Starch/polyvinyl alcohol （PVA） blended materials for using as a solid carbon source （SCS） were prepared by blending PVA and gelatinized starch in an aqueous solution system, in which PVA served as framework materi...Starch/polyvinyl alcohol （PVA） blended materials for using as a solid carbon source （SCS） were prepared by blending PVA and gelatinized starch in an aqueous solution system, in which PVA served as framework material and starch as carbon source. The optimization of starch content and temperature effects were investigated. It was indicated that higher denitrification efficiency could be achieved with more starch in the materials. The average specific denitrification rates were 0.93, 0.66, 0.37 and 0.36 mg/（g·day） corresponding to starch content of 70%, 60%, 40% and 30% respectively at 37℃. The denitrification rates increased when operating temperature was raised from 23℃ to 30℃ and then 37℃. The mechanism of carbon release was analyzed incorporating the experimental results of abiotic release in deionized water. The organic carbon was mainly hydrolyzed by microbes, and the biological release efficiencies were at the range of 89.2% to 96.0%. A long-term experiment with a continuous flow reactor with SCS material containing 70% starch was conducted to gain some experience for practical application. When the influent nitrate concentration was in the range of 35.2 to 39.1 mg/L, hydraulic retention time of 4 hr, and operating temperature of 30℃, a nitrogen removal efficiency up to 94.6% and denitrification rate of 0.217 kg/（m3.day） was achieved. The starch-based materials developed in this study can be used as a solid carbon source for tertiary nitrogen removal from secondary effluent.展开更多
Tertiary denitrification is an effective method for nitrogen removal from wastewater. A pilot-scale biofilter packed with suspended carriers was operated for tertiary denitrification with ethanol as the organic carbon...Tertiary denitrification is an effective method for nitrogen removal from wastewater. A pilot-scale biofilter packed with suspended carriers was operated for tertiary denitrification with ethanol as the organic carbon source. Long-term performance, biokinetics of denitrification and biofilm growth were evaluated under filtration velocities of 6, 10 and 14 m/hr. The pilot-scale biofilter removed nitrate from the secondary effluent effectively, and the nitrate nitrogen（NO_3-N） removal percentage was 82%, 78% and 55% at the filtration velocities of 6, 10 and 14 m/hr, respectively. At the filtration velocities of 6 and 10 m/hr, the nitrate removal loading rate increased with increasing influent nitrate loading rates, while at the filtration velocity of 14 m/hr, the removal loading rate and the influent loading rate were uncorrelated.During denitrification, the ratio of consumed chemical oxygen demand to removed NO_3-N was 3.99-4.52 mg/mg. Under the filtration velocities of 6, 10 and 14 m/hr, the maximum denitrification rate was 3.12, 4.86 and 4.42 g N/（m^2·day）, the half-saturation constant was 2.61, 1.05 and 1.17 mg/L, and the half-order coefficient was 0.22, 0.32 and 0.24（mg/L）1/2/min,respectively. The biofilm biomass increased with increasing filtration velocity and was 2845,5124 and 7324 mg VSS/m^2 at filtration velocities of 6, 10 and 14 m/hr, respectively. The highest biofilm density was 44 mg/cm^3 at the filtration velocity of 14 m/hr. Due to the low influent loading rate, biofilm biomass and thickness were lowest at the filtration velocity of 6 m/hr.展开更多
基金supported by the Ministry of Science and Technology of China (No.2009AA063805)
文摘Starch/polyvinyl alcohol （PVA） blended materials for using as a solid carbon source （SCS） were prepared by blending PVA and gelatinized starch in an aqueous solution system, in which PVA served as framework material and starch as carbon source. The optimization of starch content and temperature effects were investigated. It was indicated that higher denitrification efficiency could be achieved with more starch in the materials. The average specific denitrification rates were 0.93, 0.66, 0.37 and 0.36 mg/（g·day） corresponding to starch content of 70%, 60%, 40% and 30% respectively at 37℃. The denitrification rates increased when operating temperature was raised from 23℃ to 30℃ and then 37℃. The mechanism of carbon release was analyzed incorporating the experimental results of abiotic release in deionized water. The organic carbon was mainly hydrolyzed by microbes, and the biological release efficiencies were at the range of 89.2% to 96.0%. A long-term experiment with a continuous flow reactor with SCS material containing 70% starch was conducted to gain some experience for practical application. When the influent nitrate concentration was in the range of 35.2 to 39.1 mg/L, hydraulic retention time of 4 hr, and operating temperature of 30℃, a nitrogen removal efficiency up to 94.6% and denitrification rate of 0.217 kg/（m3.day） was achieved. The starch-based materials developed in this study can be used as a solid carbon source for tertiary nitrogen removal from secondary effluent.
基金supported by the Major Science and Technology Program for Water Pollution Control and Treatment of China (No. 2012ZX07302002)
文摘Tertiary denitrification is an effective method for nitrogen removal from wastewater. A pilot-scale biofilter packed with suspended carriers was operated for tertiary denitrification with ethanol as the organic carbon source. Long-term performance, biokinetics of denitrification and biofilm growth were evaluated under filtration velocities of 6, 10 and 14 m/hr. The pilot-scale biofilter removed nitrate from the secondary effluent effectively, and the nitrate nitrogen（NO_3-N） removal percentage was 82%, 78% and 55% at the filtration velocities of 6, 10 and 14 m/hr, respectively. At the filtration velocities of 6 and 10 m/hr, the nitrate removal loading rate increased with increasing influent nitrate loading rates, while at the filtration velocity of 14 m/hr, the removal loading rate and the influent loading rate were uncorrelated.During denitrification, the ratio of consumed chemical oxygen demand to removed NO_3-N was 3.99-4.52 mg/mg. Under the filtration velocities of 6, 10 and 14 m/hr, the maximum denitrification rate was 3.12, 4.86 and 4.42 g N/（m^2·day）, the half-saturation constant was 2.61, 1.05 and 1.17 mg/L, and the half-order coefficient was 0.22, 0.32 and 0.24（mg/L）1/2/min,respectively. The biofilm biomass increased with increasing filtration velocity and was 2845,5124 and 7324 mg VSS/m^2 at filtration velocities of 6, 10 and 14 m/hr, respectively. The highest biofilm density was 44 mg/cm^3 at the filtration velocity of 14 m/hr. Due to the low influent loading rate, biofilm biomass and thickness were lowest at the filtration velocity of 6 m/hr.