The corrosion types of buried steel pipelines were summarized from two aspects of internal corrosion and external corrosion;the main detection technology for internal and external corrosion was introduced;and the prot...The corrosion types of buried steel pipelines were summarized from two aspects of internal corrosion and external corrosion;the main detection technology for internal and external corrosion was introduced;and the protective measures for corrosion and corrosion of buried steel pipelines were presented. The study of corrosion protection for buried steel pipeline provided the basis for the corrosion protection of buried steel pipeline.展开更多
A rectangle crevice assembly was used to study the effects of cathodic protection （CP） potential, crevice thickness, holiday size, bubbling CO2, and surface condition on the chemical and electrochemical environment ...A rectangle crevice assembly was used to study the effects of cathodic protection （CP） potential, crevice thickness, holiday size, bubbling CO2, and surface condition on the chemical and electrochemical environment of the local solution under disbonded coatings. It is found that the cathodic protection removes dissolved oxygen from the crevice and thus shifts the solution to a more al- kaline state. Furthermore, the potential of the steel reaches the protected potential range. The available protection distance increases with the negative applying potential. The steady potential and pH distribution are easily achieved, but the polarization degree is not satisfied within the thinner crevice. The difference in the solution environment is found to correlate to the holiday size. The smaller the holiday, the smaller the difference is. The presence of CO2 inhibits the formation of an alkaline environment. It is also found that the rust layer dramatically decreases the polarization rate in the crevice.展开更多
Electrochemical techniques, X-ray diffraction （XRD）, and scanning electron microscopy （SEM） were applied to study the corrosion behaviors of X65 steel in static solution with carbon dioxide （CO2） at 65℃. The re...Electrochemical techniques, X-ray diffraction （XRD）, and scanning electron microscopy （SEM） were applied to study the corrosion behaviors of X65 steel in static solution with carbon dioxide （CO2） at 65℃. The results show that iron carbonate （FeCO3） deposits on the steel surface as a corrosion product scale. This iron carbonate scale acts as a barrier to CO2 corrosion, and can reduce the general corrosion rate. The protection ability of the scale is closely related to the scale morphological characteristics.展开更多
目前,对管线钢在外加电位下的应力腐蚀开裂的研究尚不全面。应用慢应变速率拉伸、扫描电镜(SEM)观察和动电位极化测试方法,研究了在近中性模拟土壤溶液(NS4)中,不同阴极保护电位下X80管线钢的应力腐蚀开裂(SCC)行为。结果表明:X80管线钢...目前,对管线钢在外加电位下的应力腐蚀开裂的研究尚不全面。应用慢应变速率拉伸、扫描电镜(SEM)观察和动电位极化测试方法,研究了在近中性模拟土壤溶液(NS4)中,不同阴极保护电位下X80管线钢的应力腐蚀开裂(SCC)行为。结果表明:X80管线钢的SCC行为与阴极保护电位密切相关;在-850,-1 000,-1 200 m V(相对饱和硫酸铜电极)3个保护电位下,阴极过程析氢反应起主要作用,随着阴极保护电位的负移,X80管线钢的脆性逐渐增大;在-1 200 m V条件下SCC敏感性系数最高,形变硬化指数最低,SCC现象最为严重。展开更多
文摘The corrosion types of buried steel pipelines were summarized from two aspects of internal corrosion and external corrosion;the main detection technology for internal and external corrosion was introduced;and the protective measures for corrosion and corrosion of buried steel pipelines were presented. The study of corrosion protection for buried steel pipeline provided the basis for the corrosion protection of buried steel pipeline.
基金supported by the National Science & Technology Infrastructure Development Program of China (No.2005DKA10400)
文摘A rectangle crevice assembly was used to study the effects of cathodic protection （CP） potential, crevice thickness, holiday size, bubbling CO2, and surface condition on the chemical and electrochemical environment of the local solution under disbonded coatings. It is found that the cathodic protection removes dissolved oxygen from the crevice and thus shifts the solution to a more al- kaline state. Furthermore, the potential of the steel reaches the protected potential range. The available protection distance increases with the negative applying potential. The steady potential and pH distribution are easily achieved, but the polarization degree is not satisfied within the thinner crevice. The difference in the solution environment is found to correlate to the holiday size. The smaller the holiday, the smaller the difference is. The presence of CO2 inhibits the formation of an alkaline environment. It is also found that the rust layer dramatically decreases the polarization rate in the crevice.
文摘Electrochemical techniques, X-ray diffraction （XRD）, and scanning electron microscopy （SEM） were applied to study the corrosion behaviors of X65 steel in static solution with carbon dioxide （CO2） at 65℃. The results show that iron carbonate （FeCO3） deposits on the steel surface as a corrosion product scale. This iron carbonate scale acts as a barrier to CO2 corrosion, and can reduce the general corrosion rate. The protection ability of the scale is closely related to the scale morphological characteristics.
文摘目前,对管线钢在外加电位下的应力腐蚀开裂的研究尚不全面。应用慢应变速率拉伸、扫描电镜(SEM)观察和动电位极化测试方法,研究了在近中性模拟土壤溶液(NS4)中,不同阴极保护电位下X80管线钢的应力腐蚀开裂(SCC)行为。结果表明:X80管线钢的SCC行为与阴极保护电位密切相关;在-850,-1 000,-1 200 m V(相对饱和硫酸铜电极)3个保护电位下,阴极过程析氢反应起主要作用,随着阴极保护电位的负移,X80管线钢的脆性逐渐增大;在-1 200 m V条件下SCC敏感性系数最高,形变硬化指数最低,SCC现象最为严重。