To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 4...To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 400 kg/m3 were tested. Ground granulated blast-furnace slag (GGBS) as a source material was activated by the following two types of alkali activators: 10% Ca(OH)2 and 4% Mg(NO3)2, and 2.5% Ca(OH)2 and 6.5% Na2SiO3. The main test parameters were water-to-binder (W/B) ratio and the substitution level (RFA) of fly ash (FA) for GGBS. Test results revealed that the dry density of AA GGBS foamed concrete was independent of the W/B ratio an RFA, whereas the compressive strength increased with the decrease in W/B ratio and with the increase in RFA up to 15%, beyond which it decreased. With the increase in the W/B ratio, the amount of macro capillaries and artificial air pores increased, which resulted in the decrease of compressive strength. The magnitude of the environmental loads of the AA GGBS foamed concrete is independent of the W/B ratio and RFA. The largest reduction percentage was found in the photochemical oxidation potential, being more than 99%. The reduction percentage was 87% - 93% for the global warming potential, 81% - 84% for abiotic depletion, 79% - 84% for acidification potential, 77% - 85% for eutrophication potential, and 73% - 83% for human toxicity potential. Ultimately, this study proved that the developed AA GGBS foamed concrete has a considerable promise as a sustainable construction material for nonstructural element.展开更多
[Objective] This study aimed to further explore the dynamics of related physiological indexes of rice seedlings under different NH4＋ /NO3- ratio and different water condition. [Method] Under the hydroponic condition ...[Objective] This study aimed to further explore the dynamics of related physiological indexes of rice seedlings under different NH4＋ /NO3- ratio and different water condition. [Method] Under the hydroponic condition in laboratory, 3 NH4＋/NO3- ratios （0/100, 50/50 and 100/0） and 2 water conditions （＋PEG,-PEG） were designed for Fengliangyou 7203. [Result] The root-canopy ratio of rice seedlings increased under any of the NH4＋/NO3- ratios and water conditions. Under water stress, the root-canopy ratio of rice seedlings changed most greatly at the NH4＋/NO3- ratio of 0/ 100; the overall water potential of rice seedlings reached the lowest at the NH4＋/ NO3- ratio of 100/0; and the changes of water potential and xylem flow pH were relatively stable at the NH4＋/NO3- ratio of 50/50. Under the condition of no water stress, the growth of rice seedlings was best at the NH4＋/NO3- ratio of 50/50, followed by the NH4＋/NO3- ratios of 0/100 and 100/0. [Conclusion] This study will pro- vide a basis for understanding the relationship between water potential and xylem flow.展开更多
In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirement...In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.展开更多
固定水胶比为0.24,通过I级粉煤灰替代砂浆中30%~70%水泥的强度试验,研究了Na 2 SO 4对粉煤灰-水泥砂浆体系的激发效果。结果表明:不掺激发剂时,砂浆抗压和抗折强度随粉煤灰替代率的增加成比例下降,且粉煤灰替代率达50%以上时对强度增长...固定水胶比为0.24,通过I级粉煤灰替代砂浆中30%~70%水泥的强度试验,研究了Na 2 SO 4对粉煤灰-水泥砂浆体系的激发效果。结果表明:不掺激发剂时,砂浆抗压和抗折强度随粉煤灰替代率的增加成比例下降,且粉煤灰替代率达50%以上时对强度增长速率有显著提升作用。粉煤灰替代率不低于50%时,1%的Na 2 SO 4掺量对砂浆抗压强度增进效果最佳,与此不同的是,Na 2 SO 4掺量越高,对砂浆抗折强度的增长越有利。随龄期增长,Na 2 SO 4激发粉煤灰-水泥砂浆的折压比显著下降,但抗折强度均在5.0 MPa以上。展开更多
文摘To provide basic data for the reasonable mixing design of the alkali-activated (AA) foamed concrete as a thermal insulation material for a floor heating system, 9 concrete mixes with a targeted dry density less than 400 kg/m3 were tested. Ground granulated blast-furnace slag (GGBS) as a source material was activated by the following two types of alkali activators: 10% Ca(OH)2 and 4% Mg(NO3)2, and 2.5% Ca(OH)2 and 6.5% Na2SiO3. The main test parameters were water-to-binder (W/B) ratio and the substitution level (RFA) of fly ash (FA) for GGBS. Test results revealed that the dry density of AA GGBS foamed concrete was independent of the W/B ratio an RFA, whereas the compressive strength increased with the decrease in W/B ratio and with the increase in RFA up to 15%, beyond which it decreased. With the increase in the W/B ratio, the amount of macro capillaries and artificial air pores increased, which resulted in the decrease of compressive strength. The magnitude of the environmental loads of the AA GGBS foamed concrete is independent of the W/B ratio and RFA. The largest reduction percentage was found in the photochemical oxidation potential, being more than 99%. The reduction percentage was 87% - 93% for the global warming potential, 81% - 84% for abiotic depletion, 79% - 84% for acidification potential, 77% - 85% for eutrophication potential, and 73% - 83% for human toxicity potential. Ultimately, this study proved that the developed AA GGBS foamed concrete has a considerable promise as a sustainable construction material for nonstructural element.
基金Supported by Natural Science Foundation of Guangdong Province(2014 A030307013)~~
文摘[Objective] This study aimed to further explore the dynamics of related physiological indexes of rice seedlings under different NH4＋ /NO3- ratio and different water condition. [Method] Under the hydroponic condition in laboratory, 3 NH4＋/NO3- ratios （0/100, 50/50 and 100/0） and 2 water conditions （＋PEG,-PEG） were designed for Fengliangyou 7203. [Result] The root-canopy ratio of rice seedlings increased under any of the NH4＋/NO3- ratios and water conditions. Under water stress, the root-canopy ratio of rice seedlings changed most greatly at the NH4＋/NO3- ratio of 0/ 100; the overall water potential of rice seedlings reached the lowest at the NH4＋/ NO3- ratio of 100/0; and the changes of water potential and xylem flow pH were relatively stable at the NH4＋/NO3- ratio of 50/50. Under the condition of no water stress, the growth of rice seedlings was best at the NH4＋/NO3- ratio of 50/50, followed by the NH4＋/NO3- ratios of 0/100 and 100/0. [Conclusion] This study will pro- vide a basis for understanding the relationship between water potential and xylem flow.
文摘In this paper, a high calcium high sulfate ash as the main material, adding fly ash, lime, cement, gypsum and some modifiers to prepare autoclaved aerated concrete. The products complies with the technical requirements of GB/T11968-2006. This paper also studies the influence of the physical methods and water ratio on autoclaved aerated concrete by high calcium high sulfate ash aerated concrete. The best ratio of water and Grinding time were found in practice study.
文摘固定水胶比为0.24,通过I级粉煤灰替代砂浆中30%~70%水泥的强度试验,研究了Na 2 SO 4对粉煤灰-水泥砂浆体系的激发效果。结果表明:不掺激发剂时,砂浆抗压和抗折强度随粉煤灰替代率的增加成比例下降,且粉煤灰替代率达50%以上时对强度增长速率有显著提升作用。粉煤灰替代率不低于50%时,1%的Na 2 SO 4掺量对砂浆抗压强度增进效果最佳,与此不同的是,Na 2 SO 4掺量越高,对砂浆抗折强度的增长越有利。随龄期增长,Na 2 SO 4激发粉煤灰-水泥砂浆的折压比显著下降,但抗折强度均在5.0 MPa以上。