The microstructure and precipitation characteristics of 22Cr-14W-2Mo superalloys added with various La contents have been studied by SEM, TEM and EDX.It is found that the carbides are refined by adding La.M23C6 carbid...The microstructure and precipitation characteristics of 22Cr-14W-2Mo superalloys added with various La contents have been studied by SEM, TEM and EDX.It is found that the carbides are refined by adding La.M23C6 carbides inside the grain in a diameter of 50 nm have a cube-cube orientation relationship with the matrix, and these precipitates on {111} planes align along 110 orientation.Since the large dissolved La atom will be a barrier to atom diffusion, it leads to an inhibiting effect on the carbides growing.M6C carbides are influenced by La-S phases.La-S phases formed in the center of M6C seem to be the heterogeneous nucleus of M6C to increase the nucleation ratio.It is also noticed that finer M6C carbides precipitated on the {111} planes of the matrix are around large M6C.The finer M6C carbides are caused by the special absorption effect of La-S phases.展开更多
基金supported by the Program for Changjiang Scholars and Innovative Research Teams in Chinese Universities (No. IRT0713)the National Natural Science Foundation of China (No. 50841025)
文摘The microstructure and precipitation characteristics of 22Cr-14W-2Mo superalloys added with various La contents have been studied by SEM, TEM and EDX.It is found that the carbides are refined by adding La.M23C6 carbides inside the grain in a diameter of 50 nm have a cube-cube orientation relationship with the matrix, and these precipitates on {111} planes align along 110 orientation.Since the large dissolved La atom will be a barrier to atom diffusion, it leads to an inhibiting effect on the carbides growing.M6C carbides are influenced by La-S phases.La-S phases formed in the center of M6C seem to be the heterogeneous nucleus of M6C to increase the nucleation ratio.It is also noticed that finer M6C carbides precipitated on the {111} planes of the matrix are around large M6C.The finer M6C carbides are caused by the special absorption effect of La-S phases.