In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of...In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of ZK60 Mg alloy after single MPO and HCPEB＋MPO compounded treatment were investigated by SEM. The results showed that the density of the ceramic layer of HCPEB＋MPO-treated ZK60 Mg alloy was improved and defects were reduced compared to that under MPO treatment alone. Surface modified layer of ZK60 Mg alloys treated by HCPEB＋MPO was divided into three zones, namely the top loose ceramic zone, middle compact zone and inside HCPEB-induced melted zone. Corrosion resistance of ZK60 Mg alloy before and after the compounded surface modification was measured in a solution of 3.5% NaCl by potentiodynamic polarization curves. It was found that the corrosion current density of ZK60 Mg alloys could be reduced by about three orders of magnitude, from 311μA/cm^2 of the original sample to 0.2μA/cm^2 of the HCPEB＋MPO-treated sample. This indicates the great application potential of the HCPEB＋MPO compounded surface modification technology in improving the corrosion resistance of ZK60 Mg alloys in the future.展开更多
Mciro-arc oxidation（MAO）was used to coat porous films on the surface of a Zr-based bulk metallic glass sample.The compressive test results indicated that,compared with the as-cast sample,the MAO treated one exhibite...Mciro-arc oxidation（MAO）was used to coat porous films on the surface of a Zr-based bulk metallic glass sample.The compressive test results indicated that,compared with the as-cast sample,the MAO treated one exhibited higher deformation capacity,associated with multiple shear bands with higher density on the side surface and well-developed vein patterns with smaller size on the fractured surface.The pore in the MAOed film and the matrix/coating interface initiated the shear bands and impeded the rapid propagation of shear bands,thus favoring the enhanced plasticity of the MAO treated sample.The obtained results demonstrated that MAO can be considered as an effective method to finely tune the mechanical performance of monolithic bulk metallic glasses.展开更多
基金supported by Liaoning BaiQianWan Talents Program of China (No. 2008921028)Doctoral Fund of Ministry of Education of China (No. 200801451082)
文摘In this study, compounded surface modification technology-high current pulsed electron beam （HCPEB） ＋ micro-plasma oxidation （MPO） was applied to treat ZK60 Mg alloys. The characteristics of the microstructure of ZK60 Mg alloy after single MPO and HCPEB＋MPO compounded treatment were investigated by SEM. The results showed that the density of the ceramic layer of HCPEB＋MPO-treated ZK60 Mg alloy was improved and defects were reduced compared to that under MPO treatment alone. Surface modified layer of ZK60 Mg alloys treated by HCPEB＋MPO was divided into three zones, namely the top loose ceramic zone, middle compact zone and inside HCPEB-induced melted zone. Corrosion resistance of ZK60 Mg alloy before and after the compounded surface modification was measured in a solution of 3.5% NaCl by potentiodynamic polarization curves. It was found that the corrosion current density of ZK60 Mg alloys could be reduced by about three orders of magnitude, from 311μA/cm^2 of the original sample to 0.2μA/cm^2 of the HCPEB＋MPO-treated sample. This indicates the great application potential of the HCPEB＋MPO compounded surface modification technology in improving the corrosion resistance of ZK60 Mg alloys in the future.
基金the financial support from the National Natural Science Foundation of China(Grant Nos.51371065,51671070,51671067,51671071)the Opening Funding of AWJ-16-Z02 in the State Key Laboratory of Advanced Welding and Joining,China
文摘Mciro-arc oxidation（MAO）was used to coat porous films on the surface of a Zr-based bulk metallic glass sample.The compressive test results indicated that,compared with the as-cast sample,the MAO treated one exhibited higher deformation capacity,associated with multiple shear bands with higher density on the side surface and well-developed vein patterns with smaller size on the fractured surface.The pore in the MAOed film and the matrix/coating interface initiated the shear bands and impeded the rapid propagation of shear bands,thus favoring the enhanced plasticity of the MAO treated sample.The obtained results demonstrated that MAO can be considered as an effective method to finely tune the mechanical performance of monolithic bulk metallic glasses.