Numerical simulation of melt flow and temperature field during DC casting 2024 aluminium alloy under different casting conditions

Casting speed,casting temperature and secondary cooling water flow rate are the main process parameters affecting the DC casting process.These parameters significantly influence the flow and temperature fields during casting,which are crucial for the quality of the ingot and can determine the success or failure of the casting operation.Numerical simulation,with the advantages of low cost,rapid execution,and visualized results,is an important method to study and optimize the DC casting process.In the present work,a simulation model of DC casting 2024 aluminum alloy was established,and the reliability of the model was verified.Then,the influence of casting parameters on flow field and temperature field was studied in detail by numerical simulation method.Results show that with the increase of casting speed,the melt flow becomes faster,the depths of slurry zone and mushy zone increase,and the variation of slurry zone depth is greater than that of mushy zone.With an increase in casting temperature,the melt flow rate increases,the depth of the slurry zone becomes shallower,and the depth of the mushy zone experiences only minor changes.The simulation results further indicate that the increase of the flow rate of the secondary cooling water slightly reduces the depths of both slurry and mushy zone.

Microstructural, wettability, and corrosion behaviour of TiO_(2) thin film sputtered on aluminium

The study investigated the application of radiofrequency(RF)-sputtered TiO2 coatings at various temperatures to enhance the hydrophobicity and corrosion resistance of Al6061 alloy.The research aimed to establish a correlation between the coating process and the resulting surface properties.Surface roughness and wettability were quantified with a surface profilometer and goniometer.Additionally,chemical boiling and salt spray corrosion tests were conducted to evaluate any topographical changes during these procedures.The analysis further involved the use of field-emission scanning electron microscopy(FESEM),energy-dispersive spectroscopy(EDS),and X-ray diffraction(XRD)techniques to characterize the deposited coatings.The findings indicated that the TiO2 coating applied at 500℃exhibited the highest water contact angle and superior corrosion resistance compared to other temperatures.Surface characterization confirmed that this specific TiO_(2) coating at 500℃ effectively delays corrosion due to its hydrophobic behavior,making it durable for industrial applications.

Static and Thermal Analysis of Aluminium (413,390,384 and 332) Piston Using Finite Element Method

The main objective of this research was to examine the suitability of aluminium alloy to design a piston of an internal combustion engine for improvement in weight and cost reduction. The piston was modelled using Autodesk Inventor 2017 software. The modelled piston was then imported into Ansys for further analysis. Static structural and thermal analysis were carried out on the pistons of the four different materials namely: Al 413 alloy, Al 384 alloy, Al 390 alloy and Al332 alloy to determine the total deformation, equivalent Von Mises stress, maximum shear stress, and the safety factor. The results of the study revealed that, aluminium 332 alloy piston deformed less compared to the deformations of aluminium 390 alloy piston, aluminium 384 alloy piston and aluminium 413 alloy piston. The induced Von Mises stresses in the pistons of the four different materials were found to be far lower than the yield strengths of all the materials. Hence, all the selected materials including the implementing material have equal properties to withstand the maximum gas load. All the selected materials were observed to have high thermal conductivity enough to be able to withstand the operating temperature in the engine cylinders.

Effectiveness of Sodium Silicate on the Corrosion Protection of AA7075-T6 Aluminium Alloy in Sodium Chloride Solution

The influence of sodium silicate on the corrosion behaviour of aluminium alloy 7075-T6 in 0.1 M sodium chloride solution was studied by open circuit potential (OCP) and electrochemical impedance spectroscopy (EIS) techniques. Scanning electron microscopy (SEM) was used to characterize the AA7075-T6 surface. Silicate can significantly reduce corrosion deterioration and the inhibition efficiency increases with the concentration of Na2SiO3. The corrosion inhibition mechanism involves the formation of a protective film over the alloy surface by adsorption of aluminosilicate anions from solution, as has also been suggested by others in literature.

基于热处理工艺的拖拉机发动机铝合金组织性能研究

采用不同时长的热处理工艺,对拖拉机发动机铝合金组织性能进行了对比分析。结果表明:热处理后,铝合金性能得到了较大程度的提高,若优先考虑材料性能,则应该采用180℃×4 h的单级热处理时效;若优先考虑工艺效率和成本,则可以采用150℃×1 h+170℃×1 h的双级热处理时效。

Microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy by micro-arc oxidation

The microstructure and mechanical properties of ceramic coatings formed on 6063 aluminium alloy obtained in silicate-,borate- and aluminate-based electrolyte without and with nanoadditive Al2O3 and TiO2 by micro-arc oxidation（MAO） were studied by scanning electron microscopy（SEM）,energy-dispersive X-ray spectroscopy（EDS）,X-ray diffraction（XRD）,microhardness and friction-abrasion tests,respectively.SEM results show that coatings with nanoadditive have less porosities than those without nanoadditive.XRD results reveal that nanoadditive-containing coatings contain more oxides compared with nanoadditive-free coatings in all cases,which are consistent with the EDS analysis.Mechanical properties tests show that nanoadditive Al2O3-containing coatings have higher microhardness values compared with the other coatings obtained in silicate-,borate- and aluminate-based electrolyte.On the other hand,nanoadditive has a positive effect on improving the wearing-resistance of MAO coatings in all cases.Furthermore,the borate-MAO coatings present an inferior anti-wearing property compared with the silicate- and aluminate-MAO coatings for both the nanoadditive-free and nanoadditive-containing coatings.

Shear deformation and plate shape control of hot-rolled aluminium alloy thick plate prepared by asymmetric rolling process

Asymmetric rolling （ASR）, as one of severe plastic deformation （SPD） methods to make ultra-fine materials with enhanced performance is mainly used to prepare foil and thin strip. The asymmetrical rolling was achieved by adjusting the diameters of the upper roll and the bottom roll and was used to prepare hot-rolled thick plate of 5182 aluminium alloy. The shear deformation and plate shape control were experimentally studied. The experimental results show that asymmetrical rolling has a significant effect on metal deformation stream and can somehow refine microstructure and improve the uniformity of microstructure and properties. The asymmetrical rolling process can also reduce the rolling force. However, bending of rolling plate often happens during asymmetrical rolling process. The factors affecting the bending were discussed.

Effect of additives on properties of aluminium titanate ceramics

The influence of some additives on bulk density,phase composition,mechanical strength and thermal shock resistance of aluminium titanate （AT） ceramics was investigated.AT ceramics with different additives of MgO,SiO2 and Fe2O3 were prepared by reaction sintering.Properties of AT ceramics were tested by using Archimedes,three-point bending and thermal cycling tests.It was found that additives of MgO,SiO2 and Fe2O3 or their compound additives are favorable to reduce the porosities of AT,enhance mechanical strength and thermal shock resistance.The role of additives can be rationalized in terms of promotion of sintering process,formation of new phases and influence on lattice constant c of AT ceramics.

Visualization and simulation of plastic material flow in friction stir welding of 2024 aluminium alloy plates

Thin copper sheets as marker material were embedded into weld path of 2024 aluminium alloy plates and their final position after friction stir welding was examined by metallographic techniques. Referring to the visualized material flow patterns, a three-dimensional model was developed to conduct the numerical simulation of the temperature profile and plastic material flow in friction stir welding. The calculated velocity contour of plastic flow in close proximity of the tool is generally consistent with the visualized results. As the tool rotation speed increases at a constant tool travel speed, the material flow near the pin gets stronger. The predicted shape and size of the weld nugget zone match with the experimentally measured ones.

Effect of pre-stretching on microstructure of aged 2524 aluminium alloy

The effects of pre-stretching following solution treatment on the hardness and microstructures of aged 2524 aluminium alloy at 170 ℃ were studied.Ageing hardness values under different pre-stretching conditions were measured,and the corresponding microstructures were characterized by transmission electron microscopy（TEM）.The results show that compared with unstretched samples,the peak hardness is increased and the time to reach the peak hardness is reduced with the increase of pre-strain;the number density of S（Al2CuMg） phases is increased and the length is shortened in pre-stretched alloy.Additionally,the number density of GPB zones is decreased with the increase of pre-strain in peak-aged samples.When the pre-strain is up to 5%,S phases play the predominant contribution to the peak hardness.Fine and uniformly distributed S phases lead to a higher hardness than GPB zones together with S phases existing in conventionally aged 2524 alloy.

Effect of electromagnetic field on microstructure and macrosegregation of flat ingot of 2524 aluminium alloy

Low frequency electromagnetic casting （LFEC） process with the application of an induction coil outside the conventional direct chill （DC） casting mould was used to prepare the flat ingot of 2524 alloy and the effect of electromagnetic field on the microstructure and macrosegregation of this alloy was systematically studied. The results show that the fiat ingot prepared by the LFEC process has a finer and more uniform as-cast microstructure and the grain morphology is transformed from dendrite and rosette-like to equiaxed structure. The LFEC process also shows a significant effect on macrosegregation, and with the application of electromagnetic field during casting process, the segregation in the centre of the ingot is obviously reduced. The mechanism of these effects was also discussed.

Simulation of extrusion process of complicated aluminium profile and die trial

The arbitrary Lagrangian-Eulerian（ALE） adaptive remeshing technology and the HyperXtrude software of transient finite element simulations were used on analogue simulation of aluminium extrusion processing.The field distributions of strain rate,stress,temperature and velocity of metal flow were obtained.The results are basically consistent with the experiment,which indicates that this method may successfully predict the defects in the actual extrusion process.

Fatigue behavior and life prediction of A7N01 aluminium alloy welded joint

Fatigue characteristics of A7N01 aluminium alloy welded joint were investigated and a fatigue crack initiation life-based model was proposed. The difference of fatigue crack initiation life among base metal, weld metal and heat affected zone (HAZ) is slight. Furthermore, the ratio of fatigue crack initiation life (Ni) to fatigue life to failure(Nf) is a material dependent parameter, 26.32%, 40.21% and 60.67% for base metal, HAZ and weld metal, respectively. Total fatigue life predicted using the presented model is in good agreement with the experimental data and that using Basquin’s model. The observation results of fatigue fracture surfaces, using scanning electron microscope (SEM), demonstrate that fatigue crack initiates from smooth surface due to welding process for weld metal, blowhole in HAZ causes fatigue crack initiation, and the crushed second phase particles play an important part in fatigue crack initiation in base metal.

Corrosion of NiFe_2O_4-10NiO-based cermet inert anodes for aluminium electrolysis

NiFe2O4-10NiO-based cermet inert anodes for aluminium electrolysis were prepared and their properties were investigated in a lab-scale electrolysis cell. The results show that the inert anodes exhibit good performance during electrolysis in molten salt cryolite at 960 °C, but according to the analyses of phase compositions and microstructures through XRD, SEM/EDX and metallographic analysis, the metal in the anodes is preferentially corroded and many pores are produced on the anode surface after electrolysis. The preferential dissolution of Fe in the NiFe2O4 phase may lead to the non-uniform corrosion of NiFe2O4 grains. Moreover, a dense protective layer of NiFe2O4-NiAl2O4-FeAl2O4 is formed on the anode surface, which originates from the reaction of Al2O3 dissolved in the electrolyte with NiO or FeO, the annexation of NiFe2O4-NiAl2O4-FeAl2O4 to NiO and volume expansion. Thus, the dense NiFe2O4-NiAl2O4-FeAl2O4 layer inhibits the metal loss and ceramic-phase corrosion on the surface of the cermet inert anodes.

Influence of introducing Zr,Ti,Nb and Ce elements on externally solidified crystals and mechanical properties of high-pressure die-casting Al–Si alloy

High pressure die casting(HPDC)AlSi10Mn Mg alloy castings are widely used in the automobile industry.Mg can optimize the mechanical properties of castings through heat treatment,while the release of thermal stress arouses the deformation of large integrated die-castings.Herein,the development of non-heat treatment Al alloys is becoming the hot topic.In addition,HPDC contains externally solidified crystals(ESCs),which are detrimental to the mechanical properties of castings.To achieve high strength and toughness of non-heat treatment die-casting Al-Si alloy,we used AlSi9Mn alloy as matrix with the introduction of Zr,Ti,Nb,and Ce.Their influences on ESCs and mechanical properties were systematically investigated through three-dimensional reconstruction and thermodynamic simulation.Our results reveal that the addition of Ti increased ESCs'size and porosity,while the introduction of Nb refined ESCs and decreased porosity.Meanwhile,large-sized Al_3(Zr,Ti)phases formed and degraded the mechanical properties.Subsequent introduction of Ce resulted in the poisoning effect and reduced mechanical properties.

Immunological Adjuvant Function of Aluminium Phosphate and Chicken IL-18 in NDV F Gene Vaccine

[Objective] This study aimed to investigate the immunological adjuvant function of aluminium phosphate and chicken IL-18 in NDV F gene vaccine. [Method] The vaccine （0.2 ml） containing aluminum phosphate adjuvant （90 μg）, pcDNA/F （200μg）, and pcDNA/chlL-18 （200 μg） was prepared. The 7 d old chick- ens to be tested were randomly divided into six groups （12 chickens in each group） and immunized through intramuscular injection with inactivated Newcastle disease vaccines, pcDNA/F＋pcDNA/chlL-18＋phosphate aluminum, pcDNA/F, pcDNA/F.＋pcDNA/ chlL-18, pcDNA/F＋aluminum phosphate, and physiological saline respectively; the secondary immunization was conducted with the same dose when the chickens were 21 d old. Their blood was sampled 0, 7, 14, 21, 28 d after first immunization. Anti- body titer was detected with ELISA and T cell transformation rate was measured with MIT. Experimental chicken will be challenged with 30 LD50 NDV virulence 28 d after first immunization. [Result] The survival rate of the chickens immunized with pcDNA/F＋aluminium phosphate＋pcDNA/chlL-18 achieved 8/12, higher than that of those immunized with pcDNA/F 4/12 and pcDNA/F＋pcDNA/chlL-18 （6/12）. The NDV antibody titer of the chickens immunized with pcDNA/F＋ aluminum phosphate, pcD- NA/F＋pcDNA/chlL-18 and pcDNA/F＋pcDNA/chlL-18＋aluminum phosphate is not differ- ent （P〉0.05）, but significantly lower than that of the chickens immunized with tradi- tional vaccine （P〈0.05）. The T cell transformation rate of the chickens immunized with pcDNA/F＋pcDNA/chlL-18＋aluminium phosphate was obviously higher than that of the chickens immunized with pcDNA/F （P〈0.05）. The T cell transformation rates of chickens immunized with pcDNA/F and the traditional vaccine showed no signifi- cant difference （P〉0.05）. [Conclusion] Combination of aluminium phosphate and pcD- NA/chlL-18 can significantly enhance the immune effect of NDV F gene vaccine.

Microstructural effects in corrosion of aluminium tube alloys

Fine gauge extruded aluminium alloy tubes can experience preferential corrosion and early failure when they are formed into ＂u-bend＂ via cold deformation. The relationship between the electrochemical reactivity and the microstructure of the bent vs straight parts of the tube was established. Investigations were carried out on two alloys containing 0.08% and 0.22% （mass fraction） of manganese. The corrosion morphology of bent tubes after immersion in salt water acetic acid test （SWAAT） solution showed the highest attack at the bent region of the high-Mn alloy. SEM characterisation of the alloys showed that each alloy has one main type of coarse intermetallic particle. However, TEM observation showed that there is a distinct difference in particle morphology between the bent and straight regions of the high-Mn tubes, the bent region revealed an additional population of 10 50 nm Mn-rich intermetallic particles, which increased both the anodic and cathodic reactivity. For the low-Mn alloy, no such effects were observed. The results suggested that cold deformation of the high-Mn tube allowed room temperature precipitation of fine Mn-rich particles, which increased the cathodic reactivity of that region by providing more cathodic sites, and increased the susceptibility to pitting by removing noble Mn from solid solution. Such an effect was not observed for the low-Mn alloy.

KINETICS OF THE DEPOSITION OF LITHIUM ON ALUMINIUM ELECTRODE

The kinetics of the deposition of lithium on aluminium electrode has been studied by cyclic voltammetry.The deposition of lithium on aluminium electrode was found to be controlled by the diffusion of lithium within the β-LiAl alloy probably through the vacancy mechanism. The limiting operating potential and current for prepanng the lithium aluminium electrodes were given.

Effect of post weld heat treatment on properties of variable polarity TIG welded AA2219 aluminium alloy joints

AA2219 aluminium alloy joints were fabricated by variable polarity tungsten inert gas （VPTIG） welding process and the effects of post weld heat treatment （PWHT） on the tensile properties, microstructure and fatigue behaviour of the welded joints were investigated. The VPTIG welding process was adopted because it could meet the need of cathode cleaning and meanwhile it could reduce the deterioration of tungsten electrode furthest. The welded samples were divided into as-welded （AW） sample and PWHT sample. The PWHT method used on the samples was solution treatment （535 ℃, 30 rain）, water quenching and artificial aging （175 ℃, 12 h）. The experimental results show that, compared with the AW samples, the microstructure characteristics and mechanical properties of the AA2219 joints after PWHT were significantly improved. The improvement of yield strength, ultimate tensile strength, and fatigue strength are 42.6%, 43.1% and 18.4%, respectively.

Prediction of flow stress of 7017 aluminium alloy under high strain rate compression at elevated temperatures

An artificial neural network(ANN) constitutive model and JohnsoneC ook(Je C) model were developed for 7017 aluminium alloy based on high strain rate data generated from split Hopkinson pressure bar(SHPB) experiments at various temperatures. A neural network configuration consists of both training and validation, which is effectively employed to predict flow stress. Temperature, strain rate and strain are considered as inputs, whereas flow stress is taken as output of the neural network. A comparative study on Johnsone Cook(Je C) model and neural network model was performed. It was observed that the developed neural network model could predict flow stress under various strain rates and temperatures. The experimental stressestrain data obtained from high strain rate compression tests using SHPB over a range of temperatures(25 e300 C), strains(0.05e0.3) and strain rates(1500e4500 s 1) were employed to formulate JeC model to predict the flow stress behaviour of 7017 aluminium alloy under high strain rate loading. The JeC model and the back-propagation ANN model were developed to predict the flow stress of 7017 aluminium alloy under high strain rates, and their predictability was evaluated in terms of correlation coefficient(R) and average absolute relative error(AARE). R and AARE for the J-C model are found to be 0.8461 and 10.624%, respectively, while R and AARE for the ANN model are 0.9995 and 2.58%, respectively. The predictions of ANN model are observed to be in consistent with the experimental data for all strain rates and temperatures.