Influence of applied potentials and loading waveform on the fatigue crack growth for steel A537 in 3.5% NaCl solution,and corresponding straining electrode behaviour have been studied.Under the applied potentials over...Influence of applied potentials and loading waveform on the fatigue crack growth for steel A537 in 3.5% NaCl solution,and corresponding straining electrode behaviour have been studied.Under the applied potentials over or below -800mV(SCE),the anodic dissolution or the hydrogen embrittlement is predominatant,respectively.For applied anodic potential,the acceleration effect of continuous loading pattern on the CF crack growth mainly appeared at the range of low ΔK values,while for cathodic potential,it appeared at the high ΔK values.The continuous straining causes a decrease of natural potential and an increase of anodic dissolution current.展开更多
文摘Influence of applied potentials and loading waveform on the fatigue crack growth for steel A537 in 3.5% NaCl solution,and corresponding straining electrode behaviour have been studied.Under the applied potentials over or below -800mV(SCE),the anodic dissolution or the hydrogen embrittlement is predominatant,respectively.For applied anodic potential,the acceleration effect of continuous loading pattern on the CF crack growth mainly appeared at the range of low ΔK values,while for cathodic potential,it appeared at the high ΔK values.The continuous straining causes a decrease of natural potential and an increase of anodic dissolution current.