The preparation technics of glass-ceramics with super low coefficient of thermal expansion containing β-quartz solid solution as a main crystal phase based on the glass in the system Li2O-Al2O3-SiO2 was introduced. T...The preparation technics of glass-ceramics with super low coefficient of thermal expansion containing β-quartz solid solution as a main crystal phase based on the glass in the system Li2O-Al2O3-SiO2 was introduced. The composition of base glass, technics of melting and heat treatment effecting on characteristic of glass-ceramics was described. Specimens were prepared by melting, anneal and controlled two steps heat treatment. Crystal phase, microstructure and elementary distributing were studied by using XRD, SEM and EDS respectively. Prepared specimens show excellent transparency and super low thermal expansion coefficient of 2×10-8 ·K-1, which reaches international advanced level.展开更多
The Li_(2)O-Al_(2)O_(3)-SiO_(2) (LAS) glass-ceramics with low lithium content were prepared from spodumene mineral by melting method.XRD,DSC,and FTIR were used to study the crystallization process and structure of the...The Li_(2)O-Al_(2)O_(3)-SiO_(2) (LAS) glass-ceramics with low lithium content were prepared from spodumene mineral by melting method.XRD,DSC,and FTIR were used to study the crystallization process and structure of the samples.The results showed that the addition of Na_(2)O promoted the precipitation of β-quartz solid solution and its transformation to β-spodumene solid solution.Mechanical performance tests and FESEM indicated that the larger grain size and inhomogeneous grain dispersion caused by the increase of Na_(2)O content led to lower mechanical properties.In addition,low expansion glass-ceramics were prepared by an appropriate heat treatment according to DSC result,and when Na_(2)O content was in the range of 1.22 wt% to 2.41 wt%,the average coefficient of thermal expansion (CTE) (30-300 ℃) increased from-5.810 ×10^(-7 )to 5.322×10^(-7)℃^(-1).展开更多
文摘The preparation technics of glass-ceramics with super low coefficient of thermal expansion containing β-quartz solid solution as a main crystal phase based on the glass in the system Li2O-Al2O3-SiO2 was introduced. The composition of base glass, technics of melting and heat treatment effecting on characteristic of glass-ceramics was described. Specimens were prepared by melting, anneal and controlled two steps heat treatment. Crystal phase, microstructure and elementary distributing were studied by using XRD, SEM and EDS respectively. Prepared specimens show excellent transparency and super low thermal expansion coefficient of 2×10-8 ·K-1, which reaches international advanced level.
基金Funded by Research Fund of Center for Materials Research and Analysis,Wuhan University of Technology (No.2018KFJJ11)。
文摘The Li_(2)O-Al_(2)O_(3)-SiO_(2) (LAS) glass-ceramics with low lithium content were prepared from spodumene mineral by melting method.XRD,DSC,and FTIR were used to study the crystallization process and structure of the samples.The results showed that the addition of Na_(2)O promoted the precipitation of β-quartz solid solution and its transformation to β-spodumene solid solution.Mechanical performance tests and FESEM indicated that the larger grain size and inhomogeneous grain dispersion caused by the increase of Na_(2)O content led to lower mechanical properties.In addition,low expansion glass-ceramics were prepared by an appropriate heat treatment according to DSC result,and when Na_(2)O content was in the range of 1.22 wt% to 2.41 wt%,the average coefficient of thermal expansion (CTE) (30-300 ℃) increased from-5.810 ×10^(-7 )to 5.322×10^(-7)℃^(-1).