinforced concrete subjected to acid rain were studied.The effects of steel fiber content and pH value of acid rain on the mass loss,erosion depth,neutralization depth,and splitting tensile strength of tested concrete were investigated.The mercury intrusion pore(MIP) test was used to analyze the influence of steel fiber on the acid rain resistance of concrete matrix.The results show that the corrosion of steel fiber reinforced concrete subjected to acid rain results from the combined effect of H^+ and SO4^2- in the acid rain,and steel fiber can improve the acid rain resistance of the tested concrete by improving the pore structure and enhancing the tie effect of the concrete matrix.The experiment further indicates that the optimum content of steel fiber is 1.5%compared to the various mixing proportion in this tests.The tested concrete mass loss and splitting tensile strength decrease followed by increasing as a function of corrosion time when the pH value of the simulation solution is 3 or 4,while they decrease continuously in the simulation solution at pH 2.Thanks to the tie effect of steel fiber,the spalling of concrete matrix is significantly improved,and the erosion depth and neutralization depth are less than those of conventional concrete.
基金the financial support from the National Natural Science Foundation of China(52178190 and 52078250)the Science and Technology on Near-Surface Detection Laboratory(6142414200505)+1 种基金the Interdisciplinary Innovation Fundation for Graduates,Nanjing University of Aeronautics and Astronautics(KXKCXJJ202005)The support provided by the China Scholarship Council(202006830096)during a visit of Zhangyu Wu to University College London。
文摘Steel fiber reinforced concrete(SFRC)has drawn extensive attention in recent years for its superior mechanical response to dynamic and impact loadings.Based on the existing test results,the highstrength steel fibers embedded in a concrete matrix usually play a strong bridging effect to enhance the bonding force between fiber and the matrix,and directly contribute to the improvement of the post-cracking behavior and residual strength of SFRC.To gain a better understanding of the action behavior of steel fibers in matrix and further capture the failure mechanism of SFRC under dynamic loads,the mesoscopic modeling approach that assumes SFRC to be composed of different mesoscale phases(i.e.,steel fibers,coarse aggregates,mortar matrix,and interfacial transition zone(ITZ))has been widely employed to simulate the dynamic responses of SFRC material and structural members.This paper presents a comprehensive review of the state-of-the-art mesoscopic models and simulations for SFRC under dynamic loading.Generation approaches for the SFRC mesoscale model in the simulation works,including steel fiber,coarse aggregate,and the ITZ between them,are reviewed and compared systematically.The material models for different phases and the interaction relationship between fiber and concrete matrix are summarized comprehensively.Additionally,some example applications for SFRC under dynamic loads(i.e.,compression,tension,and contact blast)simulated using the general mesoscale models are given.Finally,some critical analysis on the current shortcomings of the mesoscale modeling of SFRC is highlighted,which is of great significance for the future investigation and development of SFRC.
基金Funded by Regulation RevisingItemof China Associationfor En-gineering Construction Standardization (CECS 15 :2000)
文摘A whole of 110 specimens divided into 22 groups were tested with varying the volume fraction of steel fibers and the matrix strength of these specimens. The stress-strain behaviors of four types of steel fiber reinforced concrete (SFRC) under uniaxial tension were studied experimentally. When the matrix strength and the fiber content increase, the tensile stress and tensile strain vary differently according to the fiber type. The mechanisms of reinforcing effect for different types of fiber were analyzed and the stress-strain curves of the specimens were plotted. Some experimental factors for stress or strain of SFRC were given. A tensile toughness modulus Re0.5 was introduced to evaluate the toughness characters of SFRC under uniaxial tension. Moreover, the formula of the tensile stress-strain curve of SFRC was regressed. The theoretical curve and the experimental ones fit well, which can be used for references in construction.
文摘The flexural behaviors of continuous fully and partially prestressed steel fiber reinforced high strength concrete beams are studied by experiment and nonlinear finite element analysis. Three levels of partial prestress ratio (PPR) are considered, and three pairs of two-span continuous beams with box sections varying in size are designed. The major parameters involved in the study include the PPR and the fiber location. It is concluded that the prestressed high strength concrete beam exhibits satisfactory ductility; the influences of steel fiber on the crack behaviors for partially prestressed beams are not as obvious as those for fully prestressed ones; steel fibers can improve the structural stiffness after cracking for fully prestressed high strength concrete beams; the moment redistribution from mid-span to intermediate support in the first stage should be mainly considered in practical design.
基金the Science Foundation for Young Scientists of Hubei Province Educational Committee of China (B200514003)
文摘By the nonlinear finite element analysis (FEA) method, the mechanical properties of the steel fiber reinforced concrete (SFRC) deep beams were discussed in terms of the crack load and ultimate bearing capacity. In the simulation process, the ANSYS parametric design language (APDL) was used to set up the finite element model; the model of bond stress-slip relationship between steel bar and concrete was established. The nonlinear FEA results and test results demonstrated that the steel fiber can not only significantly improve the cracking load and ultimate bearing capacity of the concrete but also repress the development of the cracks. Meanwhile, good agreement was found between the experimental data and FEA results, if the unit type, the parameter model and the failure criterion are selected reasonably.
文摘Three kinds of polymers, polymethyl acrylate emulsion (POLYVINYLformal solution (PV- FO), styrene acrylate copolymer emulsion (SA)are chosen To study the effect of polymer in steel fiber rein forcedce- Ment composites (SFRCC). The experimental results show That thebonding properties in SFRCC are remarkably im- Proved after theaddition of three kinds of polymer.
基金Project supported by the Science and Technology of Department of Communications of Liaoning Province (Grant No.200514)the Science and Technology of Department of Education of Liaoning Province (Grant No.L2010378)
文摘Through the experiments of 7 T-section composite beams, steel fiber reinforced self-stressing concrete (SFRSC) as the composite beam in the composite layer was studied under the hogging bending. The tests simulated composite layer tensile strain under the hogging bending of inverted loading composite beams, giving the relationship under the different fatigue stress ratios between fatigue cycles and steel bar’s stress range, crack width, stiffness loss and damage, etc., in composite layer. This article established fatigue life equation, and analyzed SFRSC reinforced mechanism to crack width and stiffness loss. The results show that SFRSC as the composite beam concrete has excellent properties of crack resistance and tensile, can reinforce the fatigue crack width and stiffness loss of composite beams, and improve the durability and in normal use of composite beams in the hogging bending zone.
文摘This study empirically investigated the influence of freeze-thaw cycling on the dynamic splitting tensile properties of steel fiber reinforced concrete(SFRC).Brazilian disc splitting tests were conducted using four loading rates(0.002,0.02,0.2,and 2 mm/s)on specimens with four steel fiber contents(0%,0.6%,1.2%,and 1.8%)subjected to 0 and 50 freeze-thaw cycles.The dynamic splitting tensile damage characteristics were evaluated using acoustic emission(AE)parameter analysis and Fourier transform spectral analysis.The results quantified using the freeze-thaw damage factor defined in this paper indicate that the degree of damage to SFRC caused by freeze-thaw cycling was aggravated with increasing loading rate but mitigated by increasing fiber content.The percentage of low-frequency AE signals produced by the SFRC specimens during loading decreased with increasing loading rate,whereas that of high-frequency AE signals increased.Freeze-thaw action had little effect on the crack types observed during the early and middle stages of the loading process;however,the primary crack type observed during the later stage of loading changed from shear to tensile after the SFRC specimens were subjected to freeze-thaw cycling.Notably,the results of this study indicate that the freeze-thaw damage to SFRC reduces AE signal activity at low frequencies.
基金the Technical Specification for Fiber Reinforced ConcreteStructure (No. CECS:2004 2000jb15)
文摘To explore a new structure form of fiber reinforced concrete, namely, the layered steel fiber and layered hybrid fiber reinforced concrete (LSFRC and LHFRC), the mechanical properties of LSFRC and LHFRC, such as compressive strength, tensile strength, flexural strength, fatigue and durability were focused on. The experimental results show that LSFRC and LHFRC can improve the flexural strength of concrete by 20%-50%. In the aspect of improving the flexural strength of concrete, adulterant rate has more obvious effect than length/diameter ratio. Double logarithmic fatigue equation considered liveability was founded. The impermeability of LHFRC is superior to LSFRC and plain concrete (C). However, the porosity of LHFRC is lower than LSFRC and C. The shrinkage of LHFRC at every age is obviously lower than C. The antifreeze durability of LHFRC is also better than C.
文摘The general goal of this research is to investigate whether steel fiber has a significant “positive” or “negative” influence on concrete compressive strength, as well as the optimal steel fiber ratio that delivers best result. Manually, cement, fine aggregates, coarse aggregates, steel fibers, and water were mixed together properly. A slump test was carried on the mixed concrete. After determining the workability, the mixed concrete was poured into cubes dimension 150 mm × 150 mm × 150 mm and left for 24 hours. After 24 hours, the samples were removed from the mold and placed in a water tank to cure for 7 to 28 days. The cube was tested for compressive and flexural strength in a universal testing machine after the samples had cured for the required 7 - 28 days. This study focuses on how to obtain high strength concrete using with steel fiber in the Conventional mix ratio to enhance concrete strength. Concrete reinforcement using steel fibers alters the characteristics of the concrete, allowing it to withstand fracture and hence improve its mechanical qualities. This study reports on an experimental study that reveals the effect of steel fiber on concrete compressive strength and the optimal steel fiber ratio that produces the best results. Steel fiber reinforcing improved the compressive strength of concrete. The average compressive strength of normal M25 concrete with 0% steel fibers and curing ages of 7 and 28 days was determined to be 22.97 N/mm<sup>2</sup> and 25.78 N/mm<sup>2</sup>, respectively. The steel fibers are then added in various concentrations, such as 1%, 2%, and 3%, with aspect ratios of 70. The compressive strength of concrete with 1%, 2%, and 3% steel fiber with an aspect ratio of 70 was examined at 7 days and found to be 23.96, 24.80, and 26.14 N/mm<sup>2</sup> correspondingly.
基金The authors would like to thank the MasterCard Foundation Scholars Program for the financial support provided to the first author.
文摘Recent developments on high-performance double-hooked-end steel fibers have enhanced the wide applications of steel fiber reinforced concrete(SFRC).This study presents the compressive properties and the cyclic flexural performance of the SFRC that were experimentally examined.Three different double-hooked-end steel fibers at 0.25%,0.5%,0.75%,and 1%volume fractions were considered.All fiber types had similar length to diameter ratios,while the first two fiber types had similar anchorage mechanisms(4D)and tensile strength and the third type had different anchorage mechanism(5D)and a higher tensile strength.The increased volumetric ratio of the fibers increased the post-peak compressive strain(ductility),the tensile strength,and the cyclic flexural strength and cumulative energy dissipation characteristics of the SFRC.Among the 4D fibers,the mixtures with the larger steel fibers showed higher flexural strength and more energy dissipation compared to the SFRCs with smaller size fibers.For 1%steel fiber dosage,4D and 5D specimens showed similar cyclic flexural responses.Finally,a 3D finite element model that can predict the monotonic and cyclic flexural responses of the double-hooked-end SFRC was developed.The calibration process considered the results obtained from the inverse analysis to determine the tensile behavior of the SFRC.
文摘The stress transfer mechanism of steel fibre reinforced concrete is studied. The solutions for the stress and displacement were regarded as the superposition of ' the elementary solutions' and ' the improved solutions'. The elementary solutions were found by using two-dimensional elastic theory and the improved solutions were found by using the Love displacement function method. The calculated results indicate that the solutions possess good convergence. By comparing the three-dimensional solutions with the shear-lag solutions, evident difference may be found.
基金Funded by the National Natural Science Foundation of China(No. 59938170and 50178044)the Natural Science Foundation of Jiangsu Province of China (No. BK2005216)
文摘Freeze-thaw durabilities of three types of concretesnormal portland cement concrete (OPC), high strength concrete (HSC) and steel fiber reinforced high strength concrete (SFRHSC) were systemically investigated under the attacks of chemical solution, and combination of external flexural stress and chemical solution. Four kinds of bitterns from salt lakes in Sinkiang, Qinghai, Inner Mongolia and Tibet provinces of China were used as chemical attack solutions. The relative dynamic modulus (RDM) was used as an index for evaluating the damage degree during the course of chemical attack and stress corrosion. The experimental results show that the freeze-thaw durability of concrete is visibly reduced in the present of the flexural stress, i e, stress accelerates the damage process. In order to quantify the stress accelerated effect, a stress accelerating coefficient was proposed. The stress accelerating coefficient is closely related with the types of bitterns and the numbers of freeze-thaw cycles is. The more numbers of freeze-thaw cycles is, the greater the stress accelerating coefficient for various concretes will be. In addition, there also exists a critical ratio of external stress to the maximum flexural stress. If the stress ratio exceeds the critical one, the freeze-thaw durability of various concretes will be greatly decreased compared to the responding concretes without applied stress. The critical stress ratio of OPC, HSC and SFRHSC is 0.30, 0.40 and 0.40, respectively, indicating that HSC and SFRHSC have advantages over OPC and are suitable to use in the bittern erosion regions.
文摘This paper presents a precise solution to predict the behavior of steel fiber reinforced concrete(SFRC) under the four point bending test(FPBT).All the force components at the beam section(before and after cracking) are formulated by applying these assumptions:a realistic stress-strain model is used for concrete behavior in compression,a linear response is considered for the uncracked tension region in a concrete constitutive model,and an exponential relationship is proposed as a stress-crack opening in the crack region which requires two parameters.Then the moment capacity of the critical cracked section is calculated by using these forces and satisfying equilibrium law at the section.Parametric studies are done on the behavior of SFRC to assess the sensitivity of the solution.Finally,this solution is validated with some existing experimental data.The result shows the proposed solution is able to estimate the behavior of SFRC under FPBT.
基金Funded by the National Natural Science Foundation of China (2008A430015)the Natural Science Foundation of Henan Educational Department of China(50879048)
文摘The article aimed to study the durability of steel fiber reinforced concrete under the coupled sewage-loading according to compressive strength,flexural strength,compressive strength corrosion coefficient,flexural strength corrosion coefficient,compressive strength balance coefficient,flexural strength balance coefficient.Through the homemade load frame applied to design specimens,the pre-loading level are equivalent the damage intensity of 0%,10%,30% and 50% four different ways.The experimental results show that the performance of concrete down gradually and sustaining load aggravated the degree of domestic sewage attacking concrete after six month;under different stress states,the more loading levels,the more serious domestic sewage attacked the steel fiber reinforced concrete.It is proved that the concrete damage can be inhibited by adding the steel fiber,when steel fiber volume fraction is 1.0%,the corrosion resistance of concrete is best.
文摘The road surface of cement concrete in highway is easily cracked and even destroyed due to inhomogeneous subsiding of the road foundation. In this work, a super-thin-coating material is prepared in order to repair the destroyed thin road surface, in which polymers and steel-fiber are added into ordinary concrete to form a steel fiber reinforced polymer-cement-based composite, the composite was successfully used to repair road surface. Microstructure and mechanical properties of the composites are measured and analyzed.
基金The National Natural Science Foundation of China (No.50278013)
文摘The objective of this study is to increase the insight into the mechanical behaviors of steel fiber reinforced high-performance concrete (SFHPC) after exposure to high temperatures. Three types of steel fibers were used and three-point bending tests on notched beams of SFHPC were carried out. The results showed that the flexural toughness and fracture energy of SFHPC increased evidently with the fiber content. The hooked steel fibers with higher strength possess higher flexural toughness and fracture energy than the marked steel fibers with lower strength. After exposure to high temperatures of 300, 600 and 900 ℃ in an electrical furnace, the compressive strength, flexural toughness and fracture energy of SFHPC decreased less than that of HPC without fibers, Both steel fiber content and type had strong influences on the flexural toughness and fracture energy. In addition, the failure patterns of SFHPC beams changed from pull-out of steel fibers at lower temperatures to tensile failure of steel fibers at 900 ℃.