Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using sc...Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using scanning electronic microscopy(SEM),X-ray diffraction(XRD),and scratch test,respectively.The effects of laser power on the coefficients of friction(COFs)and corrosive-wear behaviors of Co30Cr8W1.6C3Ni1.4Si coatings were investigated using a wear tester in 3.5%NaCl solution,and the electrochemical corrosion performance was analyzed using an electrochemical workstation.The experimental results show that the Co30Cr8W1.6C3Ni1.4Si coating is bonded with the substrate in the metallurgical form,and the bonding strengths of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 76.5,56.5,and 55.6 N,respectively.The average COFs of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 0.769,0.893,and 0.941,respectively;and the corresponding wear rates are 0.267×105,0.3178×105,and 0.325×105μm3/Nm,respectively,which increases with the increase of laser power,the wear mechanism is primarily abrasive wear.The corrosion potential of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W is-0.05,-0.25,and-0.31 V,respectively,higher than-0.45 V of substrate which enhances the electrochemical corrosion resistance of substrate.展开更多
The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray ...The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investiga ted by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introdu cing a transition layer between Ni alloy substrate and ZrO 2 ceramic coating guarantees the high quality and properties of the coatings; ZrO 2 coatings doped with a little SiO 2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO 2 coating materials without SiO 2 ;the improvement in performance of ZrO 2 coating doped with SiO 2 is due to forming more dense coating structure by self closing effects of the flaws and pores in the ZrO 2 coatings.展开更多
The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heat...The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heated at 1 000 ℃ in vacuum oven of 1 kPa for 5 h. The properties of coatings were investigated. The results indicate that Fe2B appears after milling for 15 h in the powder at room temperature, a part of ternary borides （Mo2FeB2） are generated in powder sintered at 900 ℃. The coatings are composed of the major phases Mo2FeB2 and a-Fe, a little of Fe203, FeO and some pores. The bonding strength between the substrate and the ceramic coating is 32.73 MPa, the thermal-shock times is about 43 and the wear resistance is enhanced by approximately 5.28 times compared with that of the substrate, respectively. The comprehensive properties of Mo2FeB2 cermet coatings can be imoroved further after vacuum heat-treatment at 1 000 ℃ for 5 h.展开更多
Oxidation behaviors of Ni(Cr)-TiB2 coating deposited by HVOF technique were studied at 800,900 and 1 000℃in air. The microstructures of as-sprayed and oxidized coatings were characterized by X-ray diffractometry(XRD)...Oxidation behaviors of Ni(Cr)-TiB2 coating deposited by HVOF technique were studied at 800,900 and 1 000℃in air. The microstructures of as-sprayed and oxidized coatings were characterized by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).After oxidation at 800℃,a thin and adherent oxide layer was formed on the surface of the coating.With increasing exposure temperature,the thickness of the oxide layer increased;and at 1 000℃the oxide layer separated from the coating.Investigation of the kinetics of oxidation by using the thermogravimetric analysis(TGA)technique shows a parabolic oxidation rate.展开更多
By adding rare earth alloy and cerium oxide, the effect of rare earths on tribological properties of nickel base alloy layer was studied to approach the possibility of applying rare earths to Ni base thermal spray ...By adding rare earth alloy and cerium oxide, the effect of rare earths on tribological properties of nickel base alloy layer was studied to approach the possibility of applying rare earths to Ni base thermal spray welding coating. Wear test results showed that the wear rates of the nickel base coating without rare earths were quite high, and the load bearing capacity of coating was low, in contrast, the wear rates of the coating with rare earths were low and the coating had higher load bearing capacity. The results show that rare earths can refine the structure of nickel base alloy, improve the interface of the coating and substrate.展开更多
The oxidation and hot corrosion behaviors of HVAF-sprayed conventional and nanostructured NiCrC coatings were studied.The oxidation experiment was conducted in air,and the hot corrosion was conducted in the Na2SO4-30%...The oxidation and hot corrosion behaviors of HVAF-sprayed conventional and nanostructured NiCrC coatings were studied.The oxidation experiment was conducted in air,and the hot corrosion was conducted in the Na2SO4-30%K2SO4 environment, in the temperature range of 550-750℃for periods up to 160 h.The corrosion kinetics was tested with the thermogravimetric method. The corrosion products were characterized by scanning electron microscopy(SEM),energy dispersive X-ray spectroscopy(EDX)and X-ray diffractometry(XRD).As indicated by the results,both types of coatings possess high corrosion resistance,especially the nanostructured NiCrC coating.The enhanced grain boundary diffusion in the nanostructured coating not only promotes the formation of a denser Cr2O3 scale with a higher rate,but also helps to mitigate the Cr depletion at the metal/scale interface.The less porosity of the nanostructured coating is also thought to be beneficial to the anti-corrosion properties.展开更多
基金Funded by the Key Research and Development Project of Jiangsu Province(BE2016052)。
文摘Co30Cr8W1.6C3Ni1.4Si coatings were fabricated on Ti6Al4V alloy using a laser thermal spraying(LTS).The surface and cross-section morphologies,phases and bonding strength of obtained coatings were investigated using scanning electronic microscopy(SEM),X-ray diffraction(XRD),and scratch test,respectively.The effects of laser power on the coefficients of friction(COFs)and corrosive-wear behaviors of Co30Cr8W1.6C3Ni1.4Si coatings were investigated using a wear tester in 3.5%NaCl solution,and the electrochemical corrosion performance was analyzed using an electrochemical workstation.The experimental results show that the Co30Cr8W1.6C3Ni1.4Si coating is bonded with the substrate in the metallurgical form,and the bonding strengths of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 76.5,56.5,and 55.6 N,respectively.The average COFs of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W are 0.769,0.893,and 0.941,respectively;and the corresponding wear rates are 0.267×105,0.3178×105,and 0.325×105μm3/Nm,respectively,which increases with the increase of laser power,the wear mechanism is primarily abrasive wear.The corrosion potential of Co30Cr8W1.6C3Ni1.4Si coatings fabricated at the laser power of 1000,1200,and 1400 W is-0.05,-0.25,and-0.31 V,respectively,higher than-0.45 V of substrate which enhances the electrochemical corrosion resistance of substrate.
文摘The thermal barrier coatings with NiCrAlY alloy bonding layer, NiCrAlY Y 2O 3 stabilized ZrO 2 transition layer and Y 2O 3 stabilized ZrO 2 ceramic layer are prepared on nickel alloy substrates using the plasma spray technique. The relationship among the composition, structure and property of the coatings are investiga ted by means of optical microscope, scanning electronic microscope and the experiments of thermal shock resistance cycling and high temperature oxidation resistance. The results show that the structure design of introdu cing a transition layer between Ni alloy substrate and ZrO 2 ceramic coating guarantees the high quality and properties of the coatings; ZrO 2 coatings doped with a little SiO 2 possesses better thermal shock resistance and more excellent hot corrosion resistance as compared with ZrO 2 coating materials without SiO 2 ;the improvement in performance of ZrO 2 coating doped with SiO 2 is due to forming more dense coating structure by self closing effects of the flaws and pores in the ZrO 2 coatings.
基金Project(2007T069)supported by Liaoning Education Department Innovation Team,China
文摘The powders of Mo2FeB2 cermet were prepared with Mo powders, Fe-B alloy powders and Fe powders as raw materials. Mo2FeB2 cermet coatings were prepared on Q235 steel by reactive thermal spraying （RTS） method and heated at 1 000 ℃ in vacuum oven of 1 kPa for 5 h. The properties of coatings were investigated. The results indicate that Fe2B appears after milling for 15 h in the powder at room temperature, a part of ternary borides （Mo2FeB2） are generated in powder sintered at 900 ℃. The coatings are composed of the major phases Mo2FeB2 and a-Fe, a little of Fe203, FeO and some pores. The bonding strength between the substrate and the ceramic coating is 32.73 MPa, the thermal-shock times is about 43 and the wear resistance is enhanced by approximately 5.28 times compared with that of the substrate, respectively. The comprehensive properties of Mo2FeB2 cermet coatings can be imoroved further after vacuum heat-treatment at 1 000 ℃ for 5 h.
文摘Oxidation behaviors of Ni(Cr)-TiB2 coating deposited by HVOF technique were studied at 800,900 and 1 000℃in air. The microstructures of as-sprayed and oxidized coatings were characterized by X-ray diffractometry(XRD)and scanning electron microscopy(SEM).After oxidation at 800℃,a thin and adherent oxide layer was formed on the surface of the coating.With increasing exposure temperature,the thickness of the oxide layer increased;and at 1 000℃the oxide layer separated from the coating.Investigation of the kinetics of oxidation by using the thermogravimetric analysis(TGA)technique shows a parabolic oxidation rate.
文摘By adding rare earth alloy and cerium oxide, the effect of rare earths on tribological properties of nickel base alloy layer was studied to approach the possibility of applying rare earths to Ni base thermal spray welding coating. Wear test results showed that the wear rates of the nickel base coating without rare earths were quite high, and the load bearing capacity of coating was low, in contrast, the wear rates of the coating with rare earths were low and the coating had higher load bearing capacity. The results show that rare earths can refine the structure of nickel base alloy, improve the interface of the coating and substrate.
基金Project(2002AA331080)supported by the National High-tech Research and Development Program of China
文摘The oxidation and hot corrosion behaviors of HVAF-sprayed conventional and nanostructured NiCrC coatings were studied.The oxidation experiment was conducted in air,and the hot corrosion was conducted in the Na2SO4-30%K2SO4 environment, in the temperature range of 550-750℃for periods up to 160 h.The corrosion kinetics was tested with the thermogravimetric method. The corrosion products were characterized by scanning electron microscopy(SEM),energy dispersive X-ray spectroscopy(EDX)and X-ray diffractometry(XRD).As indicated by the results,both types of coatings possess high corrosion resistance,especially the nanostructured NiCrC coating.The enhanced grain boundary diffusion in the nanostructured coating not only promotes the formation of a denser Cr2O3 scale with a higher rate,but also helps to mitigate the Cr depletion at the metal/scale interface.The less porosity of the nanostructured coating is also thought to be beneficial to the anti-corrosion properties.