Study on Characteristics of Gold Powder with Round Shape for Maki-e

Maki-e is a traditional Japanese decorative technique that uses the natural lacquer Urushi and metal powders. Currently, there exist only two companies that manufacture metal powder for the purpose of Maki-e, and this research focuses on comparing the material characteristics of the gold powders with round shape manufactured by them. EDS (energy-dispersive X-ray spectroscopy) analysis, image analysis of particle shape before and after Maki-e processing, and color analysis of samples after Maki-e processing were carried out in this research. The study revealed that current gold powders with round shape had almost the same content ratio regardless of the manufacturing company and the powder diameter. In addition, spherical shape and irregular shape were observed in any gold powders, and the aggregates were observed in powder with increasing the powder diameter, while the shape of the aggregates differed with manufacturing companies. Therefore, it was indicated that the aggregates in the powder made by Asano Co., Ltd. had an influence on the particle diameter and its deviation after Maki-e processing. Moreover, the powder in Urushi resin has an influence on the Maki-e appearance because there is a color difference in polished powder, powder in Urushi resin, and Urushi resin.

基于Voigt函数拟合的能量色散X射线荧光光谱(EDXRF)法测定金矿粉末中低品位金

为了提高金矿粉末含金量检测的准确性和安全性,以金矿粉末为研究对象,运用能量色散X射线荧光光谱法(EDXRF)对金矿粉末进行检测,利用Voigt函数拟合分离出金元素的Lα纯元素特征峰,分析测定金矿粉末中金的含量。在实验中,发现金的Lα峰与锌的Kβ峰存在明显重叠,为了排除锌元素的干扰,引入降噪技术和Voigt函数进行分峰处理,利用纯锌和纯金的标准溶液配制符合金矿粉末样品中锌金四种比例的混合溶液,通过滤波和降噪算法处理得到相对纯净的重叠峰,加入Voigt函数拟合分离锌和金的重叠峰,得到金的Lα峰净强度值,通过纯金和纯锌标准溶液建立回归线得到金矿粉末中金的真实含量,对比金矿粉末的参考含量数据,偏差度皆小于10%,含量大于3 g/t以上偏差值则小于2%,结合EDXRF法对检测样品无损伤的特点,提高了金矿中金含量检测的安全性、准确性和可靠性。

人丝/人棉缎织物复合印花工艺

以有光人丝为经纱与人棉纬纱织成的缎类织物,经过活性印花+涂料印花+金粉印花复合印花工艺,可以达到蚕丝印花织物的手感和色泽,且印花图案精细、立体感强。介绍了织物的印染生产流程、工艺参数及注意事项。该工艺得到的人丝/人棉缎活性印花织物富有层次感,解决了活性色浆与金粉胶浆叠加造成的金粉黏合牢度差的问题;印花织物的断裂强力降低10%以内,撕破强力降低15%以内;耐摩擦色牢度、耐水洗色牢度、耐汗渍色牢度等均可达3~4级以上;成品缩率经向仅0.2%、纬向0.1%。

金尾矿粉对C25混凝土力学性能及微观结构影响试验研究

为研究金尾矿粉取代水泥对低强混凝土力学性能的影响,通过金尾矿粉等质量取代0~30%水泥,研究其对C25混凝土凝结时间以及力学性能的影响,并采用扫描电镜(SEM)和X射线衍射仪(XRD)等手段表征硬化浆体的水化产物、微观形貌。结果表明,金尾矿粉作为辅助胶凝材料能延长C25混凝土的凝结时间,金尾矿粉掺量在30%范围内,坍落度和凝结时间均可满足普通硅酸盐水泥标准要求。C25混凝土的抗压强度、轴心抗压强度、静弹性模量,均随着金尾矿粉掺量的增加,呈现出先增加后降低的趋势,在掺量5%时出现峰值。随着养护龄期的增加,金尾矿粉颗粒表面被水化产物覆盖,结构紧密孔隙较少,表现出良好的力学性能。但随着金尾矿粉替代率的增加,水化产物减少微观结构松散,力学性能降低。

锌粉置换工艺中脱氧塔填料改良研究

为解决某黄金冶炼厂锌粉置换工艺中脱氧塔长期运行后产生的脱氧贵液含氧量偏高问题,对脱氧塔填料类型和装填方式开展了一系列改良研究。通过对脱氧率、置换贫液、金泥品位等多项工艺指标进行深入对比分析,发现采用聚丙烯鲍尔环替代塑料点波填料,可明显缓解填料结钙后缝隙易被堵塞的问题,较好地改善脱氧塔的脱氧性能,锌粉消耗量明显降低,置换贫液贵金属品位降低,金泥品位得到提升。填料的改良延长了脱氧塔的使用周期,减少了贱金属元素对金泥冶炼过程的干扰,经济效益显著。

掺黄金尾矿粉水泥基复合胶凝材料的制备及性能研究

研究了黄金尾矿粉掺量(0、10%、20%、30%)对净浆流动度和强度的影响,并对净浆配合比进行了优化;在此基础上,研究了黄金尾矿粉掺量对混凝土坍落度和强度的影响。结果表明:黄金尾矿粉的掺入增大了净浆的流动度,但降低了强度,可通过适当降低水胶比的方式优化净浆配合比;优化后掺黄金尾矿粉净浆的流动度与对照组相当,且随着黄金尾矿粉掺量从10%增至30%,净浆试件的抗压强度逐渐增大;在混凝土坍落度基本相同的前提下,当黄金尾矿粉掺量为30%时,混凝土试件的28 d抗压强度较对照组仅降低了5.88%;当黄金尾矿粉掺量为10%时,混凝土试件的28 d劈裂抗拉强度相对最高。

哥伦比亚某金矿提高锌粉置换率试验研究

哥伦比亚某金矿从全泥氰化技改为先进行硫浮选,然后硫浮选精矿进行浸出的工艺流程后,贵液锌粉置换率低,金属流失,回收金效果差,贵液品位约1.5~1.8g/t,相比技改前期上升27%左右。通过开展氰化钠浓度、锌粉用量、醋酸铅用量、PH值单因素试验,优化药剂制度,提高氰化钠与醋酸铅用量,金作业置换率稳定在99.0%以上,贫液金品位降低至0.015 ppm以内,尾矿带走水分中金含量下降,彻底解决了因置换率低造成金属流失的问题,保证了锌粉置换作业技术指标。

肺脾相关理论在肺系疾病中的运用

肺系疾病的发生与其他脏腑密切相关,中医理论认为肺与脾的关系密切,两者之间的关系在古代文献中论述颇多,通过理论探讨,肺脾之间在生理上以及病理上都存在着密切的关系,生理上存在经脉联络、五行相生、气的形成与运行及津液代谢的关系,病理上主要有津液代谢异常、气的形成及气机异常,肺脾同治在临床当中运用较为广泛,许多经典名方,如玉屏风散、参苓白术散、补中益气汤等都体现肺脾同治,运用肺脾同治的治疗方法在临床当中治疗肺系相关疾病时可以大大提升临床疗效。

从金还原后液中回收贵金属的试验研究

探索以树脂吸附代替锌粉置换,从金还原后液中回收金、铂、钯。由试验结果可见:该方法可行,金、铂、钯的吸附效果很好,铂的吸附效果受进液流速的影响较大。选择树脂吸附新工艺路线,有利于金还原后液中贵金属的富集与提取,并可减少生产工序,降低贵金属损失,产生较好的经济效益。

形貌可控金粉的制备及其对LTCC导体浆料性能的影响

金导体浆料因具有较好的稳定性与可焊性而被广泛应用于低温共烧陶瓷(LTCC)中。金粉的表面形貌、粒径等性质会对金导体浆料产生较大影响。以氯金酸为原料、D-异抗坏血酸为还原剂、阿拉伯树胶为分散剂,采用不同试验条件制备了纯度较高的三种类球形金粉,且三种金粉的表面形貌、粒径与比表面积均不同。金粉生长过程属于种子介导的生长方法,控制Cl-浓度与反应液pH值最终可获得不同形貌与粒径的金粉。研究表明,三种金粉的比表面积分别为0.740、0.418、0.447 m^(2)·g^(-1)。金粉比表面积显著影响金浆的黏度,以三种金粉为功能相,在相同配比下制备LTCC用金导体浆料,其黏度分别为326、209及214 Pa·s。试验结果表明,以NaOH溶液溶解氯金酸并调整氯金酸溶液pH值为2,30%(质量分数)二乙二醇乙醚溶液作还原剂溶剂时制得的金粉为功能相来制备金导体浆料,烧结后膜层致密度最高、方阻较低以及金丝键合强度最高,其方阻与金丝键合强度分别为1.11 mΩ/□与8.66 g,三种金导体浆料均具有较好的可焊性。

半导体芯片用5N级微米导电金球的制备

微米球形金属粉制备技术已经成为芯片、医疗诊断、3D打印等领域共性的“卡脖子”技术。采用“全湿法制粉+等离子球化”工业制备高纯导电金球,以自产的Au-99.999%为原料,水合肼作为还原剂,PVP作为稀散剂,控制还原电势在1 692~1 002 mV,制得高纯高分散金粉,经气流破碎、等离子球化得到半导体芯片用5N级微米导电金球。该方法目前已经实现工业化10 kg批次量产,初步解决国产芯片封装用导电金球被国外卡脖子的问题,为完善我国芯片研发产业链特别是电子级金原料研发作出重要贡献。

从低金高杂质氯化溶液中制备高品质粗金粉的试验研究

针对从杂质含量高的含金氯化溶液中还原得到的粗金粉品质波动问题,进行了SO 2气体从低金高杂质氯化溶液中直接还原制备粗金粉的试验研究。结果表明:所得粗金粉金品位可达99.95%以上,为高品质粗金粉。该方法步骤简便,适用性广,有价金属回收率高,特别克服了严寒地区或冬季气温低问题,保障了工艺稳定性。

锌粉置换回收锑精矿碱浸液中的金

锑精矿碱浸液是湿法处理锑精矿产生的中间产物含有少量的金,必须回收。以山东某公司锑精矿碱浸液为原料,经多种提取剂对比,采用锌粉置换回收其中的金。考察了锌粉用量、料液pH、浸出温度、时间的影响,得到的最佳工艺条件为:锌粉用量4.0 kg/m^(3),溶液pH=11,反应时间3 h,反应温度80℃,多批次试验金回收率88%。工艺过程简单,经济性可行,有效解决了资源浪费问题,为锑精矿碱浸液回收金提供了一条新的工艺。

提高4N金粉生产一次合格率的改进措施

黄金属高价值贵金属,其产品一次合格率低对企业效益影响很大。分析影响4N金粉生产一次合格率的主要原因是银含量超标。试验改进了粗金粉精制还原工艺,在原金还原化学精炼工艺中增加氧化酸浸—控电还原工序,并在氯化液过滤前增加冷却系统。试验结果表明,粗金粉精制还原工艺改进后,生产的4N金粉平均品位达到99.997%,含银仅为0.001%,一次合格率达到100%。

Five Recent Books on Super-fine Powders

Presenting five monographs on the technology of superfine powders including their preparation, measurement and application, and ranging from catalysts through medicines and cosmetics to pyrotechnics.

锌粉置换硫代硫酸盐浸金液中金试验研究

以10μg/L金标准液与硫代硫酸钠、氨水合成浸金液,采用锌粉置换法回收所合成浸金液中的金。结果表明:锌粉用量增加,金置换率提高;选取锌粉用量为0.4 g/L,随反应时间增加,金置换率下降;浸金液中铜离子和单质S、SO_4^(2-)、SO_3^(2-)等多硫化物对置换反应不利;游离硫代硫酸盐对置换影响较小;添加铅盐对置换反应有利。SEM-EDS分析表明,经5%乙酸铅溶液浸泡后的锌粉表面有铅生成,生成的铅与锌形成电偶加速置换反应,同时,锌粉表面变蓬松,增大了锌粉与Au(S_2O_3)_2^(3-)的接触面积,有利于置换反应的进行。

铁粉还原法从含金滤液中回收金银铜

采用铁粉还原法回收含金滤液中的金、银、铜等有价金属。考察了铁粉添加量、还原时间、还原温度对金属置换率的影响。结果表明,当铁粉添加量为5kg/m^3,在40℃反应30min,含金滤液中金、银、铜含量分别从2.4、53、950mg/L降至0.05、0.4、7mg/L。置换后所得滤饼中金、银、铜分别达到386.8g/t、5 521.7g/t和29.8%。

中温固化的金导电胶的研究

一种金导电胶，由改性的酚类树脂（NF）、片状金粉与球状金粉的混合粉末、少量锑粉和醇类为主的溶剂组成，固化温度范围150－300℃，体积电阻率5×10(-4)Ω．cm，存放或可达半年以上，该导电胶可应用在二、三极管及组合电路中。

陕西驾鹿金矿床发现40种含氧金矿物——物性、X射线衍射及晶体结构初步分析

指出驾鹿金矿床发现的４０种含氧金矿物呈不同色调的褐、紫、黑等色，多为不规则粒状微细晶集合体，粒径在０．０１ｍｍ～０．５ｍｍ之间；条痕紫、黑色，半金属光泽，不透明；反射多色性显著；摩氏硬度为２～３。Ｘ射线衍射分析表明，大部分的晶体结构可能是由Ａｕ，Ａｇ，Ｃｕ，Ｆｅ或Ｐｂ等金属互化物组成的假立方晶格与一个由β－ＴｅＯ２（可能包括ＰｂＯ或ＣａＯ）组成的斜方晶格的混晶，但不排除它们是含金氧化物的可能性；还有些可能是玻璃质或纳米级矿物，少部分则呈现了准晶态物质的特征。

一种用于扩散连接的金浆料

研制了一种用于扩散连接的金浆料。这种浆料主要由金粉和有机载体组成。浆料的烧成特性和粘度对扩散连接强度影响较大。金粉的分散性、表面形态和颗粒尺寸会影响浆料的烧成特性和粘度。载体会影响浆料的粘度。