An effective method was proposed to establish the continuous cooling transformation（CCT） diagrams of aluminum alloys using in situ voltage measurement.The voltage change of samples with predefined dimension was reco...An effective method was proposed to establish the continuous cooling transformation（CCT） diagrams of aluminum alloys using in situ voltage measurement.The voltage change of samples with predefined dimension was recorded under the constant current state during continuous cooling.Solutionizing time,together with starting and finishing temperatures of phase transformation of the alloy can be obtained from relationships of voltage vs time and temperature.A critical cooling rate without detectable phase transition during continuous cooling can be determined.Continuous cooling transformation diagrams of tested samples can be established conveniently based on these results.Microstructure observation and differential scanning calorimetry（DSC） testing were applied to verify the reliability of continuous cooling transformation diagram.展开更多
采用DIL805L型膨胀仪研究了弹簧钢52Cr Mo V4连续冷却相变组织变化规律,分析了合金元素和冷却速度对CCT曲线、相变组织和显微硬度的影响。结果表明:Cr、Mo、V、Mn等元素的加入使得弹簧钢52Cr Mo V4珠光体和贝氏体转变曲线完全分离,可以...采用DIL805L型膨胀仪研究了弹簧钢52Cr Mo V4连续冷却相变组织变化规律,分析了合金元素和冷却速度对CCT曲线、相变组织和显微硬度的影响。结果表明:Cr、Mo、V、Mn等元素的加入使得弹簧钢52Cr Mo V4珠光体和贝氏体转变曲线完全分离,可以在较宽的冷却速度范围内得到马氏体+贝氏体组织,当冷却速度大于等于5℃/s时,连续冷却转变获得单一的马氏体组织。冷却速度增加,促使了连续冷却转变后的组织细化,显微硬度增大。展开更多
文摘An effective method was proposed to establish the continuous cooling transformation（CCT） diagrams of aluminum alloys using in situ voltage measurement.The voltage change of samples with predefined dimension was recorded under the constant current state during continuous cooling.Solutionizing time,together with starting and finishing temperatures of phase transformation of the alloy can be obtained from relationships of voltage vs time and temperature.A critical cooling rate without detectable phase transition during continuous cooling can be determined.Continuous cooling transformation diagrams of tested samples can be established conveniently based on these results.Microstructure observation and differential scanning calorimetry（DSC） testing were applied to verify the reliability of continuous cooling transformation diagram.
文摘采用DIL805L型膨胀仪研究了弹簧钢52Cr Mo V4连续冷却相变组织变化规律,分析了合金元素和冷却速度对CCT曲线、相变组织和显微硬度的影响。结果表明:Cr、Mo、V、Mn等元素的加入使得弹簧钢52Cr Mo V4珠光体和贝氏体转变曲线完全分离,可以在较宽的冷却速度范围内得到马氏体+贝氏体组织,当冷却速度大于等于5℃/s时,连续冷却转变获得单一的马氏体组织。冷却速度增加,促使了连续冷却转变后的组织细化,显微硬度增大。