Influence of Equal Channel Angular Pressing on Tribological Properties of Low Carbon Steel (Fe-0,09C-0,64Si-,26Mn)

This paper presents the results of equal channel angular pressing (ECAP) and subsequent heat treatment (HT) as a method to improve the wear resistance of metallic materials in friction sliding. The effect of ECAP and HT on the microstructure and mechanical properties of low carbon steel is investigated in this work. The mechanisms of wear resistance of steel with ultrafine and nanostructures produced by equal-channel angular pressing is analyzed. The results show that ECAP at room temperature and annealing at 350&degC and 450&degC can be used as a technology of reducing wear in friction sliding.

淬回火工艺对Cronidur30钢组织及性能的影响

利用扫描电镜、摩擦磨损试验机和X射线衍射仪等研究了淬火温度、冷处理温度和回火温度对Cronidur30钢的硬度、残余奥氏体含量以及摩擦磨损性能和耐腐蚀性的影响。结果表明:淬火温度为1 025,1 060℃时,回火态试样硬度均不低于59 HRC,1 025℃淬火试样的残余奥氏体含量略低且组织更加均匀细小;淬火温度为1 025℃时,-75和-196℃这2种冷处理温度对试样硬度和残余奥氏体含量影响的差别不大;淬火温度1 025℃,冷处理温度-75℃时,155,480℃回火温度下试样的硬度均高于58 HRC,155℃回火后试样的减摩性优于480℃,耐磨性则略低;随着回火温度升高,试样的耐腐蚀性下降,回火温度550℃时试样的耐腐蚀性最差。

薄规格高强度工程机械用钢板在线淬火工艺开发

通过对薄规格高强度工程机械用钢研发过程中的技术难题进行了分析,并有针对性采取了措施,使得20~29 mm厚度钢板在线淬火工艺得以成功应用。通过对轧制道次的优化提高了轧制板形、通过冷却单元上下水比、边部遮挡优化保证了冷却的均有性,通过钢板头部跟踪位置优化解决了头部过冷问题,为水冷后板形的改善创造了条件。通过头尾遮挡参数及热处理回火工艺优化,保证了钢板性能的均匀性,实现了薄规格钢板的短流程生产,取得了较好的经济效益和社会效益。

直连绳索取心钻杆分区热处理技术研究

为了提高绳索取心钻杆的性能,对直连绳索取心钻杆的受力情况、结构特点以及传统处理工艺进行分析,提出了分区热处理的工艺。通过对两端进行热加工处理,使钻杆中间管体区域和两端热处理螺纹区域性能出现差异,提高两端综合强度的同时改善螺纹部分的受力状态,可使钻杆柱既具有高强度又兼具柔性,大幅提高钻杆机械性能以及耐磨性。其中调质硬度HRC33~38能在保证管体延伸率与正火、回火基本一致的情况下,强度提高37.7%,硬度提高40%,抗冲击性提高46.7%。调质硬度HRC38~42时,材料的耐磨性提高9.1%。更适合全液压钻机施工及深孔钻进,为钻探施工提供了钻机、钻杆配套性的优选方案。

NM500级高强度低合金耐磨钢的研制开发

在研制开发NM500级高强度低合金耐磨钢过程中,通过设计合理成分体系及淬火+回火工艺方案,实现塑韧性与硬度匹配良好、高强度低合金耐磨钢NM500的稳定生产。布氏硬度均在489~528HBW,显微组织观察发现厚度截面为全马氏体组织。针对典型工艺的成品钢进行冲击磨料磨损耐磨对比试验,结果显示:NM500级高强度低合金耐磨钢的相对耐磨性优于NM400和NM450级高强度低合金耐磨钢,为Q355B级高强度低合金耐磨钢的8.30倍。

超紧凑型钢管感应调质热处理线的研究应用

通过ARE产线钢管感应调质热处理线研究应用项目的开展,对现有感应热处理线进行改造。现有的ARE钢管感应热处理线整体布局不变,整流变压器、上料台架、上料装置、下料装置、双向链式冷床、下料台架及液压站等利旧,输送辊道部分利旧、局部改造,淬火电源、回火电源及感应圈根据产品方案按照淬火+回火工艺要求重新设计并更新,补齐相应的水淬及配套的水循环系统,配套相应仪表、自动化、计算机系统,实现温度闭环控制。通过改造将现有感应热处理线打造成一条超紧凑型钢管感应调质热处理线,使其具备年淬火+回火热处理管线管、接箍料、石油套管等3万t的生产能力,弥补ARE产线热处理的缺口,提高产线的盈利能力。

淬火温度对高速钢微观组织和力学性能的影响研究

本文研究了淬火温度(900℃、1000℃、1050℃和1100℃等)对高速钢微观组织和力学性能的影响。结果表明:高速钢淬火态基体组织为马氏体和残余奥氏体,硬质相为M_(6)C、M_(2)C和MC(M=Fe、W、Cr、Mo和V等)。随着淬火温度的上升,试样中析出的碳化物逐渐细化呈层片状,当淬火温度为1000℃时,合金的宏观硬度达到最大值为73.08HRC,较铸态硬度提高了约14.04%。此外,JmatPro模拟结果显示高的淬火温度可以促进碳化物的析出,增强其抗变形和抗磨损性能。

Development of SA-533 Type B CL. 1+SA-240 Type 304L roll-bonded clad steel plate for safety injection tank of CAP1400 nuclear power plant

Aiming to meet the demand of the country＇ s nuclear demonstration project on the CAP1400 nuclear power plant, Baosteel uses the roll-bonding technology and develops the SA-533 Type B CL. 1 ＋ SA-240 Type 304L high-strength and high-toughness clad steel plate with a shear strength of over 310 MPa for the nuclear power plant＇ s safety injection tank. The properties of the quenched and tempered and the simulated post-weld heat treatment states are systematically studied herein through a comprehensive inspection and evaluation of the composition,microstructure,and properties of the clad steel plate. The results show that the bonding interface has high shear strength and that the base metal has high strength and good toughness at low temperatures. Hence, the performance fully meets the technical requirements of the CAP1400 nuclear power plant＇ s safety injection tank in the country＇ s nuclear demonstration project. The roll-bonded clad steel plate can be used to manufacture the safety injection tank of the CAP1400 nuclear power plant.

热处理工艺对双金属带锯条背材用钢RM80组织和性能的影响

采用扫描电镜、洛氏硬度计和万能试验机研究了不同热处理工艺对RM80钢显微组织和力学性能的影响。结果表明,随着淬火温度升高,RM80钢中碳化物逐渐溶解,原奥氏体晶粒不断长大;在回火过程中,RM80组织由回火屈氏体转变为回火索氏体,且在较高温度淬火再回火后的RM80组织中仍能看到马氏体形态。经1 150℃淬火和550℃三次回火后,RM80钢可以实现强度和塑性的良好匹配,其屈服强度为1 244 MPa,抗拉强度为1 590 MPa,延伸率为12.0%。

矿用齿辊破碎机齿环热处理脆性研究

针对当前国产齿辊破碎机齿环制造开裂问题,在不改变破碎机齿环整体硬度和韧性的前提下,基于中碳合金钢热处理第一类回火脆性特征,通过调整材质元素含量区间和重复试验,找到最合理的铸件淬火温度和低温回火温度,从而解决整个制造过程中局部开裂缺陷,降低制造成本,提升齿环整体可靠性。

淬火-回火热处理对超高强Fe-Mn-Al-C合金钢组织与力学性能影响研究

对一种成分为Fe-8Mn-8Al-0.8C的Fe-Mn-Al-C系超高强合金钢的热轧钢板进行“淬火+回火”热处理试验,研究其力学性能和微观组织。结果表明,试验用钢在热轧后由铁素体、奥氏体以及κ-碳化物三种物相组成,且组织呈现明显的带状,经热处理后κ-碳化物消除,热轧板在900℃保温1 h后水淬200℃回火60 min后呈现最优整体力学性能,抗拉强度达到1410 MPa,延伸率为29%,强塑积达到41 GPa·%。

锻造核级316L奥氏体不锈钢的热处理和力学性能

小型轻水堆在军民两用领域具有广阔的应用前景,316L奥氏体不锈钢具有优异的耐热性和抗晶界腐蚀性能,可用于小型轻水堆核电站管道和阀门的制造。本研究采用真空感应熔炼-锻造-固溶热处理的技术路线制备出兼具良好强度、延伸率和冲击韧性的316L不锈钢,其屈服强度、抗拉强度、延伸率和断面收缩率分别达到了280 MPa、585 MPa、64%和75%,均满足国标要求,而且冲击韧性可达212 J/cm^(2)。研究进一步分析了回火处理对316L不锈钢力学性能的影响,发现750℃的高温回火对316L奥氏体不锈钢的力学性能具有严重的损害,会导致316L不锈钢冲击韧性降低60%。

液压泥炮泥缸的制备

针对进口液压泥炮泥缸出现内表面磨损、变形、缸体炸裂等现象迫使设备停机,进口泥缸价格昂贵、交货期长等问题,采用含钕特殊合金钢和淬火+回火热处理加工工艺,制备了国产液压泥炮泥缸,完全满足进口液压泥炮的工作条件与性能要求,可以实现替代进口泥缸,满足生产的需要,单个泥缸可降低备件成本16万元。

提升弹簧钢性能的研究与分析

弹簧钢因其具有优异的弹性和韧性,广泛应用于汽车制造、钢轨固定等领域。为了进一步优化弹簧钢性能及质量,生产厂家有必要展开相关技术研究。基于此,通过分析弹簧钢轧制的特点、化学成分、相变规律、高温力学性能和奥氏体动态再结晶等方面,对弹簧钢的基本性能进行研究。以55Si2MnV弹簧钢为例,对淬火阶段热处理工艺、回火阶段热处理工艺进行总结,通过热处理工艺提升弹簧钢性能,以期为提升弹簧钢性能研究提供参考。

Application of the Computer-aided Quenching Technology on the Connecting Bar of 42CrMo4

In order to obtain the desired mechanical properties of connecting bar after quenching and tempering,and reduce the cracking tendency and distortion,a program of controllable quenching was established.Furthermore,a computer-aided quenching (CAQ) system was developed.The applications show satisfactory results.

调质参数对转子用25Cr2NiMo1V钢性能的影响

对转子用25Cr2NiMo1V钢材料进行940℃淬火+660℃回火的调质处理,研究改变淬火冷却速度和回火保温时间对材料组织和性能的影响。结果表明,随着淬火冷却速度的提高,材料的屈服强度和抗拉强度逐渐升高,冲击韧性逐渐降低;不同回火保温时间对材料组织影响较小,均为贝氏体回火组织;随着回火保温时间的增加,材料的强度和高温持久性能逐渐降低,冲击韧性逐渐升高,韧脆转变温度下降。

国产9Cr-1Mo-V-Nb-N钢的组织及热处理工艺研究

通过测试采用不同参数热处理后材料的力学性能,以及组织结构分析,基本查明了影响国产P91钢性能的关键.研究结果表明:回火温度和时间的选择,直接影响最终组织和碳化物的形态与分布,从而导致了力学性能的差异;同时,测试数据与进口材料数据的对比表明,通过工艺优化,国产P91钢的性能已明显改善.

工程机械用Q960钢的调质热处理工艺

为开发960MPa级工程机械用Q960钢板,研究确定了其调质热处理工艺。结果表明:其最佳的淬火工艺为900℃保温20min,最佳的回火工艺为600℃保温40min;经最佳调质热处理后试验钢的组织为回火索氏体,屈服强度为1 030 MPa,抗拉强度为1 080 MPa,伸长率为16.8%,-40℃冲击功达144J,满足GB/T 16270-2009的要求。

高温热处理对活性炭纤维微孔及表面性能的影响

研究了1173K高温改性处理对沥青基活性炭纤维吸附性能、孔径分布、微孔结构和表面化学的影响。低温(77K)N2吸附结果表明热处理后活性炭纤维比表面积略有下降,通过密度函数理论解析活性炭纤维全孔范围的孔分布得出活性炭纤维表面孔径大于1.0nm的微孔明显减少,微孔孔径更加集中于0.5nm～1.0nm,从而提高了活性炭纤维的碘吸附值。X射线衍射分析表明活性炭纤维是乱层石墨结构,热处理使活性炭纤维类石墨微晶碳层面的层间距下降,X光电子能谱分析表明热处理后活性炭纤维表面的含氧官能团C=O和COOH的含量变化不大,而呈碱性酚羟基C OH含量的明显下降使活性炭纤维表面碱性降低。

热处理工艺对12Cr1MoVG厚壁无缝钢管表面硬度的影响

分析了12CrlMoVG厚壁无缝钢管组织分布状态与硬度的关系；通过测定其CCT曲线，确定出Ф219mmx45mm规格12CrlMoVG厚壁无缝钢管的最佳热处理工艺：淬火970℃×60min、水淬20s，回火750℃×150min。生产结果表明：通过控制淬火时间，可减少铁素体的析出量，避免马氏体组织的大量析出，从而实现产品硬度的控制；新热处理工艺实现了12CrlMoVG厚壁无缝钢管硬度在161～182HB内的稳定控制，表面硬度合格率达100％，且其各项机械性能指标均满足标准要求。