Poly（trimethyleneterephthalate）（PTT）/styrene-ethylene-buthylene-styrene（SEBS）composites were prepared by melt compounding.Polarizing opticalmicroscopy was used to observe the spherulitic morphology and the cryst...Poly（trimethyleneterephthalate）（PTT）/styrene-ethylene-buthylene-styrene（SEBS）composites were prepared by melt compounding.Polarizing opticalmicroscopy was used to observe the spherulitic morphology and the crystalstructure of PTT and PTT/SEBS composites.Scanning electron microscopy was used to determine the dispersion and the compatibility of fracture surfaces of PTT and SEBS.The curves of thermalgravimetric analysis illustrated that the thermo stability decreased with increasing SEBS content.Differentialscanning calorimetry was used to investigate the crystallization behavior;and the result showed that the glass transition temperature of the compound increased with the SEBS content.The Avramiequation described the isothermalcrystallization kinetics.Stress-strain curves for PTT and PTT/SEBS composites showed that the elongation at break was enhanced with increasing SEBS content.展开更多
通过熔融共混的方法制备了不同配比的聚苯硫醚(PPS)/马来酸酐接枝苯乙烯-乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS-g-MAH)共混物,采用热失重方法,分析了SEBS-g-MAH对PPS热稳定性能的影响,并且通过差示扫描量热分析法研究了SEBS-g-MAH对PPS结...通过熔融共混的方法制备了不同配比的聚苯硫醚(PPS)/马来酸酐接枝苯乙烯-乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS-g-MAH)共混物,采用热失重方法,分析了SEBS-g-MAH对PPS热稳定性能的影响,并且通过差示扫描量热分析法研究了SEBS-g-MAH对PPS结晶性能的影响,同时研究了PPS/SEBS-g-MAH共混物的力学性能。结果表明,共混物的热稳定性较纯PPS有所下降;PPS结晶峰宽度随SEBS-g-MAH含量的增加先减小后增大,结晶速率和结晶度较纯PPS减小,但对熔点影响较小;SEBS-g-MAH的加入使共混物的缺口冲击强度和断裂伸长率增大,韧性增加。当SEBS-g-MAH含量为40%时,缺口冲击强度为13.1 k J/m2,断裂伸长率为13.7%,但拉伸强度较纯PPS下降,为54.2 MPa。展开更多
以SEBS(苯乙烯-乙烯-丁烯-苯乙烯共聚物)、SBS(苯乙烯-丁二烯-苯乙烯共聚物)、丙烯酸酯、环保型溶剂和过氧化二苯甲酰(BPO)等为原料,制备出SEBS/SBS基胶粘剂,并着重考察了SEBS掺量对胶粘剂的黏度、光学性能、电性能、力学性能及粘接性...以SEBS(苯乙烯-乙烯-丁烯-苯乙烯共聚物)、SBS(苯乙烯-丁二烯-苯乙烯共聚物)、丙烯酸酯、环保型溶剂和过氧化二苯甲酰(BPO)等为原料,制备出SEBS/SBS基胶粘剂,并着重考察了SEBS掺量对胶粘剂的黏度、光学性能、电性能、力学性能及粘接性能等影响。研究结果表明:当w(SEBS)=5%~25%(相对于基体树脂总质量而言)时,胶粘剂的黏度适中,适合施工操作;当w(SEBS)=15%时,胶粘剂的接枝率、接枝效率(分别为17.11%、87.43%)相对最大,而单体转化率(为97.17%~98.36%)则变化不大;随着SEBS掺量的增加,胶粘剂的剪切强度或180°剥离强度呈先升后降态势,并且在w(SEBS)=25%或30%时相对最大(为1.87 MPa或1.73 k N/m),而且与不加SEBS体系相比分别增加了24.67%、140.28%。展开更多
基金Far Eastern New Century Corporation,Apex Nanotek Corporation,Grabio Greentech Corporation,ChingYung Trading Co.,Ltd.,Fabric King Textile Co.,Ltd.,Everlight Chemical Industrial Corporationthe Institute of Labor,Occupational Safety and Health,Ministry of Laborthe Ministry of Economic Affairs,and the National Science Council for supporting this work
文摘Poly（trimethyleneterephthalate）（PTT）/styrene-ethylene-buthylene-styrene（SEBS）composites were prepared by melt compounding.Polarizing opticalmicroscopy was used to observe the spherulitic morphology and the crystalstructure of PTT and PTT/SEBS composites.Scanning electron microscopy was used to determine the dispersion and the compatibility of fracture surfaces of PTT and SEBS.The curves of thermalgravimetric analysis illustrated that the thermo stability decreased with increasing SEBS content.Differentialscanning calorimetry was used to investigate the crystallization behavior;and the result showed that the glass transition temperature of the compound increased with the SEBS content.The Avramiequation described the isothermalcrystallization kinetics.Stress-strain curves for PTT and PTT/SEBS composites showed that the elongation at break was enhanced with increasing SEBS content.
文摘通过熔融共混的方法制备了不同配比的聚苯硫醚(PPS)/马来酸酐接枝苯乙烯-乙烯-丁二烯-苯乙烯嵌段共聚物(SEBS-g-MAH)共混物,采用热失重方法,分析了SEBS-g-MAH对PPS热稳定性能的影响,并且通过差示扫描量热分析法研究了SEBS-g-MAH对PPS结晶性能的影响,同时研究了PPS/SEBS-g-MAH共混物的力学性能。结果表明,共混物的热稳定性较纯PPS有所下降;PPS结晶峰宽度随SEBS-g-MAH含量的增加先减小后增大,结晶速率和结晶度较纯PPS减小,但对熔点影响较小;SEBS-g-MAH的加入使共混物的缺口冲击强度和断裂伸长率增大,韧性增加。当SEBS-g-MAH含量为40%时,缺口冲击强度为13.1 k J/m2,断裂伸长率为13.7%,但拉伸强度较纯PPS下降,为54.2 MPa。
文摘以SEBS(苯乙烯-乙烯-丁烯-苯乙烯共聚物)、SBS(苯乙烯-丁二烯-苯乙烯共聚物)、丙烯酸酯、环保型溶剂和过氧化二苯甲酰(BPO)等为原料,制备出SEBS/SBS基胶粘剂,并着重考察了SEBS掺量对胶粘剂的黏度、光学性能、电性能、力学性能及粘接性能等影响。研究结果表明:当w(SEBS)=5%~25%(相对于基体树脂总质量而言)时,胶粘剂的黏度适中,适合施工操作;当w(SEBS)=15%时,胶粘剂的接枝率、接枝效率(分别为17.11%、87.43%)相对最大,而单体转化率(为97.17%~98.36%)则变化不大;随着SEBS掺量的增加,胶粘剂的剪切强度或180°剥离强度呈先升后降态势,并且在w(SEBS)=25%或30%时相对最大(为1.87 MPa或1.73 k N/m),而且与不加SEBS体系相比分别增加了24.67%、140.28%。