The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufacture...The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufactured by means of reasonable fabricating technology. The application results of the developed magnesia-chrome bricks at 300t RH degasser of Baosteel indicate that the lining life has been increased up to 150 heats.展开更多
The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually i...The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually increased with the reduction of the impurity content of brick , the pre-synthetic raw material it applied and the operating condition of convener is optimized so that the service life of convener is largely enhanced.展开更多
Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and...Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.展开更多
The paper analyzed the recycle condition and developing trend of used refractories China and other countries, irwluding research achievements of recycles of used refractories such as MgO-C bricks, Al2O3-MgO-C brics, A...The paper analyzed the recycle condition and developing trend of used refractories China and other countries, irwluding research achievements of recycles of used refractories such as MgO-C bricks, Al2O3-MgO-C brics, Al2O3-SiC-C castable and MgO-Cr2O3 bricks. Recycled refractories exhibit the same or even better properties as compared with the original. In addition, prospects for recycle of used refractories are also discusseded.展开更多
文摘The paper analyses the wear mechanism of magnesia-chrome bricks for snorkel of RH degasser. High-performance magnesia-chrome bricks with good resistance to molten slag and infiltration resistance have been manufactured by means of reasonable fabricating technology. The application results of the developed magnesia-chrome bricks at 300t RH degasser of Baosteel indicate that the lining life has been increased up to 150 heats.
文摘The state-of-art of magnesia-chrome refractories from direct-bonded magnesia chrome brick to fused-grain rebounded magnesia chrome brick for P-S converter is dis-cribed. The Cr2O3 content of the brick is continually increased with the reduction of the impurity content of brick , the pre-synthetic raw material it applied and the operating condition of convener is optimized so that the service life of convener is largely enhanced.
文摘Effects of FeO content （0, 5%, 10%, and 15% in mass, respectively ） in lab-synthesized smelting redttc- tion slag with iron bath and test temperature （1 450, 1 500, 1550, anti 1 600 ℃ ） on corrosion am,amount and microstructure of fused rebonded magnesia - chrome brick with 26.02 massqc of Cr2O3 were researched by rotary cylinder method. The results show that ： （ 1 ） the corro- sion amolult of magnesia -chrome brick by slag without FeO is higher than that by the slag with 5% FeO, and the vorrosion amount increases when FeO content increa- ses from 5% to 15% ; （2） the test temperature is one of the important factors affecting the slag corrosion resist- ance of magnesia - chrome brick, and the corrosion of smelting reduction slag to brick increases with the temperature rising.
文摘The paper analyzed the recycle condition and developing trend of used refractories China and other countries, irwluding research achievements of recycles of used refractories such as MgO-C bricks, Al2O3-MgO-C brics, Al2O3-SiC-C castable and MgO-Cr2O3 bricks. Recycled refractories exhibit the same or even better properties as compared with the original. In addition, prospects for recycle of used refractories are also discusseded.