The bonding of solid steel plate to liquid aluminum was studied using rapidsolidification. The surface of solid steel plate was defatted, descaled, immersed (in K_2ZrF_6 fluxaqueous solution) and stoved. In order to d...The bonding of solid steel plate to liquid aluminum was studied using rapidsolidification. The surface of solid steel plate was defatted, descaled, immersed (in K_2ZrF_6 fluxaqueous solution) and stoved. In order to determine the thickness of Fe-Al compound layer at theinterface of steel-aluminum solid to liquid bonding under rapid solidification, the interface ofbonding plate was investigated by SEM (Scanning Electron Microscope) experiment. The relationshipbetween bonding parameters (such as preheat temperature of steel plate, temperature of aluminumliquid and bonding time) and thickness of Fe-Al compound layer at the interface was established byartificial neural networks (ANN) perfectly. The maximum of relative error between the output and thedesired output of the ANN is only 5.4%. From the bonding parameters for the largest interfacialshear strength of bonding plate (226℃ for preheat temperature of steel plate, 723℃ for temperatureof aluminum liquid and 15.8 s for bonding time), the reasonable thickness of Fe-Al compound layer10.8 μm was got.展开更多
In this study, CrN/Cr2O3 double-layered coatings with various thickness ratios of CrN vs Cr2O3 layer were prepared by arc ion plating technology. The influences of the thickness ratio of CrN vs Cr2O3 layer on the micr...In this study, CrN/Cr2O3 double-layered coatings with various thickness ratios of CrN vs Cr2O3 layer were prepared by arc ion plating technology. The influences of the thickness ratio of CrN vs Cr2O3 layer on the microstructural characteristics as well as the mechanical and tribological properties of the CrN/Cr2O3 doublelayered coatings were investigated. The corresponding mechanisms were also discussed. The results indicated that the insertion of CrN layer between the Cr2O3 layer and substrate can effectively decrease the internal stress level of the coating. With increasing the thickness ratio of CrN vs Cr2O3 layer, the surface roughness of double-layered coatings decreased gradually, which had a certain influence on the friction coefficient. In addition, the microhardness also declined gradually, the adhesive strength almost increased linearly, whereas the wear rate declined firstly and then increased slightly. As the thickness ratio was 2：1, the double-layered coating exhibited the best wear resistance.展开更多
基金This project is financially supported by National Natural Science Foundation of China (No.50274047) and Advanced Technical Committee of China(No. 715-009-060)
文摘The bonding of solid steel plate to liquid aluminum was studied using rapidsolidification. The surface of solid steel plate was defatted, descaled, immersed (in K_2ZrF_6 fluxaqueous solution) and stoved. In order to determine the thickness of Fe-Al compound layer at theinterface of steel-aluminum solid to liquid bonding under rapid solidification, the interface ofbonding plate was investigated by SEM (Scanning Electron Microscope) experiment. The relationshipbetween bonding parameters (such as preheat temperature of steel plate, temperature of aluminumliquid and bonding time) and thickness of Fe-Al compound layer at the interface was established byartificial neural networks (ANN) perfectly. The maximum of relative error between the output and thedesired output of the ANN is only 5.4%. From the bonding parameters for the largest interfacialshear strength of bonding plate (226℃ for preheat temperature of steel plate, 723℃ for temperatureof aluminum liquid and 15.8 s for bonding time), the reasonable thickness of Fe-Al compound layer10.8 μm was got.
基金the National Key Basic Research Program of China("973 Program",No.2012CB625100)the National Natural Science Foundation of China(No.51001106&No.51301181)the Doctoral Starting up Foundation of Liaoning Province Science and Technology Agency,China(No.20131118)
文摘In this study, CrN/Cr2O3 double-layered coatings with various thickness ratios of CrN vs Cr2O3 layer were prepared by arc ion plating technology. The influences of the thickness ratio of CrN vs Cr2O3 layer on the microstructural characteristics as well as the mechanical and tribological properties of the CrN/Cr2O3 doublelayered coatings were investigated. The corresponding mechanisms were also discussed. The results indicated that the insertion of CrN layer between the Cr2O3 layer and substrate can effectively decrease the internal stress level of the coating. With increasing the thickness ratio of CrN vs Cr2O3 layer, the surface roughness of double-layered coatings decreased gradually, which had a certain influence on the friction coefficient. In addition, the microhardness also declined gradually, the adhesive strength almost increased linearly, whereas the wear rate declined firstly and then increased slightly. As the thickness ratio was 2：1, the double-layered coating exhibited the best wear resistance.