Low temperature cracking behavior of asphalt binders and mixtures: A review

Low temperature cracking(LTC)distress on pavement seriously affects road life.This paper finished a literature review of the research on the mechanism of LTC of asphalt composites(asphalt composites refers to asphalt binder and asphalt mixture in this article),test methods,factors contributing to LTC,measures to prevent and control the distress,and prediction of LTC in asphalt pavements.The following conclusions were obtained:the cracking mechanism of asphalt mixtures needs to be further revealed by means of simulation at the micro level,the BBR and 4 mm plate test(by DSR)methods are currently optimal,and a correlation between asphalt and asphalt mixture evaluation indexes needs to be established.Sensitivity analyses are needed for the factors affecting LTC of asphalt mixtures.It is necessary to calculate the contribution of each factor to the LTC of asphalt mixtures.The aim is to propose targeted improvement measures for the most unfavourable factors,as well as to carry out research and development of key materials for anti-cracking.Measures for the prevention and control of LTC of asphalt pavement are analyzed and discussed.Existing researches on the prediction of LTC of asphalt pavements is discussed.It is necessary to analyse the mechanical response of asphalt pavement,the damage process and the sensitivity of anti-cracking parameters on the basis of considering the complex geometrical characteristics and material properties of asphalt pavement materials.Finally,the mechanism of LTC,evaluation methods,factors influencing LTC,and remedial measures for asphalt composites were summarized,and future research prospects were suggested.This paper provides theoretical support for the further solution of LTC distress of asphalt pavement,which is effective on the improvement of pavement life.

Construction Technical Temperature Cracking for a and Control of Concrete Plate Type Raft Foundation

The mass fiat raft foundation Section is large and Cement is in large quantities, the temperature changes in the larger cement hydration heat of the water releasing, the temperature stress is main reason reducing cracking. According to the basement of a project of Guangzhou large slab raft foundation engineering as an example, Discussing the construction technology measures of early crack of large volume concrete of raft plate in the process of construction,. The results show that it Can effectively prevents the slab foundation structure cracking and achieves good results through controlling Concrete materials and concrete temperature Parameter such as the lifting machine temperature and the pouring temperature and the expansion joint or the whole pouring length.

Extraction of the key infrared radiation temperature features concerning stress and crack evolution of loaded rocks

The infrared radiation temperature(IRT)variation concerning stress and crack evolution of rocks is a critical focus in rock mechanics domain and engineering disaster warning.In this paper,a methodology to extract the key IRT features related to stress and crack evolution of loaded rocks is proposed.Specifically,the wavelet denoising and reconstruction in thermal image sequence(WDRTIS)method is employed to eliminate temporal noise in thermal image sequences.Subsequently,the adaptive partition temperature drift correction(APTDC)method is introduced to alleviate temperature drift.On this basis,the spatial noise correction method based on threshold segmentation and adaptive median filtering(OTSU-AMF)is proposed to extract the key IRT features associated with microcracks of loaded rocks.Following temperature drift correction,IRT provides an estimation of the thermoelastic factor in rocks,typically around 5.29×10^(-5) MPa^(-1) for sandstones.Results reveal that the high-temperature concentrated region in cumulative thermal images of crack evolution(TICE)can elucidate the spatiotemporal evolution of localized damage.Additionally,heat dissipation of crack evolution(HDCE)acquired from TICE quantifies the progressive failure process of rocks.The proposed methodology enhances the reliability of IRT monitoring results and provides an innovative approach for conducting research in rock mechanics and monitoring engineering disasters.

Novel Methodologies for Preventing Crack Propagation in Steel Gas Pipelines Considering the Temperature Effect

Using the software ANSYS-19.2/Explicit Dynamics,this study performedfinite-element modeling of the large-diameter steel pipeline cross-section for the Beineu-Bozoy-Shymkent gas pipeline with a non-through straight crack,strengthened by steel wire wrapping.The effects of the thread tensile force of the steel winding in the form of single rings at the crack edges and the wires with different winding diameters and pitches were also studied.The results showed that the strengthening was preferably executed at a minimum value of the thread tensile force,which was 6.4%more effective than that at its maximum value.The analysis of the influence of the winding dia-meters showed that the equivalent stresses increased by 32%from the beginning of the crack growth until the wire broke.The increment in winding diameter decelerated the disclosure of the edge crack and reduced its length by 8.2%.The analysis of the influence of the winding pitch showed that decreasing the distance between the winding turns also led to a 33.6%reduction in the length of the straight crack and a 7.9%reduction in the maximum stres-ses on the strengthened pipeline cross-section.The analysis of the temperature effect on the pipeline material,within a range from-40℃ to+50℃,resulted in a crack length change of up to 5.8%.As the temperature dropped,the crack length decreased.Within such a temperature range,the maximum stresses were observed along the cen-tral area of the crack,which were equal to 413 MPa at+50℃ and 440 MPa at-40℃.The results also showed that the presence of the steel winding in the pipeline significantly reduced the length of crack propagation up to 8.4 times,depending on the temperature effect and design parameters of prestressing.This work integrated the existing methods for crack localization along steel gas pipelines.

Simulation-Based Investigation of Crack Formation in Forged MB15 Magnesium Alloy

In the process of riveting an MB15 forging die,cracks were discovered emerging along the longitudinal direction and near the riveting hole.Through fracture analysis,microscopic observation,energy spectrum analysis,metallographic examination,and hardness test,the properties and causes of the cracks are discussed.The results indicate that the cracking type is intergranular brittle cracking,occurring during the forging stage.Furthermore,the recrystallization at the crack site is found to be incomplete,which is attributed to the low deformation temperature.

Fatigue crack propagation in fine-grained magnesium under low temperature tension-tension cyclic loading

Fine-grained magnesium was tested under stress-controlled tension-tension cyclic loading at -30 ℃ and the tested sample was observed using scanning electron microscope and electron backscatter diffraction to explore the fatigue behavior and crack propagation. The fatigue data showed that the material experienced cyclic softening followed by cyclic hardening before the final fracture failure. The microscopic observations demonstrated that the cracks were almost perpendicular to the loading direction with some zigzags and the cracks progressed along both small angle grain boundaries and large angle grain boundaries. Although the cracks were mainly propagated along large angle grain boundaries, the value of grain boundary angle was not the primary factor to determine the crack propagation direction. The local residual strain from the rolling process was released due to the crack propagation and there was more strain relaxation at regions closer to the cracks.

Stability analysis of the temperature cracks in Xiaowan arch dam

In the Xiaowan arch dam there are massive temperature cracks nearly parallel to the dam axis. Obviously, whether the cracks may spread or not during the water storage process is one of the crucial factors for the safety of a dam. In this paper, a new type of crack element, in which the contact component is implicitly included into the concrete component, is proposed to simulate the effects of the existing cracks. The crack element is proved by numerical example to share the merits of both conventional contact elements and joint elements. With a finite element model of the cracked arch dam together with its rock foundation established, the transient displacement and stress fields of the dam are obtained. The complicated rock foundation, the construction process of the arch dam, the massive cracks, the transient temperature field, as well as the water storage process have been taken into consideration in the simulation. In addition to the global model, several sub-models for typical crack tips are also generated with finer elements placed around the tips. Thus, more accurate displacement and stress distribution are obtained by simultaneous sub-model simulation. Based on the calculation of stress intensity factor for crack tips by extension method, the temperature cracks in the Xiaowan arch dam are finally proved to be stable.

Continuous-discontinuous element method for three-dimensional thermal cracking of rocks

Thermal cracking of rocks can significantly affect the durability of underground structures in engineering practices such as geothermal energy extraction,storage of nuclear waste and tunnelling in freezeethaw cycle induced areas.It is a scenario of strong coupled thermomechanical process involving discontinuity behaviours of rocks.In this context,a numerical model was proposed to investigate the thermal cracking of rocks,in a framework of the continuous-discontinuous element method(CDEM)for efficiently capturing the initiation and propagation of multiple cracks.A simplex integration strategy was adopted to account for the influences of temperature-dependent material properties.Several benchmark tests were considered and the obtained results were compared with analytical solutions and numerical results from the literature.The results show that the fracture degree of the cases when considering temperature-dependent material parameters had 10%differences approximately compared with the cases with constant parameters.

NUMERICAL SIMULATION OF TEMPERATURE FIELDS FOR WELD METAL SOLIDIFICATION CRACKING IN STAINLESS STEELS

This paper has analyzed the influences of the heat input of welding arc, the latent heat of solidifica- tion,fluid flow of liquid metal on the heat conductivity pertaining to welding solidification crack of stainless steels. As a result,two - dimensional heat conduction models with prescribed heat flux mov- ing along the the have been developed that can simulate welding arc, convection and radiation heat loss from top and bottom surfaces of the workpiece. Finally, the finite element model was used to ana- lyze and calculate the temperature field.

Effects of Calcination Temperature on the Acidity and Catalytic Performances of HZSM-5 Zeolite Catalysts for the Catalytic Cracking of n-Butane

The acidic modulations of a series of HZSM-5 catalysts were successfully made by calcination at different treatment temperatures, i.e. 500, 600, 650, 700 and 800 ℃, respectively. The results indicated that the total acid amounts, their density and the amount of B-type acid of HZSM-5 catalysts rapidly decreased, while the amounts of L-type acid had almost no change and thus the ratio of L/B was obviously enhanced with the increase of calcination temperature （excluding 800 ℃）. The catalytic performances of modified HZSM-5 catalysts for the cracking of n-butane were also investigated. The main properties of these catalysts were characterized by means of XRD, N2 adsorption at low temperature, NH3-TPD, FTIR of pyridine adsorption and BET surface area measurements. The results showed that HZSM-5 zeolite pretreated at 800 ℃ had very low catalytic activity for n-butane cracking. In the calcination temperature range of 500-700 ℃, the total selectivity to olefins, propylene and butene were increased with the increase of calcination temperature, while, the selectivity for arene decreased with the calcination temperature. The HZSM-5 zeolite calcined at 700 ℃ produced light olefins with high yield, at the reaction temperature of 650 ℃ the yields of total olefins and ethylene were 52.8% and 29.4%, respectively. Besides, the more important role is that high calcination temperature treatment improved the duration stability of HZSM-5 zeolites. The effect of calcination temperature on the physico-chemical properties and catalytic performance of HZSM-5 for cracking of n-butane was explored. It was found that the calcination temperature had large effects on the surface area, crystallinity and acid properties of HZSM-5 catalyst, which further affected the catalytic performance for n-butane cracking.

Temperature control and cracking prevention in coastal thin-wall concrete structures

A three-dimensional finite element program for thermal analysis of hydration heat in concrete structures with a plastic pipe cooling system is introduced in this paper. The program was applied to simulation of the temperature and stress field of the Cao＇e Sluice during the construction period. From the calculated results, we can find that the temperaiure and stress of concrete cooled with plastic pipes are much lower than those of concrete without pipes. Moreover, plastic pipes could not be corroded by seawater. That is to say, a good effect of temperature control and cracking prevention can be achieved, which provides a useful reference for other similar nearshore concrete projects.

Temperature field at time of pulse current discharge in metal structure with elliptical embedding crack

Theoretical analysis is made on the temperature field at the time of pulse current discharge in a metal structure with an elliptical embedding crack. In finding the temperature field, analogy between the current flow through an elliptical embedding crack and the fluid flow through a barrier is made based on the similarity principle. Boundary conditions derived from this theory are introduced so that the distribution of current density and the temperature field expressions can be obtained. The study provides a theoretic basis to the applications of stopping spatial crack with electromagnetic heating.

Fatigue small crack growth threshold determination of a high-Nb TiAl alloy at different temperatures by in-situ observation

The purpose of this paper is to estimate the fatigue crack growth threshold of a high-Nb TiAl alloy at the different temperatures based on scanning electron microscopy （SEM） in-situ observation. The results indicated that the fatigue crack growth threshold △Kth of a nearly lamellar high-Nb TiAl alloy with 8% Nb content at room temperature and 750℃ was determined as 12.89 MPa.m^1/2 and 8.69 MPa.m^1/2, respectively. The effect of the elevated temperature on the fatigue crack growth threshold cannot be ignored. At the same time, the early stage of fatigue crack propagation exhibited multicrack initiation and bridge-link behavior.

Outlet Temperature Correlation and Prediction of Transfer Line Exchanger in an Industrial Steam Ethylene Cracking Process

Predicting the best shutdown time of a steam ethylene cracking furnace in industrial practice remains a challenge due to the complex coking process. As well known, the shutdown time of a furnace is mainly determined by coking condition of the transfer line exchangers （TLE） when naphtha or other heavy hydrocarbon feedstocks are cracked. In practice, it is difficult to measure the coke thickness in TLE through experimental method in the complex industrial situation. However, the outlet temperature of TLE （TLEOT） can indirectly characterize the coking situation in TLE since the coke accumulation in TLE has great influence on TLEOT. Thus, the TLEOT could be a critical factor in deciding when to shut down the furnace to decoke. To predict the TLEOT, a paramewic model was proposed in this work, based on theoretical analysis, mathematic reduction, and parameters estimation. The feasibility of the proposed model was further checked through industrial data and good agreements between model prediction and industrial data with maximum deviation 2% were observed.

In-plane shear(ModeⅡ) crack sub-critical propagation of rock at high temperature

In-plane shear crack sub-critical propagation of rock at high temperature was studied by finite element method and shear-box(i.e.compression-shear) test with newly designed electrically conductive adhesive method.Numerical and experimental results show that the normalized shear(Mode Ⅱ) stress intensity factors,K ⅡT/KT0 is decreased as the temperature increases because high temperature can improve stress distribution at crack tip and reduce the Mode Ⅱ stress intensity factor.Microscopic features of fractured surface are of little pits and secondary micro-cracks in the vicinity(1.5-4.0 mm) of the crack tip.The chevron-shape secondary cracks gradually merge in the length of about 4-5 mm and disappear along the direction of crack propagation.Stable shear crack propagation time is increased with the increasing temperature while the stable shear crack propagation rate is decreased with the increasing temperature,since high temperature can increase the shear(Mode Ⅱ) fracture toughness and prevent the crack growth.It is necessary to ensure the ligament of specimen long enough to measure the maximum unstable crack propagation rate of rock.

EFFECIS OF TEMPERATURE AND OVERLOAD RETARDATION ON CORROSION FATIGUE CRACK GROWTH OF HIGH STRENGTH STEEL

The fatigue crack growth rate (CGR) of ultra high strength steel 30CrMnSiNi2A in distilled water at 18,35 and 55℃ were measured.It was confirmed that the temperature is strongly af- fected on the corrosion fatigue CGR of ultra high strength steel.An expression concerning the effects of Δ K and temperature on the CGR was proposed.The fact that the apparent activation energy (36.6 kJ/mol) resulted from regressive analysis of CGR data was similar to the activation energy of hydrogen diffusion in γ-Fe,strongly supporting the theory of hydrogen-assisted crack growth.The overload retardation effect was greatly reduced in cor- rosion fatigue crack growth,especially at lower frequency,e.g.,0.1 Hz.This phenomenon might be due to the increase of the SCC component of CGR after an overload.

Numerical simulation of temperature fields for weld metal solidification cracking in stainless steels

This paper has analyzed the influences of the heat input of the welding arc, the latent heat of solidification, the fluid flow of liquid metal on the heat conductivity pertaining to the welding solidification crack of stainless steels. As a result, two dimensional heat conduction models with the prescribed heat flux moving along the weld have been developed that can simulate welding arc, convection and radiation heat loss from top and bottom surfaces of the workpiece. Finally, the finite element model was used to analyze and calculate the temperature fields.

Fractal Nature of Crack Growth under Different Temperature

We have studied numerically a simple crack growth model in a two-dimensional triangular lattice of bonds and nodes which incorporates the surface of a growing crack bond-breaking probability P-i similar to exp{(-V-i+E(i))phi(T)}, where E(i) is elastic energy stored in the i-th bond. Different energy temperature factors phi(T) are employed during crack formation and propagation process with a uniform dilation strain case and a shear case and with periodic boundary condition in the horizontal direction. Our results show that the patterns of the cracks generated are fractal structure and the effective fractal dimensionalities decrease with the increase of the temperature factor phi(T)(the absolute temperature T decreasing). In the paper we also discuss the relation between the effective fractal dimension D-eff (the radius R(g) of gyration) and the fractal dimensions D (the radius R of circular), and also give their modification values Omega about two kinds of methods in the lattice model.

Surface crack imaging based on delayed temperature difference at symmetric points by laser spot thermography

Laser spot thermography is a novel technique for the detection of surface cracks with a laser to heat sample locally and with an IR camera to record the surface temperature distribution. Common methods to characterize cracks are only suitable for the situation that the laser scanning path is vertical to the crack. But due to the randomness of cracks,when the scanning path is parallel to the crack,surface cracks cannot be detected by these methods. To tackle this problem,a method is presented which is suitable for the situation that the scanning path is parallel to crack. The main idea is to evaluate the crack-caused asymmetries of the surface temperature distribution. The effect of temperature gradient and the maximum scanning interval are analyzed by a 2D simulation. A new crack imaging technique is presented that is based on delayed temperature difference at symmetric points to characterize the crack in the thermal image. Compared well with those obtained by the spatial first derivative method,experimental results are shown to efficiently prove this method.

Effect of sintering temperature and holding time on structure and properties of Li_(1.5)Ga_(0.5)Ti_(1.5)(PO_4)_(3)electrolyte with fast ionic conductivity

Li1.5Ga0.5Ti1.5(PO4)3(LGTP)is recognized as a promising solid electrolyte material for lithium ions.In this work,LGTP solid electrolyte materials were prepared under different process conditions to explore the effects of sintering temperature and holding time on relative density,phase composition,microstructure,bulk conductivity,and total conductivity.In the impedance test under frequency of 1-10~6 Hz,the bulk conductivity of the samples increased with increasing sintering temperature,and the total conductivity first increased and then decreased.SEM results showed that the average grain size in the ceramics was controlled by the sintering temperature,which increased from(0.54±0.01)μm to(1.21±0.01)μm when the temperature changed from 750 to 950°C.The relative density of the ceramics increased and then decreased with increasing temperature as the porosity increased.The holding time had little effect on the grain size growth or sample density,but an extended holding time resulted in crack generation that served to reduce the conductivity of the solid electrolyte.