A superabsorbent polymer was prepared by grafting sodium acrylate （ SA ） onto Konjac flour using potassium persulfate （KPS） and N, N＇-methylene bis acrylamide （ MBA ） as an initiator and crosslinker , respectiv...A superabsorbent polymer was prepared by grafting sodium acrylate （ SA ） onto Konjac flour using potassium persulfate （KPS） and N, N＇-methylene bis acrylamide （ MBA ） as an initiator and crosslinker , respectively. The effect of various preparation conditions on its water absorbency was investigated. When the Konjac Flour content was 3.0g, the acrylic acid （AA） content was 30.0 g, the amount of initiator was 0. 150 g, the neutralization degree of monomer was 85% , the reaction temperature was 60 ℃ and the amount of crosslinker was 0.025 g, the polymer＇s absorbency was 750 times in pure water and 279 times in tap water at ambient temperature. It had also high water retention. The graft efficiency reached 67% . The analyses of FT-IR and SEM indicate that sodium acrylate is grafted on the polysaccharides of Konjac flour.展开更多
The effectiveness of a superabsorbent polymer of sodium polyacrylate was studied, with emphasis on water management, i.e., absorption, retention and desorption in the soil. The polymer was applied in plots with a sand...The effectiveness of a superabsorbent polymer of sodium polyacrylate was studied, with emphasis on water management, i.e., absorption, retention and desorption in the soil. The polymer was applied in plots with a sandy soil near Grandola (southern Portugal). Characterization of the most relevant physical and chemical properties of the polymer was made, namely, its specific gravity, particle diameter, capacity of water absorption and desorption. In the plots with and without the polymer, soil moisture was continuously monitored, and grassland biomass samples were collected and weighed. The results reflected the effective role of the polymer both in the improvement of the water regime in the soil and in the substantial increment of grassland productivity.展开更多
Superabsorbents starch grafted sodium polyacrylate was synthesized by inverse suspension polymerization, using toluene as the continuous phase, potassium persulfate as the initiator. The effect of reaction parameters,...Superabsorbents starch grafted sodium polyacrylate was synthesized by inverse suspension polymerization, using toluene as the continuous phase, potassium persulfate as the initiator. The effect of reaction parameters, such as starch pretreatment temperature, neutralization degree of monomer, reaction time and temperature, concentration of initiator, molar ratio of monomer and starch, on water absorbency of the starch grafted polymer was studied. The effects of the last two parameters were investigated by uniform design method, and the prediction equation was obtained.展开更多
采用乳液聚合方法将引发剂过硫酸铵(APS)和乳化剂十二烷基硫酸钠(SDS)制备出聚丙烯酸树脂乳液,再加入不同条件交联剂固化成聚丙烯酸(PAA)水凝胶,并探究使用紫外固化和热固化2种不同固化方式及不同固化时间对PAA水凝胶性能的影响。通过...采用乳液聚合方法将引发剂过硫酸铵(APS)和乳化剂十二烷基硫酸钠(SDS)制备出聚丙烯酸树脂乳液,再加入不同条件交联剂固化成聚丙烯酸(PAA)水凝胶,并探究使用紫外固化和热固化2种不同固化方式及不同固化时间对PAA水凝胶性能的影响。通过氮气等温吸脱附曲线测试(Brunauer-Emmet-Teller,BET)、扫描电子显微镜(scanning electron microscope,SEM)、热失重分析(thermogravimetric analysis,TGA)、溶胀度、力学测试等方法,对水凝胶的性能进行表征分析。结果表明,形成的PAA水凝胶主要为片状颗粒材料,在紫外固化20 min条件下,其孔径主要分布在2~4 nm;且在热固化条件下,当交联剂质量浓度为0.06、0.07 g/mL时PAA水凝胶溶胀度可达到667%,在交联剂质量浓度为0.09 g/mL时拉伸强度可达到60 k Pa。综上所述,对比紫外固化和热固化2种方法以及不同条件交联剂下制备的PAA水凝胶的差异,对理解和优化PAA水凝胶的制备具有一定的指导意义。展开更多
基金Funded by the Project Hubei Provincial Science &TechnologyDepartment ,China(2001AA207B02)
文摘A superabsorbent polymer was prepared by grafting sodium acrylate （ SA ） onto Konjac flour using potassium persulfate （KPS） and N, N＇-methylene bis acrylamide （ MBA ） as an initiator and crosslinker , respectively. The effect of various preparation conditions on its water absorbency was investigated. When the Konjac Flour content was 3.0g, the acrylic acid （AA） content was 30.0 g, the amount of initiator was 0. 150 g, the neutralization degree of monomer was 85% , the reaction temperature was 60 ℃ and the amount of crosslinker was 0.025 g, the polymer＇s absorbency was 750 times in pure water and 279 times in tap water at ambient temperature. It had also high water retention. The graft efficiency reached 67% . The analyses of FT-IR and SEM indicate that sodium acrylate is grafted on the polysaccharides of Konjac flour.
文摘The effectiveness of a superabsorbent polymer of sodium polyacrylate was studied, with emphasis on water management, i.e., absorption, retention and desorption in the soil. The polymer was applied in plots with a sandy soil near Grandola (southern Portugal). Characterization of the most relevant physical and chemical properties of the polymer was made, namely, its specific gravity, particle diameter, capacity of water absorption and desorption. In the plots with and without the polymer, soil moisture was continuously monitored, and grassland biomass samples were collected and weighed. The results reflected the effective role of the polymer both in the improvement of the water regime in the soil and in the substantial increment of grassland productivity.
文摘Superabsorbents starch grafted sodium polyacrylate was synthesized by inverse suspension polymerization, using toluene as the continuous phase, potassium persulfate as the initiator. The effect of reaction parameters, such as starch pretreatment temperature, neutralization degree of monomer, reaction time and temperature, concentration of initiator, molar ratio of monomer and starch, on water absorbency of the starch grafted polymer was studied. The effects of the last two parameters were investigated by uniform design method, and the prediction equation was obtained.
文摘采用乳液聚合方法将引发剂过硫酸铵(APS)和乳化剂十二烷基硫酸钠(SDS)制备出聚丙烯酸树脂乳液,再加入不同条件交联剂固化成聚丙烯酸(PAA)水凝胶,并探究使用紫外固化和热固化2种不同固化方式及不同固化时间对PAA水凝胶性能的影响。通过氮气等温吸脱附曲线测试(Brunauer-Emmet-Teller,BET)、扫描电子显微镜(scanning electron microscope,SEM)、热失重分析(thermogravimetric analysis,TGA)、溶胀度、力学测试等方法,对水凝胶的性能进行表征分析。结果表明,形成的PAA水凝胶主要为片状颗粒材料,在紫外固化20 min条件下,其孔径主要分布在2~4 nm;且在热固化条件下,当交联剂质量浓度为0.06、0.07 g/mL时PAA水凝胶溶胀度可达到667%,在交联剂质量浓度为0.09 g/mL时拉伸强度可达到60 k Pa。综上所述,对比紫外固化和热固化2种方法以及不同条件交联剂下制备的PAA水凝胶的差异,对理解和优化PAA水凝胶的制备具有一定的指导意义。