CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage ...CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage capacities of these ternary oxides were characterized by XRD, Raman spectra and oxygen storage capacity measurements. It was found that Al3＋ and Zr4＋ inserted into CeO2 lattice, forming CeO2-ZrO2-Al2O3 solid solution. The concentration of aluminium isopropoxide in the solution affected the concentration of oxygen vacancy and the distortion of oxygen sublattice which were responsible for the oxygen storage capacity. The rapidest oxygen uptake/release rate and maximum total oxygen storage capacity （122.0 mmolO2/molCeO2） were obtained with the aluminitun isopropoxide concentration at 0.2 wt.% in the solution.展开更多
Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperat...Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperature） were investigated to explore the effects of catalyst structure and physic-chemical properties （i.e., morphology, reducing property, oxygen storage capacity and specific surface area）. The resulting materials were characterized with X-ray diffraction （XRD）, high resolution transmission electron micros-copy （HRTEM）, Brunauer-Emmett-Teller （BET）,hydrogen temperature programmed reduction （H2-TPR） and oxygen storage capac-ity （OSC） measurement, respectively. The experimental results showed that lower temperatures promoted production of hollow struc-ture nano-particulates. The particle morphology also changed significantly, i.e. the solid construction was first transferred to hollow structure then back to solid construction. The optimal conditions for obtaining hollow nano-particles were determined at 45 °C, 18.0–24.0 MPa.展开更多
Taking extraction rate as an indicator,the extraction technology of Chinese-fir heartwood by supercritical carbon dioxide treatment was studied, and the extraction rate of the SFE-CO<sub>2</sub> method was...Taking extraction rate as an indicator,the extraction technology of Chinese-fir heartwood by supercritical carbon dioxide treatment was studied, and the extraction rate of the SFE-CO<sub>2</sub> method was compared to that of traditional extraction method. The results show that when extraction processing condition were:extraction pressure 30 MPa,extraction temperature 40℃,extraction time 120 m,and flow velocity 20 kg/h,the extraction rate of SFE-CO<sub>2</sub> was 0.99%,0.20%more than that of the traditional extraction method.However,taking the cost into consideration,it is proposed that the traditional extraction is used unless there are specific requirements.展开更多
基金National Natural Science Foundation of China(20976120)the Natural Science Foundation of Tianjin(09JCYBJC06200)
文摘CeO2-ZrO2-Al2O3 ternary oxides were successfully prepared by a green route of supercritical anti-solvent precipitation with supercritical CO2 as anti-solvent and methanol as solvent. The structures and oxygen storage capacities of these ternary oxides were characterized by XRD, Raman spectra and oxygen storage capacity measurements. It was found that Al3＋ and Zr4＋ inserted into CeO2 lattice, forming CeO2-ZrO2-Al2O3 solid solution. The concentration of aluminium isopropoxide in the solution affected the concentration of oxygen vacancy and the distortion of oxygen sublattice which were responsible for the oxygen storage capacity. The rapidest oxygen uptake/release rate and maximum total oxygen storage capacity （122.0 mmolO2/molCeO2） were obtained with the aluminitun isopropoxide concentration at 0.2 wt.% in the solution.
基金supported by the National Natural Science Foundation of China(20976120)Natural Science Foundation of Tianjin(09JCYBJC06200)
文摘Hollow CuO-CeO2-ZrO2nano-particles were prepared with supercritical anti-solvent apparatus by using methanol as sol-vent and supercritical carbon dioxide as anti-solvent. Two key factors （i.e., pressure and temperature） were investigated to explore the effects of catalyst structure and physic-chemical properties （i.e., morphology, reducing property, oxygen storage capacity and specific surface area）. The resulting materials were characterized with X-ray diffraction （XRD）, high resolution transmission electron micros-copy （HRTEM）, Brunauer-Emmett-Teller （BET）,hydrogen temperature programmed reduction （H2-TPR） and oxygen storage capac-ity （OSC） measurement, respectively. The experimental results showed that lower temperatures promoted production of hollow struc-ture nano-particulates. The particle morphology also changed significantly, i.e. the solid construction was first transferred to hollow structure then back to solid construction. The optimal conditions for obtaining hollow nano-particles were determined at 45 °C, 18.0–24.0 MPa.
文摘Taking extraction rate as an indicator,the extraction technology of Chinese-fir heartwood by supercritical carbon dioxide treatment was studied, and the extraction rate of the SFE-CO<sub>2</sub> method was compared to that of traditional extraction method. The results show that when extraction processing condition were:extraction pressure 30 MPa,extraction temperature 40℃,extraction time 120 m,and flow velocity 20 kg/h,the extraction rate of SFE-CO<sub>2</sub> was 0.99%,0.20%more than that of the traditional extraction method.However,taking the cost into consideration,it is proposed that the traditional extraction is used unless there are specific requirements.