EFFECTS OF Nb/Ti+ Nb MICRO ALLOYING ON 900℃ TENSILE PROPERTIES OF ALLOYGH652

Theeffectsof Nband Ti+ Nb microalloyingon mechanicalpropertiesand rupturelifeunder900 ℃ tensiletest on alloy GH652 were studied. Among theoriginalalloy GH652 and its Nb/ Ti+ Nb microalloyed alloys, the Ti+ Nb microalloyed alloy exhibited optimum com bined900℃ tensilestrength and plasticity and longer 900℃ 49 MPa prolonged tensile rup turelife as well. The role of refractory alloying elementscould be effectively brought intoplay with highertemperaturesolution treatment. Coordination strengthening of Matrix andgrain boundary wasthekeyfactoroflifetimeextension andthe mobilityof dislocationsinthematrix wasresponsableforthe plasticity ofthe micro alloyedsamples.

Effect of hot isostatic pressure on the microstructure and tensile properties of γ'-strengthened superalloy fabricated through induction-assisted directed energy deposition

The microstructure characteristics and strengthening mechanism of Inconel738LC(IN-738LC) alloy prepared by using induction-assisted directed energy deposition(IDED) were elucidated through the investigation of samples subjected to IDED under 1050℃ preheating with and without hot isostatic pressing(HIP,1190℃,105 MPa,and 3 h).Results show that the as-deposited sample mainly consisted of epitaxial columnar crystals and inhomogeneously distributed γ’ phases in interdendritic and dendritic core regions.After HIP,grain morphology changed negligibly,whereas the size of the γ’ phase became increasingly even.After further heat treatment(HT,1070℃,2 h + 845℃,24 h),the γ’ phase in the as-deposited and HIPed samples presented a bimodal size distribution,whereas that in the as-deposited sample showed a size that remained uneven.The comparison of tensile properties revealed that the tensile strength and uniform elongation of the HIP + HTed sample increased by 5% and 46%,respectively,due to the synergistic deformation of bimodal γ’phases,especially large cubic γ’ phases.Finally,the relationship between phase transformations and plastic deformations in the IDEDed sample was discussed on the basis of generalized stability theory in terms of the trade-off between thermodynamics and kinetics.

Effects of magnesium and copper additions on tensile properties of Al-Si-Cr die casting alloy under as-cast and T5 conditions

Aluminum high pressure die casting(HPDC)technology has evolved in the past decades,enabling stronger and larger one-piece casting with significant part consolidation.It also offers a higher design freedom for more mass-efficient thin-walled body structures.For body structures that require excellent ductility and fracture toughness to be joined with steel sheet via self-piercing riveting(for instance,shock towers and hinge pillars,etc.),a costly T7 heat treatment comprising a solution heat treatment at elevated temperatures(450℃-500℃)followed by an over-ageing heat treatment is needed to optimize microstructure for meeting product requirement.To enable cost-efficient mass production of HPDC body structures,it is important to eliminate the expensive T7 heat treatment without sacrificing mechanical properties.Optimizing die cast alloy chemistry is a potential solution to improve fracture toughness and ductility of the HPDC components.The present study intends to tailor the Mg and Cu additions for a new Al-Si-Cr type die casting alloy(registered as A379 with The Aluminum Association,USA)to achieve the desired tensile properties without using T7 heat treatment.It was found that Cu addition should be avoided,as it is not effective in enhancing strength while degrades tensile ductility.Mg addition is very effective in improving strength and has minor impact on tensile ductility.The investigated Al-Si-Cr alloy with a nominal composition of Al-8.5wt.%Si-0.3wt.%Cr-0.2wt.%Fe shows comparable tensile properties with the T7 treated AlSi10MnMg alloy which is currently used for manufacturing shock towers and hinge pillars.

Multiscale tensegrity model for the tensile properties of DNA nanotubes

DNA nanotubes(DNTs)with user-defined shapes and functionalities have potential applications in many fields.So far,compared with numerous experimental studies,there have been only a handful of models on the mechanical properties of such DNTs.This paper aims at presenting a multiscale model to quantify the correlations among the pre-tension states,tensile properties,encapsulation structures of DNTs,and the surrounding factors.First,by combining a statistical worm-like-chain(WLC)model of single DNA deformation and Parsegian's mesoscopic model of DNA liquid crystal free energy,a multiscale tensegrity model is established,and the pre-tension state of DNTs is characterized theoretically for the first time.Then,by using the minimum potential energy principle,the force-extension curve and tensile rigidity of pre-tension DNTs are predicted.Finally,the effects of the encapsulation structure and surrounding factors on the tensile properties of DNTs are studied.The predictions for the tensile behaviors of DNTs can not only reproduce the existing experimental results,but also reveal that the competition of DNA intrachain and interchain interactions in the encapsulation structures determines the pre-tension states of DNTs and their tensile properties.The changes in the pre-tension states and environmental factors make the monotonic or non-monotonic changes in the tensile properties of DNTs under longitudinal loads.

Improved continuous precipitation kinetics and tensile properties of extruded AZ80 alloy through {10-12} twin formation

This study investigates the effect of{10-12}deformation twins on the continuous precipitation behavior of an extruded Mg-8.0Al-0.5Zn-0.2Mn(AZ80)alloy during aging.The extruded AZ80 alloy is compressed along the transverse direction to introduce{10-12}twins,followed by an aging treatment at 300℃.The extruded material exhibits a twin-free microstructure with low internal strain energy,whereas the pre-twinned material possesses abundant{10-12}twins and has high internal strain energy.The aging results reveal that the peak-aging time of the pre-twinned material(1 h)is one-eighth of that of the extruded material(8 h).Although Mg_(17)Al_(12)continuous precipitates(CPs)are observed in both the peak-aged materials,these CPs are much smaller and more densely distributed in the pre-twinned material despite the significantly shorter aging time.The CPs size in the peak-aged materials increases in the following order:twinned region in the pre-twinned material(0.47μm)<residual matrix region in the pre-twinned material(1.71μm)<matrix region in the extruded material(2.55μm).Moreover,the CPs number density in the twinned region of the pre-twinned material is approximately 11 times higher than that in the matrix region of the extruded material.The peak-aged pre-twinned material exhibits significantly higher tensile strength and ductility than the peak-aged extruded material.These results demonstrate that the formation of{10-12}twins in the extruded AZ80 alloy substantially accelerates the static precipitation of CPs during aging at 300℃and improves the tensile properties of the peak-aged material.

Effect of Curing Age on Tensile Properties of Fly Ash Based Engineered Geopolymer Composites(FA-EGC)by Uniaxial Tensile Test and Ultrasonic Pulse Velocity Method

Tensile properties of fly ash based engineered geopolymer composites(FA-EGC)at different curing ages were studied by uniaxial tensile test and ultrasonic pulse velocity(UPV)methods,which included uniaxial tensile properties,the correlation between ultrasonic pulse velocity and tensile properties,and characteristic parameters of microcracks.The experimental results show that obvious strain hardening behavior can be found in FA-EGC at different curing ages.With the increase of curing age,the tensile strength increases,the tensile strain decreases and the toughness becomes worse.The UPV of FA-EGC increases with curing age,and a strong correlation can be found between tensile strength and UPV.With the increase of curing age,the average crack width of FA-EGC decreases and the total number of cracks increases.This is because the strength of geopolymer increases fast at early age,thus the later strength development of FA-EGC tend to be stable.At the same time,the bond strength between fiber and matrix,and the friction of fiber/matrix interface continue to increase with curing age,thus the bridging effect of fiber is gradually strengthened.In conclusion,the increase of curing age is beneficial to the development of tensile properties of FA-EGC.

Microstructural characterization and mechanical properties of(TiC+TiB)/TA15 composites prepared by an in-situ synthesis method

Titanium matrix composites reinforced with ceramic particles are considered a promising engineering material due to their combination of high specific strength,low density,and high modulus.In this study,the TA15-based composites reinforced with a volume fraction of 10% to 25%(TiB+TiC)were prepared using powder metallurgy and casting technique.Microstructural characterization and phase constitution were examined using optical microscopy(OM),scanning electron microscopy(SEM),and X-ray diffraction(XRD).In addition,the microhardness,room temperature(RT)and high temperature(HT)tensile properties of the composites were evaluated.Results revealed that the reinforcements are distributed uniformly even in the composites with a high volume of TiB and TiC.However,as the volume fraction exceeds 15%,TiB and TiC particles become coarsening and exhibit rod-like and dendritic-like morphology.Microhardness increases gradually from 321.2 HV for the base alloy to a maximum of 473.3 HV as the reinforcement increases to 25vol.%.Tensile test results indicate that a reinforcement volume fraction above 20% is beneficial for enhancing tensile strength and yield strength at high temperatures,but it has an adverse effect on room temperature elongation.Conversely,if the reinforcement volume fraction is below 20%,it can improve high-temperature elongation when the temperature exceeds 600℃.

Effect of slow shot speed on externally solidified crystal,porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy

The effect of slow shot speed on externally solidified crystal(ESC),porosity and tensile property in a newly developed high-pressure die-cast Al-Si alloy was investigated by optical microscopy(OM),scanning electron microscopy(SEM)and laboratory computed tomography(CT).Results showed that the newly developed AlSi9MnMoV alloy exhibited improved mechanical properties when compared to the AlSi10MnMg alloy.The AlSi9MnMoV alloy,which was designed with trace multicomponent additions,displays a notable grain refining effect in comparison to the AlSi10MnMg alloy.Refining elements Ti,Zr,V,Nb,B promote heterogeneous nucleation and reduce the grain size of primaryα-Al.At a lower slow shot speed,the large ESCs are easier to form and gather,developing into the dendrite net and net-shrinkage.With an increase in slow shot speed,the size and number of ESCs and porosities significantly reduce.In addition,the distribution of ESCs is more dispersed and the net-shrinkage disappears.The tensile property is greatly improved by adopting a higher slow shot speed.The ultimate tensile strength is enhanced from 260.31 MPa to 290.31 MPa(increased by 11.52%),and the elongation is enhanced from 3.72%to 6.34%(increased by 70.52%).

Microstructure,interfacial reaction behavior,and mechanical properties of Ti_3AlC_(2)reinforced Al6061 composites

The interfacial reaction behavior of Al and Ti_3AlC_(2)at different pouring temperatures and its effect on the microstructure and mechanical properties of the composites were investigated.The results show that the addition of3.0 wt.%Ti_3AlC_(2)refines the average grain size ofα(Al)in the composite by 50.1%compared to Al6061 alloy.Morphological analyses indicate that an in-situ Al_(3Ti)transition layer of-180 nm in thickness is generated around the edge of Ti_3AlC_(2)at 720℃,forming a well-bonded Al-Al_(3Ti)interface.At this processing temperature,the ultimate tensile strength of A16061-3.0 wt.%Ti_3AlC_(2)composite is 199.2 MPa,an improvement of 41.5%over the Al6061 matrix.Mechanism analyses further elucidate that 720℃is favourable for forming the nano-sized transition layer at the Ti_3AlC_(2)edges.And,the thermal mismatch strengthening plays a dominant role in this state,with a strengthening contribution of about 74.8%.

Effect of heat treatment on microstructure and tensile properties of A356 alloys

Two heat treatments of A356 alloys with combined addition of rare earth and strontium were conducted.T6 treatment is a long time treatment（solution at 535 ℃ for 4 h ＋ aging at 150 ℃ for 15 h）.The other treatment is a short time treatment（solution at 550 ℃ for 2 h ＋ aging at 170 ℃ for 2 h）.The effects of heat treatment on microstructure and tensile properties of the Al-7%Si-0.3%Mg alloys were investigated by optical microscopy,scanning electronic microscopy and tension test.It is found that a 2 h solution at 550 ℃ is sufficient to make homogenization and saturation of magnesium and silicon in α（Al） phase,spheroid of eutectic Si phase.Followed by solution,a 2 h artificial aging at 170 ℃ is almost enough to produce hardening precipitates.Those samples treated with T6 achieve the maximum tensile strength and fracture elongation.With short time treatment（ST）,samples can reach 90% of the maximum yield strength,95% of the maximum strength,and 80% of the maximum elongation.

Microstructure and tensile properties of containerless near-isothermally forged TiAl alloys

Ti-47Al-2Nb-2Cr-0.4（W, Mo） （mole fraction, %） alloy ingot fabricated using vacuum consumable melting was containerless near-isothermally forged, and the high temperature forgeability, microstructure and tensile properties were investigated. The results show that the TiAl ingot exhibits good heat workability during containerless near-isothermally forging process, and there are not evident cracks on the surface of as-forged TiAl pancake with a total deformation degree of 60%. The microstructure of the TiAl ingot appears to be typical nearly-lamellar（NL）, comprising a great amount of lamellar colonies （α2＋γ） and a few equiaxed γ grains. After near-isothermally forging, the as-forged pancake shows primarily fine equiaxed γ grains with an average grain size of 20 μm and some broken lamellar pieces, and some bent lamellas still exist in the hard-deformation zone. Tensile tests at room temperature show that ultimate tensile strength increases from 433 MPa to 573 MPa after forging due to grain refinement effect.

Microstructure and tensile properties of AE42-based magnesium alloys with calcium addition

The as-cast microstructure of AE42 was of typical dendritic and composed of the a matrix and some needle-shaped interphases Al11RE3. A small mount of Ca addition results in significant microstructural refinement and formation of a Al2Ca phase, which showed two kinds of morphologies, lamellar and tiny granular. The former distributes on grain boundaries and the later is within the matrix grains. With the increase of Ca addition the volume fraction of Al-RE compound (Al11RE3) decreases, but Al2Ca increases. Addition of Ca causes a significant increase of yield strength of the alloy both at ambient and elevated temperatures, but a little decrease of the ductility. With calcium addition the ultimate strength decreases at ambient temperature and 150°t, but increases at 175°C and 200°C.

Tensile and wear properties of TiC reinforced 420 stainless steel fabricated by in situ synthesis

TiC particle reinforced 420 stainless steel matrix composites were fabricated, and the microstructure, tensile properties and wear resistance of the composites were studied. The experimental results indicate that the distribution of TiC particles with size of 5 to 10 μm in diameter is uniform if the volume fraction of TiC is lower than 6%. However, slight agglomeration can be observed when the TiC content exceeds 6%. With the increase of TiC content the tensile and yield strength of the composites prepared increases and reaches the maximum when the volume fraction of TiC increases to 5%. Further increase of TiC content causes reductions of yield and tensile strength. The ductility of the composites shows a monotone decrease with the increase of TiC addition. The introduction of TiC into 420 stainless steel results in significant improvement on wear resistance, which reaches a steady level when the volume fraction of TiC increases to 11% and does not show obvious variation if the TiC content is further increased.

Molecular dynamics study on temperature and strain rate dependences of mechanical tensile properties of ultrathin nickel nanowires

Based on the EAM potential, a molecular dynamics study on the tensile properties of ultrathin nickel nanowires in the （100〉 orientation with diameters of 3.94, 4.95 and 5.99 nm was presented at different temperatures and strain rates. The temperature and strain rate dependences of tensile properties were investigated. The simulation results show that the elastic modulus and the yield strength are gradually decreasing with the increase of temperature, while with the increase of the strain rate, the stress--strain curves fluctuate more intensely and the ultrathin nickel nanowires rupture at one smaller and smaller strain. At an ideal temperature of 0.01 K, the yield strength of the nanowires drops rapidly with the increase of strain rate, and at other temperatures the strain rate has a little influence on the elastic modulus and the yield strength. Finally, the effects of size on the tensile properties of ultrathin nickel nanowires were briefly discussed.

Tensile properties and microstructure of Ti14 alloy after semi-solid forging

Tensile properties of a new α＋Ti2Cu alloy after solid forging at 950 °C and semi-solid forging at 1 000 °C and 1 050 °C were investigated over the temperature range of 20-600 °C. The results reveal that high strength and low ductility are obtained in all semi-solid forged alloys. Tensile properties decrease as the semi-solid forging temperature increases, and cleavage fractures are observed after semi-solid forging at 1 050 °C. The variations in tensile properties are attributed to the coarse microstructures obtained in the semi-solid alloys. It is found that the elevated semi-solid temperatures lead to more liquid precipitates along the prior grain boundaries, which increases the peritectic precipitation and formation of Ti2Cu precipitation zones during re-solidification. Recrystallization heat treatment leads to fine microstructure of semi-solid forged alloys, resulting in improvement of tensile properties.

Biaxial tensile properties and elastic constants evaluation of envelope material for airship

This paper presents an experimental study to determine the tensile properties of the envelope fabric Uretek3216L under biaxial cyclic loading.First the biaxial cyclic tests were carefully carried out on the envelope material to obtain the stress-strain data and the corresponding nonlinearity and orthotropy of the material were analyzed. Then for some determination options with different stress ratios the least squares method minimizing the strain terms was used to calculate the elastic constants from the experimental data.Finally the influences of the determination options with different stress ratios and the reciprocal relationship on the elastic constants were discussed.Results show that the orthotropy of the envelope material can be attributed to the unbalanced crimp of their constitutive yarns in warp and weft directions and the elastic constants vary noticeably with the determination options as well as the normalized stress ratios.In real design practice it is more reasonable to use constants determined for specific stress states in particular stress ratios depending on the project＆#39;s needs.Also calculating the structures with two limitative sets of elastic constants instead of using only one set is recommendable in light of the great variety of the constant＆#39;s values.

IMPROVEMENT ON TENSILE PROPERTIES AND CREEP RESISTANCE OF Fe 3Al BASED ALLOYS

Effects of alloying processing on tensile test properties of Fe 3Al based alloys have been studied. Results show that microalloying of cerium is very effective on increasing the room temperature ductility of Fe 3Al based alloys. Surface analysis by XPS demonstrates that cerium addition causes the change in the oxide chemistry and provides rapid passivation of the specimen surface. The high temperature strength and creep resistance of Fe 3Al based alloys can be significantly enhanced by alloying additions of tungsten, niobium or molybdenum, especially when combined additions of tungsten with niobium or molybdenum are used. The additions of tungsten, niobium or molybdenum also result in the significant microstructural refinement and the formation of fine precipitates which are identified as M 6C type carbide in the alloys containing tungsten.

Orientation dependence of transverse tensile properties of nickel-based third generation single crystal superalloy DD9 from 760 to 1100 ℃

At temperatures ranging from 760 to 1100 °C, the tensile properties of a nickel-based third generation single crystal superalloy DD9 with [100],[120] and [110] orientations were studied. The microstructures and fracture surfaces were observed by OM, SEM and TEM. Results show that the tensile strength of [100] specimen is higher than that of [120] and [110] specimens at 760 and 850 °C;while at the temperatures higher than 980 °C, the tensile strength of all specimens has little difference. The fracture mechanisms of [100],[120] and [110] specimens are the same at 760 and 980 °C. At 1100 °C, the fracture surfaces of [100] and [120] specimens are characterized by dimple features;while [110] specimen shows mixed quasi-cleavage and dimple featured fracture surfaces. At 760 °C, obvious superlattice stacking faults (SSFs) are observed only in [100] specimen;while at 1100 °C, the dislocation configurations of all specimens are similar. The difference in the number of potential active slip systems in [100],[120] and [110] specimens during the tensile deformation process is the main reason for the transverse tensile anisotropy.

Microstructures,tensile properties and serrated flow of Al_xCrMnFeCoNi high entropy alloys

Microstructures and mechanical properties of dual-phase AlxCrMnFeCoNi (x=0.4, 0.5, 0.6, at.%) alloys were investigated. Thermomechanical processing leads to a microstructural evolution from cast dendritic structures to equiaxed ones, consisting of face-centered cubic (fcc) and body-centered cubic (bcc) phases in the two states. The volume fraction of bcc phase increases and the size of fcc grain decreases with increasing Al content, resulting in remarkably improved tensile strength. Specifically, the serrated flow occurring at the medium temperatures varies from type A+B to B+C or C as the testing temperature increases. The average serration amplitude of these Al-containing alloys is larger than that of CoCrFeNiMn alloy due to the enhanced pinning effect. The early small strain produces low-density of dislocation arrays and bowed dislocations in fcc grains while the dislocation climb and shearing mechanism dominate inside bcc grains. The cross-slip and kinks of dislocations are frequently observed and high-density-tangled dislocations lead to dislocation cells after plastic deformation with a high strain.

Effect of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg-8Li-3Al-(1,2,3)Sn alloys

The effects of Sn content on microstructure and tensile properties of as-cast and as-extruded Mg-8Li-3Al-(1,2,3)Sn(wt.%)alloys were investigated by X-ray diffractometry(XRD),optical microscopy(OM),scanning electron microscopy(SEM)and tensile test.It is found that,as-cast Mg-8Li-3Al-(1,2,3)Sn alloys consist ofα-Mg+β-Li duplex matrix,MgLiAl2 and Li2Mg Sn phases.Increasing Sn content leads to grain refinement ofα-Mg dendrites and increase in content of Li2MgSn phase.During hot extrusion,complete dynamic recrystallization(DRX)takes place inβ-Li phase while incomplete DRX takes place inα-Mg phase.As Sn content is increased,the volume fraction of DRXedα-Mg grains is increased and the average grain size of DRXedα-Mg grains is decreased.Increasing Sn content is beneficial to strength but harmful to ductility for as-cast Mg-8Li-3Al-(1,2,3)Sn alloys.Tensile properties of Mg-8Li-3Al-(1,2,3)Sn alloys are improved significantly via hot extrusion and Mg-8Li-3Al-2Sn alloy exhibits the best tensile properties.