4,4-Dialkyl-2-oxazolin-5-ones are prepared by one step reaction of 2-oxazolin-5-one with the magnesium methyl carbonate(MMC)and alkyIhalides.It is a novel and convenient method for synthesis of α, Υ-disubstitutcd α...4,4-Dialkyl-2-oxazolin-5-ones are prepared by one step reaction of 2-oxazolin-5-one with the magnesium methyl carbonate(MMC)and alkyIhalides.It is a novel and convenient method for synthesis of α, Υ-disubstitutcd α-amino acid by hydrolysis of 4,4-dialkyl-2-oxazolin-5-ones.展开更多
The magnesia -hercynite bricks offer a new lining to rotary cement kiln. They are well adopted and widely used in the high temperature zone of cement kiln, and have obtained good performance at rigorous and severe wor...The magnesia -hercynite bricks offer a new lining to rotary cement kiln. They are well adopted and widely used in the high temperature zone of cement kiln, and have obtained good performance at rigorous and severe working conditions. The synthesis of hercynite requires a suitable atmosphere with proper O2 partial pressures which makes sure FeO can stably exist at the synthesizing temperature. Current industrial production of hercynite mainly adopts fused method. The other method, sinte- ring method, is not mature and needs further research. The magnesia - hercynite brick shows high hot toughhess, high adhesion strength to kiln crust, and good corrosion resistance to alkali salt in cement kilns. The mismatching of thermal expansion between magnesia and hercynite can improve the thermal shock resistance of the bricks, but the oxidation of partial Fe^2＋ , the high temperature solution, and low temperature exsolution of transgranular secondary spinel lead to cubical expansion, .formation of more cracks, and poor thermal shock resistance of the bricks.展开更多
Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases co...Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases corresponding to ZnS nanoparticles, PVA and PANI. Field emission scanning electron microscopy shows the formation of agglomerated PANI along the PVA backbone, within which the ZnS nanoparticles are dispersed.UV-visible spectroscopy is conducted to measure the transmittance spectra of samples revealing the electronic absorption characteristics of ZnS and PANI nanoparticles. Photo-acoustic（PA） setup is installed to investigate the thermal properties of samples. The PA spectroscopy indicates a high value of thermal diffusivity for samples due to the presence of ZnS and PANI nanoparticles. Moreover, at higher doses, the more polymerization and formation of PANI and ZnS nanoparticles result in enhancement of thermal diffusivity.展开更多
文摘4,4-Dialkyl-2-oxazolin-5-ones are prepared by one step reaction of 2-oxazolin-5-one with the magnesium methyl carbonate(MMC)and alkyIhalides.It is a novel and convenient method for synthesis of α, Υ-disubstitutcd α-amino acid by hydrolysis of 4,4-dialkyl-2-oxazolin-5-ones.
文摘The magnesia -hercynite bricks offer a new lining to rotary cement kiln. They are well adopted and widely used in the high temperature zone of cement kiln, and have obtained good performance at rigorous and severe working conditions. The synthesis of hercynite requires a suitable atmosphere with proper O2 partial pressures which makes sure FeO can stably exist at the synthesizing temperature. Current industrial production of hercynite mainly adopts fused method. The other method, sinte- ring method, is not mature and needs further research. The magnesia - hercynite brick shows high hot toughhess, high adhesion strength to kiln crust, and good corrosion resistance to alkali salt in cement kilns. The mismatching of thermal expansion between magnesia and hercynite can improve the thermal shock resistance of the bricks, but the oxidation of partial Fe^2＋ , the high temperature solution, and low temperature exsolution of transgranular secondary spinel lead to cubical expansion, .formation of more cracks, and poor thermal shock resistance of the bricks.
文摘Gamma irradiation is employed for in situ preparation of PVA-PANI-ZnS nanocomposite. The irradiation dose is varied from 10 to 40 kGy at 10 kGy intervals. The XRD result confirms the formation of crystalline phases corresponding to ZnS nanoparticles, PVA and PANI. Field emission scanning electron microscopy shows the formation of agglomerated PANI along the PVA backbone, within which the ZnS nanoparticles are dispersed.UV-visible spectroscopy is conducted to measure the transmittance spectra of samples revealing the electronic absorption characteristics of ZnS and PANI nanoparticles. Photo-acoustic（PA） setup is installed to investigate the thermal properties of samples. The PA spectroscopy indicates a high value of thermal diffusivity for samples due to the presence of ZnS and PANI nanoparticles. Moreover, at higher doses, the more polymerization and formation of PANI and ZnS nanoparticles result in enhancement of thermal diffusivity.