Morphology and Precipitation Kinetics of MnS in Low-Carbon Steel During Thin Slab Continuous Casting Process

The morphology of manganese sulfide formed during thin slab continuous casting process in low-carbon steel produced by compact strip production （CSP） technique was investigated. Using transmission electron microscopy analysis, it was seen that a majority of manganese sulfides precipitated at austenite grain boundaries, the morphologies of which were spherical or close to the spherical shape and the size of MnS precipitates ranged from 30 nm to 100 nm. A mathematical model of the manganese sulfide precipitation in this process was developed based on classical nucleation theory. Under the given conditions, the starting and finishing precipitation temperatures of MnS in the continuous casting thin slab of the studied low-carbon steel are 1 189 ℃ and 1 171 ℃, respectively, and the average diameter of MnS precipitates is about 48 nm within this precipitation temperature range. The influences of chemical components and thermo-mechanical processing conditions on the precipitation behavior of MnS in the same process were also discussed.

Modeling of unsteadiness of fluid flows and level fluctuations in thin slab continuous casting moulds

Unsteady fluid flows and level fluctuations in a thin slab continuous casting mould have significant influence on product quality. In this study, the phenomena concerning transient flow features and free surface motions were analyzed by means of the large eddy simulation （LES） software with the smagorinsky SGS model--VisualCast （VCast） II, where the Simpler algorithm on a body-fitted mesh was used to resolve governing equations. A series of water analog experiments on the fluid flow and the surface wave in the moulds of thin slab continuous casting were also performed. The results of fluid regions, middle of vortex and level fluctuation from digital simulations were identical with the results of the water analog experiments.

Technological Investigation on the Continuous Casting of Mid-Width Thin Slabs

Continuous casting of thin slabs is a key state project for 7th and sth five -year plans. On thebasis of foundamental works , CISRI condueted the tests of 102 heats in Lanzhou Steel Works in the periodof January 1991- June 1992. Three slab assortments of 50× 900 mm . 70 × 900 mm , 70 × 500 mm were ex-amined. In June of 1992, 412 t steel of 46 heats were cast with the efficiency of 91. 3 %. This. result meetsthe requiremeni of the state in this period. The mould, hedt transfer . casting technology and factors influ-encing slab’s qualities are investigated as well.

Numerical Simulation of Fluid Flow and Heat Transfer in Funnel Shaped Mold of Thin Slab Continuous Caster

Thin slab casting is used widely in the world. The control of molten steel flow and solidification in the mold is difficult due to the high casting speed and complicated configuration of the mold. Numerical simulation was carried out to study the fluid flow and heat transfer in the funnel shaped mold. The influence of nozzle design, casting speed and nozzle submersion depth on the flow and temperature fields in the mold was investigated, and guidance for selecting configurations of submerged nozzle was obtained.

Development of Continuous Casting Technology of Electrical Steel and New Products

The development of continuous casting technology of electrical steel was analyzed. The technologies and products characteristics of conventional continuous casting, thin slab continuous casting and rolling, middle thin slab continuous casting and rolling and twin-roll thin strip were compared. Conventional continuous casting technology was widely adopted in producing electrical steel, thin slab continuous casting and rolling and middle thin slab contin- uous casting and roiling technology industrialized electrical steel~ and study of twin-roll thin strip casting technology was focused on fundamental experiments.

Dynamic CCT Diagram of Automobile Beam Steel With High Strength Produced by FTSR Technology

The dynamic continuous cooling transformation（CCT）diagram and phase transformation rules of 510 MPa automobile beam steel,which is produced by a continuous casting of thin slab of FTSR technology in Tangshan Iron and Steel Co.Ltd.,are researched by thermal simulation experiment.The microstructure characteristics of the beam steel under different test conditions are studied by means of optical microscope and scanning electron microscope.The test results show that the critical temperatures of phase transformation Ar3 and Ar1 will all decrease with the increase of the cooling rate.When the cooling rate is lower than 20 ℃·s-1,the ferrite and pearlite phase transformations are the main parts;when the cooling rate is higher than 20 ℃·s-1,the bainite phase appears.Moreover,the microstructures of 510 MPa automobile beam steel produced by FTSR technology are also studied,and the results are basically in accordance with the CCT diagram gained from the test.