Hot-rolled wide strip for production of large diameter,heavy gauged(up to 19 mm) helical line pipe grade X80 was a priority development over the last three years.Microstructure,texture and mechanical properties of str...Hot-rolled wide strip for production of large diameter,heavy gauged(up to 19 mm) helical line pipe grade X80 was a priority development over the last three years.Microstructure,texture and mechanical properties of strips have been characterised.Also the welding conditions have been simulated.The favourable microstructure is achieved by the proper selection of an appropriate chemical composition of low carbon content and increased niobium micro alloying in combination with suitable strictly controlled hot-rolling parameters.The addition of niobium in combination with the adjustment of other alloying elements increases the recrystallisation stop temperature and thus makes it possible to apply a high temperature processing(HTP) concept.The homogeneous bainitic microstructure across the strip gauge is then formed during accelerated cooling on the run-out table of the hot-rolling mill.All results indicated excellent properties of these hot strips which make it suitable for spiral pipes of grade X80 for example 18.9mm×Φ1 220 mm at dimension.展开更多
During the process of laying long-distance oil and gas transmission pipelines, the hot-induction-bend method is extensively used when the direction has to be changed. By considering the pipeline＇ s ongoing processing...During the process of laying long-distance oil and gas transmission pipelines, the hot-induction-bend method is extensively used when the direction has to be changed. By considering the pipeline＇ s ongoing processing and loading states during service, the pipeline that is generally used exhibits thicker walls than those that are observed in the line pipe. As such, during pipeline construction, hot-induction-bend and line pipes with different wall thickness are girth-welded. The chemical composition of hot-induction-bend and line pipes differs, with the carbon content being particularly higher in the hot-induction-bend pipe;it also depicts a higher carbon equivalent, which makes it possible to modify the girth of the pipe. In this study, using Baosteel＇ s standard X70M UOE hot- induction-bend and line pipes, solid-wire automatic gas-metal-arc girth welding was performed and the performance of the girth-welded joint was evaluated. Furthermore,the weldability of the pipeline girth and the microstructure of the girth-welded joint were analyzed. The results reveal that Baosteel＇ s standard UOE hot-induction-bend and line pipes exhibit good girth weldability, and their technical quality can be guaranteed in case of consumer field- construction applications.展开更多
Since the development of offshore oil and gas, increased submarine oil and gas pipelines were installed. All the early steel pipes of submarine pipelines depended on importing because of the strict requirements of com...Since the development of offshore oil and gas, increased submarine oil and gas pipelines were installed. All the early steel pipes of submarine pipelines depended on importing because of the strict requirements of comprehensive properties, such as, anti-corrosion, resistance to pressure and so on. To research and develop domes- tic steel pipes used for the submarine pipeline, the Longitudinal-seam Submerged Arc Welded （LSAW） pipes were made of steel plates cut from leveled hot rolled coils by both the JCOE and UOE （the forming process in which the plate like the letter “J”, “C”, “0” or “U” shape, then expansion） forming processes. Furthermore, the mechanical properties of the pipe base metal and weld metal were tested, and the results were in accordance with the corresponding pipe specification API SPEC 5L or DNV- OS-FI01, which showed that domestic LSAW pipes could be used for submarine oil and gas pipelines.展开更多
The objective of this study is to investigate the influence of post weld heat treatment （PWHT） on the distribution of residual stress in welded pipes with large thickness. The detailed pass-by-pass finite element si...The objective of this study is to investigate the influence of post weld heat treatment （PWHT） on the distribution of residual stress in welded pipes with large thickness. The detailed pass-by-pass finite element simulation was developed to study the residual stress in narrow gap multipass welding of pipes with a wall thickness of 150 mm and 89 weld beads. The effect of PWHT on welding residual stress was also investigated by means of numerical analysis. The simulated results show that the hoop stress is tensile stress in the weld region and compressive stress in the parent metal areas adjacent to weld seam. After heat treatment, the residual stresses decrease substantially, and the simulated residual stress is validated by the experimental one. The distribution of the through-wall axial residual stress along the weld center line is a self-equilibrating type.展开更多
In order to solve the problems of excess ovality and cross-section distortion of longitudinally submerged arc welding pipes after forming,a new three-roller continuous setting round process was proposed.This process c...In order to solve the problems of excess ovality and cross-section distortion of longitudinally submerged arc welding pipes after forming,a new three-roller continuous setting round process was proposed.This process can be divided into three stages:loading stage,roll bending stage and unloading stage.Based on the discretization idea,the mechanical model of the primary statically indeterminate problem of the longitudinally submerged arc welding pipes at the roll bending stage was established,and the deformation response was obtained.The simulation and theoretical results show that there are three positive bending regions and three reverse bending regions along the circumference of the pipe.The loading force of each roller shows growth,stability and downward trend with time.The error between the theoretical fitting curve and the simulated data point is very small,and the simulation results verify the reliability of the theoretical calculation.The experimental results show that the residual ovality decreases with the increase of the reduction,and the reduction of the turning point is the optimum reduction.In addition,the residual ovality of the pipe is less than 0.7%without cross-section distortion,which verifies the feasibility of this process.展开更多
This study developed a sequential coupling finite element procedure to predict residual stresses of steel pipes with longitudinal wela／ circumferential weld and spiral weld.The results show that the residual stress i...This study developed a sequential coupling finite element procedure to predict residual stresses of steel pipes with longitudinal wela／ circumferential weld and spiral weld.The results show that the residual stress in heat affected zone（HAZ）is higher than that in weld for spiral weld pipe.For the circumferential weld pipe and spiral weld pipe,the residual stress in inner surface is higher than that in outer surface.However,for the spiral weld pipe,the residual stress in inner surface is smaller than that in outer surface.The hoop residual stress of circumferential weld pipe is higher than that of longitudinal weld pipe,while the axial residual stress of circumferential weld pipe is smaller than that of longitudinal weld pipe.The hoop stresses for circumferential weld pipe and axial stress for longitudinal weld pipe have exceeded the yield strength of base metal.With the increase of helix angle,the hoop stress decreases while the axial stress increases.For the spiral pipe（α=30° to 50°）,both the hoop stress and axial stress are relatively small.The spiral pipe（helix angle ranging from 30° to 50°） is helpful to reduce stress corrosion cracking（SCC） and it is recommended to manufacture the steel pipe.展开更多
In this article the research and development of X70 large diameter longitudinal seam submerged arc welded (LSAW) steel pipes for West East Gas Transportation Pipeline project (WEGTP) in China are introduced, including...In this article the research and development of X70 large diameter longitudinal seam submerged arc welded (LSAW) steel pipes for West East Gas Transportation Pipeline project (WEGTP) in China are introduced, including the key technique, fabrication of pipe production line, mass production and the latest progress of LSAW steel pipe technique.展开更多
文摘Hot-rolled wide strip for production of large diameter,heavy gauged(up to 19 mm) helical line pipe grade X80 was a priority development over the last three years.Microstructure,texture and mechanical properties of strips have been characterised.Also the welding conditions have been simulated.The favourable microstructure is achieved by the proper selection of an appropriate chemical composition of low carbon content and increased niobium micro alloying in combination with suitable strictly controlled hot-rolling parameters.The addition of niobium in combination with the adjustment of other alloying elements increases the recrystallisation stop temperature and thus makes it possible to apply a high temperature processing(HTP) concept.The homogeneous bainitic microstructure across the strip gauge is then formed during accelerated cooling on the run-out table of the hot-rolling mill.All results indicated excellent properties of these hot strips which make it suitable for spiral pipes of grade X80 for example 18.9mm×Φ1 220 mm at dimension.
文摘During the process of laying long-distance oil and gas transmission pipelines, the hot-induction-bend method is extensively used when the direction has to be changed. By considering the pipeline＇ s ongoing processing and loading states during service, the pipeline that is generally used exhibits thicker walls than those that are observed in the line pipe. As such, during pipeline construction, hot-induction-bend and line pipes with different wall thickness are girth-welded. The chemical composition of hot-induction-bend and line pipes differs, with the carbon content being particularly higher in the hot-induction-bend pipe;it also depicts a higher carbon equivalent, which makes it possible to modify the girth of the pipe. In this study, using Baosteel＇ s standard X70M UOE hot- induction-bend and line pipes, solid-wire automatic gas-metal-arc girth welding was performed and the performance of the girth-welded joint was evaluated. Furthermore,the weldability of the pipeline girth and the microstructure of the girth-welded joint were analyzed. The results reveal that Baosteel＇ s standard UOE hot-induction-bend and line pipes exhibit good girth weldability, and their technical quality can be guaranteed in case of consumer field- construction applications.
文摘Since the development of offshore oil and gas, increased submarine oil and gas pipelines were installed. All the early steel pipes of submarine pipelines depended on importing because of the strict requirements of comprehensive properties, such as, anti-corrosion, resistance to pressure and so on. To research and develop domes- tic steel pipes used for the submarine pipeline, the Longitudinal-seam Submerged Arc Welded （LSAW） pipes were made of steel plates cut from leveled hot rolled coils by both the JCOE and UOE （the forming process in which the plate like the letter “J”, “C”, “0” or “U” shape, then expansion） forming processes. Furthermore, the mechanical properties of the pipe base metal and weld metal were tested, and the results were in accordance with the corresponding pipe specification API SPEC 5L or DNV- OS-FI01, which showed that domestic LSAW pipes could be used for submarine oil and gas pipelines.
基金The authors acknowledge the financial support of the National Science and Technology Support Program of China （2009BAF44 BO0） and Research Fund for the Doctoral Program of Higher Education of China （20100201110065） and National Natural Science Foundation of China （ 51375370 ）.
文摘The objective of this study is to investigate the influence of post weld heat treatment （PWHT） on the distribution of residual stress in welded pipes with large thickness. The detailed pass-by-pass finite element simulation was developed to study the residual stress in narrow gap multipass welding of pipes with a wall thickness of 150 mm and 89 weld beads. The effect of PWHT on welding residual stress was also investigated by means of numerical analysis. The simulated results show that the hoop stress is tensile stress in the weld region and compressive stress in the parent metal areas adjacent to weld seam. After heat treatment, the residual stresses decrease substantially, and the simulated residual stress is validated by the experimental one. The distribution of the through-wall axial residual stress along the weld center line is a self-equilibrating type.
基金supported by the National Natural Science Foundation of China (Nos. 52005431, 51705449 and 51975509)the Natural Science Foundation of Hebei Province of China (No. E2020203086)the National Major Science and Technology Projects of China (No. 2018ZX04007002)
文摘In order to solve the problems of excess ovality and cross-section distortion of longitudinally submerged arc welding pipes after forming,a new three-roller continuous setting round process was proposed.This process can be divided into three stages:loading stage,roll bending stage and unloading stage.Based on the discretization idea,the mechanical model of the primary statically indeterminate problem of the longitudinally submerged arc welding pipes at the roll bending stage was established,and the deformation response was obtained.The simulation and theoretical results show that there are three positive bending regions and three reverse bending regions along the circumference of the pipe.The loading force of each roller shows growth,stability and downward trend with time.The error between the theoretical fitting curve and the simulated data point is very small,and the simulation results verify the reliability of the theoretical calculation.The experimental results show that the residual ovality decreases with the increase of the reduction,and the reduction of the turning point is the optimum reduction.In addition,the residual ovality of the pipe is less than 0.7%without cross-section distortion,which verifies the feasibility of this process.
基金supported by the Taishan Scholar Construction Funding(ts201511018)the National Natural Science Foundation of China(11372359)+2 种基金the Natural Science Foundation for Distinguished Young Scholars of Shandong Province(JQ201417)the Fundamental Research Funds for the Central Universities(15Cx08006A)the Innovation Project Foundation for Graduate Student of China University of Petroleum(YCXJ2016029)
文摘This study developed a sequential coupling finite element procedure to predict residual stresses of steel pipes with longitudinal wela／ circumferential weld and spiral weld.The results show that the residual stress in heat affected zone（HAZ）is higher than that in weld for spiral weld pipe.For the circumferential weld pipe and spiral weld pipe,the residual stress in inner surface is higher than that in outer surface.However,for the spiral weld pipe,the residual stress in inner surface is smaller than that in outer surface.The hoop residual stress of circumferential weld pipe is higher than that of longitudinal weld pipe,while the axial residual stress of circumferential weld pipe is smaller than that of longitudinal weld pipe.The hoop stresses for circumferential weld pipe and axial stress for longitudinal weld pipe have exceeded the yield strength of base metal.With the increase of helix angle,the hoop stress decreases while the axial stress increases.For the spiral pipe（α=30° to 50°）,both the hoop stress and axial stress are relatively small.The spiral pipe（helix angle ranging from 30° to 50°） is helpful to reduce stress corrosion cracking（SCC） and it is recommended to manufacture the steel pipe.
文摘In this article the research and development of X70 large diameter longitudinal seam submerged arc welded (LSAW) steel pipes for West East Gas Transportation Pipeline project (WEGTP) in China are introduced, including the key technique, fabrication of pipe production line, mass production and the latest progress of LSAW steel pipe technique.