Atomic layer deposition of Al_2O_3 on porous polypropylene hollow fibers for enhanced membrane performances

Porous polypropylene hollow fiber(PPHF) membranes are widely used in liquid purification. However, the hydrophobicity of polypropylene(PP) has limited its applications in water treatment. Herein, we demonstrate that, for the first time, atomic layer deposition(ALD) is an effective strategy to conveniently upgrade the filtration performances of PPHF membranes. The chemical and morphological changes of the deposited PPHF membranes are characterized by spectral, compositional, microscopic characterizations and protein adsorption measurements. Al_2O_3 is distributed along the cross section of the PP hollow fibers, with decreasing concentration from the outer surface to the inner surface. The pore size of the outer surface can be easily turned by altering the ALD cycles. Interestingly, the hollow fibers become much more ductile after deposition as their elongation at break is increased more than six times after deposition with 100 cycles. The deposited membranes show simultaneously enhanced water permeance and retention after deposition with moderate ALD cycle numbers.For instance, after 50 ALD cycles a 17% increase in water permeance and one-fold increase in BSA rejection are observed. Moreover, the PP membranes exhibit improved fouling-resistance after ALD deposition.

Investigation of anti-corrosion property of hybrid coatings fabricated by combining PEC with MAO on pure magnesium

Novel hybrid coatings on pure magnesium were prepared by combining plasma electrolytic carburizing(PEC)with micro-arc oxidation(MAO)to further enhance the anti-corrosion property in this paper.Scanning electron microscopy(SEM)was used to observe the microstructure of the coatings,meanwhile,energy dispersive spectrometry(EDS)and X-ray diffraction(XRD)were separately used to investigate the elemental as well as phase compositions of the coatings.The anti-corrosion property of the coatings was evaluated by potentiodynamic polarization curves as well as electrochemical impedance spectroscopy(EIS).The results show that PEC process is closely related with the effects of adsorption as well as diffusion of the activated carbon atoms,and it can provide a favorable pretreatment surface with predesigned chemical composition to obtain a new kind of phase,namely Si C with superior corrosion resistance and chemical stability,in the following PEC+MAO hybrid coatings.Meanwhile,PEC preprocessing also can afford an excellent micro-structure to increase the coating thickness as well as to improve the compactness of the PEC+MAO hybrid coatings.During the fabrication process of the PEC+MAO hybrid coatings,an overlapping phenomenon in regard to coating thickness can be observed instead of heaping up layer by layer.Compared with both single PEC surface modification layers as well as single MAO coatings,the PEC+MAO hybrid coatings exhibit more superior anti-corrosion property.Especially,the EIS data reveal that the PEC+MAO hybrid coatings can act as an effective protection system to provide relatively excellent long-range anti-corrosion protection.Note also that employing same MAO technique for both single MAO treatment as well as PEC+MAO combining procedure is the key to this research.

Corrosion Resistance of AZ91 Magnesium Alloy after Laser Remelting Treatment

The main objective of the study was the modification of the surface layer of magnesium alloy by the COlaser. The studied material was the commercial AZ91 magnesium alloy. The effectiveness of the alternations caused by the remelting process was verified on the basis of microscopic observation and corrosion investigations, i e, recording of potentiodynamic polarization curves, electrochemical noise measurements and hydrogen evolution rate measurements. For the adopted range of the treatment parameters, favourable changes were observed in the surface layer such as the refinement of structure and more uniform arrangement of individual phases. As a consequence of those favourable structural changes the improvement of the corrosion resistance of the alloy was achieved in comparison to its non-remelted equivalent. For the treated material corrosion rates expressed as corrosion current densities were at least three times lower than the appropriate values for the untreated alloy comparing them for the same period of samples immersion in the test solution. The obtained results have confirmed the effectiveness of the applied surface treatment resulting in favourable changes in the structure and corrosion properties of the AZ91 magnesium alloy.