Design Method and Performance for Large Stone Porous Asphalt Mixtures

Design method for large stone porous asphalt mixtures （LSPM） was analyzed to avoid the early distresses of semi-rigid asphalt pavements. Based on stone-to-stone skeleton structure concept, processes of LSPM gradation design was given. The gradation composite design for LSPM shows that the LSPM nominal maximum size （ N MS） should be larger than 26.5 mm, and the NMS sieve passing percentage should be greater than 50%. Through experiments and calculations on the volume properties of the aggregate, the range of aggregate gradation curve of LSPM was given. In terms of asphalt binder＇s normalized test results, MAC-70 and SBS modified asphalt were selected as the asphalt binders. The applicability of large scale Marshall Method and gyratory compaction method to shape specimens was investigated. Based on the asphalt mixture performance evaluation, the optimum asphalt content range （3.1%-3.6%）, the bitumen film＇s thickness range （13-16 μm） and the air void range （13%-18 %） were recommended. Finally, LSPM was tested by the laboratory performance tests including rutting resistance test, fatigue test and water stability test. The theoretic and practical analysis shows that LSPM has a good performance on water permeability, rutting resistance and reflection crack resistance.

Design of Small Stone Asphalt Mixture based on Anti-skidding Performance

Small stone asphalt mixture（SSAM） was designed by Bailey method and coarse aggregate voids-filling method.The optimum asphalt content was determined by Marshal test.Surface texture depth for SSAM with different voidage,and the BPN of SSAM and SMA before after wet track abrasion were measured.The experimental results indicate that the surface texture depth increases with the decreasing of asphalt aggregate ratio.The SSAM with the optimal asphalt content has a good skid resistance.BPN of asphalt mixture decreases with the increasing of wearing time,but the extent of reduction is different.The reduction rate of BPN for SSAM is smaller than that of SMA,indicating that SSAM has a good skid resistance attenuation capacity.Finally,the other properties of SSAM are also evaluated,showing that the splitting strength and modulus and SSAM are higher than those of SMA,and the other properties of SSAM,such as high-temperature performance and water stability can also satisfy the technical requirements.

Numerical analysis of reflective cracking and fatigue lives of semi-rigid pavement structures using ABAQUS and FE-SAFE

In order to compare the impact of thickness of different layers on fatigue lives of different semi-rigid asphalt pavement structures, the mechanical results from finite element models in ABAQUS are incorporated with the fatigue results from fatigue models in FE-SAFE to calculate the mechanical response and fatigue lives of semi-rigid pavement structures under heavy traffic loads. Then the influences on fatigue lives caused by the changes in the thickness of layers in pavement structures are also evaluated. The numerical simulation results show that the aggregated base and the large stone porous mixture （LSPM） base have better anti-cracking performance than the conventional semi-rigid base. The appropriate thickness range for the aggregated layer in the aggregated base is 15 to 18 cm. The thickness of the LSPM layer in the LSPM base is recommended to be less than 15 cm.