Double cantilever beam tests were used to measure the energy release rates of linear vibrational welded moso bamboo joints.The influence of the length of the preserved cracks,the different combinations of the inner an...Double cantilever beam tests were used to measure the energy release rates of linear vibrational welded moso bamboo joints.The influence of the length of the preserved cracks,the different combinations of the inner and outer bamboo surfaces and the moisture content is studied herein.The experimental compliance method,which is based on linear elastic fracture mechanics and has been shown to be an ideal method,was used to analyze data with the power equation.The results show that the preserved initial crack length does not have a significant effect on the final measured energy release rate,while the moso bamboo combination does affect the properties dramatically.The welded moso bamboo joints with inner-inner surfaces have the highest energy release rate of 122 J/m^2.The average energy release of the outer-outer combination was only 102 J/m^2.The expansion of the cracks also became easier when the moisture content of the welded joints was 18.5%compared to 4.5% and 10.1%.So the moisture resistance of the welded joints should be duly improved.展开更多
In order to analyze the failure data from repairable systems, the homogeneous Poisson process (HPP) is usually used. In general, HPP cannot be applied to analyze the entire life cycle of a complex, re-pairable system ...In order to analyze the failure data from repairable systems, the homogeneous Poisson process (HPP) is usually used. In general, HPP cannot be applied to analyze the entire life cycle of a complex, re-pairable system because the rate of occurrence of failures (ROCOF) of the system changes over time rather than remains stable. However, from a practical point of view, it is always preferred to apply the simplest method to address problems and to obtain useful practical results. Therefore, we attempted to use the HPP model to analyze the failure data from real repairable systems. A graphic method and the Laplace test were also used in the analysis. Results of numerical applications show that the HPP model may be a useful tool for the entire life cycle of repairable systems.展开更多
为解决信息处理微系统中双倍速率同步动态随机存储器(Double Data Rate,DDR)复杂互连故障的检出效率和测试成本问题,通过分析DDR典型互连故障模式,将单个存储器件的自动测试设备(Auto Test Equipment,ATE)测试算法与板级系统的系统级测...为解决信息处理微系统中双倍速率同步动态随机存储器(Double Data Rate,DDR)复杂互连故障的检出效率和测试成本问题,通过分析DDR典型互连故障模式,将单个存储器件的自动测试设备(Auto Test Equipment,ATE)测试算法与板级系统的系统级测试(System Level Test,SLT)模式相结合,提出面向DDR类存储器的测试算法和实现技术途径。并基于现场可编程门阵列(Field Programmable Gate Array,FPGA)器件实现微系统内DDR互连故障的自测试,完成了典型算法的仿真模拟和实物测试验证。相较于使用ATE测试机台的存储器测试或通过用户层测试软件的测试方案,本文所采用的FPGA嵌入特定自测试算法方案可以实现典型DDR互连故障的高效覆盖,测试效率和测试成本均得到明显改善。展开更多
Peel test measurements and simulations of the interfacial mechanical parameters for the Al/Epoxy/Al2O3 system are performed in the present investigation. A series of Al film thicknesses between 20 and 250 microns and ...Peel test measurements and simulations of the interfacial mechanical parameters for the Al/Epoxy/Al2O3 system are performed in the present investigation. A series of Al film thicknesses between 20 and 250 microns and three peel angles of 90, 135 and 180 degrees are considered. Two types of epoxy adhesives are adopted to obtain both strong and weak interface adhesions. A finite element model with cohesive zone elements is used to identify the interfacial parameters and simulate the peel test process. By simulating and recording normal stress near the crack tip, the separation strength is obtained, Furthermore, the cohesive energy is identified by comparing the simulated steady-state peel force and the experimental result. It is found from the research that both the cohesive energy and the separation strength can be taken as the intrinsic interfacial parameters which are dependent on the thickness of the adhesive layer and independent of the film thickness and peel angle.展开更多
文摘Double cantilever beam tests were used to measure the energy release rates of linear vibrational welded moso bamboo joints.The influence of the length of the preserved cracks,the different combinations of the inner and outer bamboo surfaces and the moisture content is studied herein.The experimental compliance method,which is based on linear elastic fracture mechanics and has been shown to be an ideal method,was used to analyze data with the power equation.The results show that the preserved initial crack length does not have a significant effect on the final measured energy release rate,while the moso bamboo combination does affect the properties dramatically.The welded moso bamboo joints with inner-inner surfaces have the highest energy release rate of 122 J/m^2.The average energy release of the outer-outer combination was only 102 J/m^2.The expansion of the cracks also became easier when the moisture content of the welded joints was 18.5%compared to 4.5% and 10.1%.So the moisture resistance of the welded joints should be duly improved.
文摘In order to analyze the failure data from repairable systems, the homogeneous Poisson process (HPP) is usually used. In general, HPP cannot be applied to analyze the entire life cycle of a complex, re-pairable system because the rate of occurrence of failures (ROCOF) of the system changes over time rather than remains stable. However, from a practical point of view, it is always preferred to apply the simplest method to address problems and to obtain useful practical results. Therefore, we attempted to use the HPP model to analyze the failure data from real repairable systems. A graphic method and the Laplace test were also used in the analysis. Results of numerical applications show that the HPP model may be a useful tool for the entire life cycle of repairable systems.
文摘为解决信息处理微系统中双倍速率同步动态随机存储器(Double Data Rate,DDR)复杂互连故障的检出效率和测试成本问题,通过分析DDR典型互连故障模式,将单个存储器件的自动测试设备(Auto Test Equipment,ATE)测试算法与板级系统的系统级测试(System Level Test,SLT)模式相结合,提出面向DDR类存储器的测试算法和实现技术途径。并基于现场可编程门阵列(Field Programmable Gate Array,FPGA)器件实现微系统内DDR互连故障的自测试,完成了典型算法的仿真模拟和实物测试验证。相较于使用ATE测试机台的存储器测试或通过用户层测试软件的测试方案,本文所采用的FPGA嵌入特定自测试算法方案可以实现典型DDR互连故障的高效覆盖,测试效率和测试成本均得到明显改善。
基金the Chinese Academy of Sciences (No.KJCX2-YW-M04) the National Science Foundationof China (Nos.10432050, 10672163 and 10721202).
文摘Peel test measurements and simulations of the interfacial mechanical parameters for the Al/Epoxy/Al2O3 system are performed in the present investigation. A series of Al film thicknesses between 20 and 250 microns and three peel angles of 90, 135 and 180 degrees are considered. Two types of epoxy adhesives are adopted to obtain both strong and weak interface adhesions. A finite element model with cohesive zone elements is used to identify the interfacial parameters and simulate the peel test process. By simulating and recording normal stress near the crack tip, the separation strength is obtained, Furthermore, the cohesive energy is identified by comparing the simulated steady-state peel force and the experimental result. It is found from the research that both the cohesive energy and the separation strength can be taken as the intrinsic interfacial parameters which are dependent on the thickness of the adhesive layer and independent of the film thickness and peel angle.