The mechanical and damage properties of single fibres used in fibrous composite have gained tremendous importance in recent years. These properties are used in determination of effective properties of composites by mi...The mechanical and damage properties of single fibres used in fibrous composite have gained tremendous importance in recent years. These properties are used in determination of effective properties of composites by micromechanics. These are also used in the micromechanical damage modeling. Further, these properties are used as an indicator of the excellence of product by manufacturers. In the present study the axial tensile modulus, ultimate strength and failure strain of single fibres are determined for carbon and glass fibres. ASTM D3379-75 standard is followed and a number of fibers are tested for statistical analysis. The axial tensile moduli measured are 246.7 GPa and 93.3 GPa, respectively and strength are 3031.6 MPa and 2035.9 MPa, respectively for carbon and glass fibres. Further, the respective axial tensile failure strains are 0.0137 and 0.0224. The error in the measurement of axial modulus is below 8% while for axial tensile strength is below 1%.展开更多
To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress—true strain curves of three kinds of aluminum alloy sheets for loading ratios of 4:1, 4:2, 4:3, 4:4, 3...To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress—true strain curves of three kinds of aluminum alloy sheets for loading ratios of 4:1, 4:2, 4:3, 4:4, 3:4, 2:4 and 1:4 were obtained by conducting biaxial tensile test in the established testing systems. It shows that the loading path has a significant influence on the stress—strain curves and as the loading ratio increases from 4:1 to 4:4, the stress—strain curve becomes higher and n-value becomes larger. Experimental yield points for three aluminum alloy sheets from 0.2% to 2% plastic strain were determined based on the equivalent plastic work. And the geometry of the experimental yield loci were compared with the yield loci calculated from several existing yield criteria. The analytical result shows that the Barlat89 and Hosford yield criterion describe the general trends of the experimental yield loci of aluminum alloy sheets well, whereas the Mises yield criterion overestimates the yield stress in all the contours.展开更多
The dynamic tensile test of 0.11C-0.62Si-1.65Mn TRIP steel was carried out at different strain rates and test temperatures. The results show that both temperature and strain rate affect the retained austenite transfor...The dynamic tensile test of 0.11C-0.62Si-1.65Mn TRIP steel was carried out at different strain rates and test temperatures. The results show that both temperature and strain rate affect the retained austenite transformation. At high strain rates, the uniform elongation decreases, whereas the total elongation and energy absorption increase. The tensile strength is less strain rate sensitive. With raising test temperature, the tensile strength is reduced and the mechanical properties generally deteriorate, especially at 110℃,However, excellent mechanical properties were obtained at 50℃ and 75℃.展开更多
文摘The mechanical and damage properties of single fibres used in fibrous composite have gained tremendous importance in recent years. These properties are used in determination of effective properties of composites by micromechanics. These are also used in the micromechanical damage modeling. Further, these properties are used as an indicator of the excellence of product by manufacturers. In the present study the axial tensile modulus, ultimate strength and failure strain of single fibres are determined for carbon and glass fibres. ASTM D3379-75 standard is followed and a number of fibers are tested for statistical analysis. The axial tensile moduli measured are 246.7 GPa and 93.3 GPa, respectively and strength are 3031.6 MPa and 2035.9 MPa, respectively for carbon and glass fibres. Further, the respective axial tensile failure strains are 0.0137 and 0.0224. The error in the measurement of axial modulus is below 8% while for axial tensile strength is below 1%.
基金Project (50475004) supported by the National Natural Science Foundation of ChinaProject (05-2) supported by the Foundation of the State Key Laboratory of Plastic Forming Simulation and Die & Mould Technology of HUSTProject (2004036197) supported by the Postdoctoral Science Foundation of China
文摘To carry out biaxial tensile test in sheet metal, the biaxial tensile testing system was established. True stress—true strain curves of three kinds of aluminum alloy sheets for loading ratios of 4:1, 4:2, 4:3, 4:4, 3:4, 2:4 and 1:4 were obtained by conducting biaxial tensile test in the established testing systems. It shows that the loading path has a significant influence on the stress—strain curves and as the loading ratio increases from 4:1 to 4:4, the stress—strain curve becomes higher and n-value becomes larger. Experimental yield points for three aluminum alloy sheets from 0.2% to 2% plastic strain were determined based on the equivalent plastic work. And the geometry of the experimental yield loci were compared with the yield loci calculated from several existing yield criteria. The analytical result shows that the Barlat89 and Hosford yield criterion describe the general trends of the experimental yield loci of aluminum alloy sheets well, whereas the Mises yield criterion overestimates the yield stress in all the contours.
基金Item Sponsored by China-Belgium Bilateral Project BIL01
文摘The dynamic tensile test of 0.11C-0.62Si-1.65Mn TRIP steel was carried out at different strain rates and test temperatures. The results show that both temperature and strain rate affect the retained austenite transformation. At high strain rates, the uniform elongation decreases, whereas the total elongation and energy absorption increase. The tensile strength is less strain rate sensitive. With raising test temperature, the tensile strength is reduced and the mechanical properties generally deteriorate, especially at 110℃,However, excellent mechanical properties were obtained at 50℃ and 75℃.