In this paper,based on three different kinds of ceramic side dams for thin strip antinuous casting,the friction and wearing property were studied.The effects of friction pressure,temperature and friction time on the f...In this paper,based on three different kinds of ceramic side dams for thin strip antinuous casting,the friction and wearing property were studied.The effects of friction pressure,temperature and friction time on the friction and wearing property of the ceramic side dam were researched.What’s more,the friction mechanism and wearing mechanism of the ceramic side dam were researched as well.Results show that the ceramic side dam of BN-SiA lO N has the best wearing resistance property.while at room temperature,16 min of friction time and0.35 MPa of friction pressure,the test friction coefficient is 0.60 and wearing capacity is 272.358 mm-3.In addition,when at 400℃,16 min of friction time and 0.18MPa of friction pressure,the test friction coefficient is0.70.The friction mechanism of ceramic side dam with the opposite wearing material is mainly the composite wear of adhesion,abrasive and fatigue.展开更多
In this study, the temperature field model of twin-roll thin strip continuous casting was developed, and the interface heat transfer coefficient between the air and the strip surface was computed by using the inverse ...In this study, the temperature field model of twin-roll thin strip continuous casting was developed, and the interface heat transfer coefficient between the air and the strip surface was computed by using the inverse method. The effects of the process parameters including the casting speed, liquid level height, pouring temperature and thickness of the thin strip on the outlet temperature of the rotating rolls and the surface temperature of the thin strip were analyzed.展开更多
BN–ZrO_(2)ceramics with different additives such as SiC,Al_(2)O_(3) and MgAl_(2)O_(4) were fabricated by hot pressing sintering process to study sintering properties and corrosion resistance by the rotary immersion m...BN–ZrO_(2)ceramics with different additives such as SiC,Al_(2)O_(3) and MgAl_(2)O_(4) were fabricated by hot pressing sintering process to study sintering properties and corrosion resistance by the rotary immersion molten steel test.The results showed that SiC,Al_(2)O_(3) and MgAl_(2)O_(4) can improve the sintering properties of BN–ZrO_(2)ceramics;especially,the introduction of SiC can significantly improve the hardness of the material;thus,the above compounds will help to improve the wear resistance of BN–ZrO_(2)ceramics.The exposed oxide layer is in contact with molten steel and forms liquid phase after BN oxidation and B_(2)O_(3) volatilization,additives can significantly affect the properties of liquid phase,and m-ZrO_(2)grains are sintered and grown by dissolution–precipitation mechanism by liquid phase.Consequently,Al_(2)O_(3) and MgAl_(2)O_(4) are more conducive to the formation of working layer with solid skeleton,which determines the corrosion resistance of BN–ZrO_(2)ceramics.展开更多
文摘In this paper,based on three different kinds of ceramic side dams for thin strip antinuous casting,the friction and wearing property were studied.The effects of friction pressure,temperature and friction time on the friction and wearing property of the ceramic side dam were researched.What’s more,the friction mechanism and wearing mechanism of the ceramic side dam were researched as well.Results show that the ceramic side dam of BN-SiA lO N has the best wearing resistance property.while at room temperature,16 min of friction time and0.35 MPa of friction pressure,the test friction coefficient is 0.60 and wearing capacity is 272.358 mm-3.In addition,when at 400℃,16 min of friction time and 0.18MPa of friction pressure,the test friction coefficient is0.70.The friction mechanism of ceramic side dam with the opposite wearing material is mainly the composite wear of adhesion,abrasive and fatigue.
文摘In this study, the temperature field model of twin-roll thin strip continuous casting was developed, and the interface heat transfer coefficient between the air and the strip surface was computed by using the inverse method. The effects of the process parameters including the casting speed, liquid level height, pouring temperature and thickness of the thin strip on the outlet temperature of the rotating rolls and the surface temperature of the thin strip were analyzed.
基金The authors gratefully acknowledge the support of National Natural Science Foundation of China(51932008 and 51772277)Central China Thousand Talents Project(204200510011).
文摘BN–ZrO_(2)ceramics with different additives such as SiC,Al_(2)O_(3) and MgAl_(2)O_(4) were fabricated by hot pressing sintering process to study sintering properties and corrosion resistance by the rotary immersion molten steel test.The results showed that SiC,Al_(2)O_(3) and MgAl_(2)O_(4) can improve the sintering properties of BN–ZrO_(2)ceramics;especially,the introduction of SiC can significantly improve the hardness of the material;thus,the above compounds will help to improve the wear resistance of BN–ZrO_(2)ceramics.The exposed oxide layer is in contact with molten steel and forms liquid phase after BN oxidation and B_(2)O_(3) volatilization,additives can significantly affect the properties of liquid phase,and m-ZrO_(2)grains are sintered and grown by dissolution–precipitation mechanism by liquid phase.Consequently,Al_(2)O_(3) and MgAl_(2)O_(4) are more conducive to the formation of working layer with solid skeleton,which determines the corrosion resistance of BN–ZrO_(2)ceramics.