The experiment of injection molding, Dais-simulating test, morphological structure investigation(Scanning Electron Microscopy, SEM),X-ray photoelectron spectroscopy(XPS)were performed on mini-automobile spherical seat...The experiment of injection molding, Dais-simulating test, morphological structure investigation(Scanning Electron Microscopy, SEM),X-ray photoelectron spectroscopy(XPS)were performed on mini-automobile spherical seat which was made of thermoplastic polyester elastomer(TPEE)and oiled polyoxymethylene(POM),respectively. The friction-wear properties between the frictionl pair of polymer spherical seat and metallic(iron)spherical pin were studied. The test results indicate that the antifriction property of TPEE is superior to that of POM, while its surface chemical effect is inferior to that of POM.展开更多
The main goal of this research was to increase the strength of Polylactic acid (PLA), an entirely biodegradable thermoplastic polyester, and an increase in elongation at the breaking point compared to neat PLA. To thi...The main goal of this research was to increase the strength of Polylactic acid (PLA), an entirely biodegradable thermoplastic polyester, and an increase in elongation at the breaking point compared to neat PLA. To this end, S1, S2, and S3 were melt blended with various percentages of Zeolite, Glycerol, White vinegar, green camphor, Eucalyptus, and Carom seed oils. Here, the addition of glycerol, eucalyptus, and carom seed oils demonstrated an average improvement in impact and tensile strength of 13.44% and 14.55% respectively. Zeolite and glycerol work together as binding agents to improve stress transfer in the matrix, which increases tensile and flexural modulus as well as toughness elongation (>10%). The addition of the aforementioned materials led to an increase in the glass transition temperature and melting temperature, according to further DSC investigation. The thermal stability increased gradually, according to TGA data.展开更多
基金FundedbyKeyScientificandTechnologicalProjectofHubeiProvince (No .96 1 0 2 1 70 94 )
文摘The experiment of injection molding, Dais-simulating test, morphological structure investigation(Scanning Electron Microscopy, SEM),X-ray photoelectron spectroscopy(XPS)were performed on mini-automobile spherical seat which was made of thermoplastic polyester elastomer(TPEE)and oiled polyoxymethylene(POM),respectively. The friction-wear properties between the frictionl pair of polymer spherical seat and metallic(iron)spherical pin were studied. The test results indicate that the antifriction property of TPEE is superior to that of POM, while its surface chemical effect is inferior to that of POM.
文摘The main goal of this research was to increase the strength of Polylactic acid (PLA), an entirely biodegradable thermoplastic polyester, and an increase in elongation at the breaking point compared to neat PLA. To this end, S1, S2, and S3 were melt blended with various percentages of Zeolite, Glycerol, White vinegar, green camphor, Eucalyptus, and Carom seed oils. Here, the addition of glycerol, eucalyptus, and carom seed oils demonstrated an average improvement in impact and tensile strength of 13.44% and 14.55% respectively. Zeolite and glycerol work together as binding agents to improve stress transfer in the matrix, which increases tensile and flexural modulus as well as toughness elongation (>10%). The addition of the aforementioned materials led to an increase in the glass transition temperature and melting temperature, according to further DSC investigation. The thermal stability increased gradually, according to TGA data.