Positron annihilation technique was used to study the micelle behaviors of two SBS triblock copolymers in MEK solvent at different temperatures. Annihilation lifetime τ_3 of ortho-positronium (o-Ps) exhibited an obvi...Positron annihilation technique was used to study the micelle behaviors of two SBS triblock copolymers in MEK solvent at different temperatures. Annihilation lifetime τ_3 of ortho-positronium (o-Ps) exhibited an obvious transition from shorter lifetime to longer lifetime with temperature. It was attributed to the change of micelle behavior of SBS copolymer molecules in the solution. Experimental results of sedimentation velocity of ultracentrifuge were also reported.展开更多
The thermal stability of oil gels formed by styrene-butadiene-styrene triblock copolymer (SBS) was improved by adding a small amount of poly(phenylene ether) (PPE), which has a higher glass transition temperature (Tg)...The thermal stability of oil gels formed by styrene-butadiene-styrene triblock copolymer (SBS) was improved by adding a small amount of poly(phenylene ether) (PPE), which has a higher glass transition temperature (Tg). In naphthenic oil which is a good solvent for the butadiene blocks, but a non-solvent for the styrene blocks and PPE, PPE was selectively included into styrene blocks in SBS, and induced the increase of the Tg of these blocks. The melting temperature determined by viscoelastic measurements and softening temperature of the gels were elevated by adding PPE, while no significant change was detected by adding polystyrene. The gel became opaque by adding PPE, and partially separated phases were observed by field emission scanning electron microscopy (FE-SEM). The dependence of the viscoelastic behavior on the PPE concentration can be explained by the structural change observed by FE-SEM.展开更多
文摘Positron annihilation technique was used to study the micelle behaviors of two SBS triblock copolymers in MEK solvent at different temperatures. Annihilation lifetime τ_3 of ortho-positronium (o-Ps) exhibited an obvious transition from shorter lifetime to longer lifetime with temperature. It was attributed to the change of micelle behavior of SBS copolymer molecules in the solution. Experimental results of sedimentation velocity of ultracentrifuge were also reported.
文摘The thermal stability of oil gels formed by styrene-butadiene-styrene triblock copolymer (SBS) was improved by adding a small amount of poly(phenylene ether) (PPE), which has a higher glass transition temperature (Tg). In naphthenic oil which is a good solvent for the butadiene blocks, but a non-solvent for the styrene blocks and PPE, PPE was selectively included into styrene blocks in SBS, and induced the increase of the Tg of these blocks. The melting temperature determined by viscoelastic measurements and softening temperature of the gels were elevated by adding PPE, while no significant change was detected by adding polystyrene. The gel became opaque by adding PPE, and partially separated phases were observed by field emission scanning electron microscopy (FE-SEM). The dependence of the viscoelastic behavior on the PPE concentration can be explained by the structural change observed by FE-SEM.